• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.83-84
• /
• 2008

The primary water stress corrosion cracking (PWSCC) of dissimilar metal weld based on Alloy 82/182 is one of major issues in material degradation of nuclear components. It is well known that the crack initiation and growth due to PWSCC is influenced by material's susceptibility to PWSCC and distribution of welding residual stress. Therefore, modeling the welding residual stress is of interest in understanding crack formation and growth in dissimilar metal weld. Currently in Korea, a numerical round robin study is undertaken to provide guidance on the welding residual stress analysis of dissimilar metal weld. As a part of this effort, the present paper investigates distribution of welding resisual stress of a ferritic low alloy steel nozzle with dissimilar metal weld using Alloy 82/182. Two-dimensional thermo-mechanical finite element analyses are carried out to simulate multi-pass welding process on the basis of the detailed design and fabrication data. The present results are compared with those from other participants, and more works incorporating physical measurements are going to be performed to quantify the uncertainties relating to modelling assumptions.

• Journal of Welding and Joining
• /
• v.23 no.2
• /
• pp.66-74
• /
• 2005

API(American Petroleum Institute) steel, as a line pipe material, requires the enhanced mechanical and chemical properties with the environmental severity. Especially, the weld part(weld metal and heat affected zone) is an important region for the safety. However, the study for the behavior of microstructure and toughness in multi-pass welding is seldom. In this study, the relationship between the microstructure and toughness of welds with several welding, bending and heat-treatment conditions was examined. In particular, HIC property in the weld metal was evaluated. The microstructure and toughness in multi-passed HAZ seemed to be determined by the final welding thermal cycle and the low toughness was attributed to the MA constituents formed in the intercritically reheated region. The weld metal showed very low toughness and it was not improved by the change in bending and heat treatment conditions. Additionally, the cracks are observed in the weld metal. from these results, it was found that the choice of welding wire/flux is very important.

• International Journal of Korean Welding Society
• /
• v.1 no.2
• /
• pp.30-35
• /
• 2001

Nowadays, repair welding on in-service natural gas pipeline is a matter of primary concern of gas company. The main purpose of this study is to investigate the effects of welding conditions on the allowable heat input for crack-free welds and welds without burn-through onto in-service natural gas pipeline. First of all, single pass weld bead on plates of the various thickness was deposited to evaluate the penetration of weld metal, the depth of heat affected zone and the hardness of repair weld under various welding conditions. Also, finite element analysis has been conducted to validate experimental results of bead-on plate welds and to develop appropriate model for repair welding. The welding experiments of bead-on-plate weld confirmed the influence of plate thickness, heat input and welding process on safety. And, the finite element model was demonstrated by comparing experimental results. The agreement between the computed and measured values was shown to be generally good. Therefore, It is possible to predict the safety of repair welding under various welding conditions with experimental results and finite element analysis model.

• Journal of Welding and Joining
• /
• v.28 no.4
• /
• pp.18-25
• /
• 2010

Super-duplex stainless steels (SDSS) have a good balance of mechanical property and corrosion resistance when they consist of approximately equal amount of austenite and ferrite. The SDSS needs to avoid the detrimental phases such as sigma(${\sigma}$), chi(${\chi}$), secondary austenite(${\gamma}2$), chromium carbide & nitride and to maintain the ratio of ferrite & austenite phase as well known. However, the effects of the subsequent weld thermal cycle were seldom experimentally studied on the micro-structural variation of weldment & pitting corrosion property. Therefore, the present study investigated the effect of the subsequent thermal cycle on the change of weld microstructure and pitting corrosion property at $40^{\circ}C$. The thermal history of root side was measured experimentally and the change of microstructure of weld root & the weight loss by pitting corrosion test were observed as a function of the thermal cycle of each weld layer. The ferrite contents of root weld were reduced with the subsequent weld thermal cycles. The pitting corrosion was occurred in the weld root region in case of the all pitted specimen & in the middle weld layer in some cases. And the weight loss by pitting corrosion was increased in proportional to the time exposed at high temperature of the root weld and also by the decrease of ferrite content. The subsequent weld thermal cycles destroy the phase balance of ferrite & austenite at the root weld. Conclusively, It is thought that as the more subsequent welds were added, the more the phase balance of ferrite & austenite was deviated from equality, therefore the pitting corrosion property was deteriorated by galvanic effect of the two phases and the increase of 2nd phases & grain boundary energy.

• Journal of Welding and Joining
• /
• v.33 no.4
• /
• pp.30-36
• /
• 2015

Austenite stainless steel(SA213-TP347H) has widely been used for the superheater & reheater tube in USC(ultra-supercritica) coal boiler because of its high creep rupture strength and anti-oxidation. But recently, the short-term failures have happened frequently in heat affected zone for only 4,000~15,000hours of service. Many investigations have been conducted to understand the failure mechanism. The root cause of failure was comfirmed to "strain induce participation hardening crack" or "reheat cracking". This mechanism often occurred due to weld residual stress and precipitation of the Cr, Nb carbides in the stabilized stainless steel such as TP347H. This paper presents an analysis of failure tube and effect of the sample tubes that conducting stabilizing heat treatment in site after 11,380hours & 16,961hours of service. Visual inspection was performed. In addition, microscopic characteristics was identified by O.M, SEM, and hardness test was carried out to find out the heat treatment effects. Failures seem to happen because of being not conducted stabilizing heat treatment in site. And another cause is inadequate weld parameter such as pass, ampere, voltage, inter-pass temperature. Thus, this paper has the purpose to describe that how to prevent similar failures in those weld-joints.

• Journal of Welding and Joining
• /
• v.32 no.5
• /
• pp.7-12
• /
• 2014

In this study, API-X100 steel pipes were welded with various kinds of welding wires in the laser-arc hybrid welding process. 10kW fiber laser source was combined to MIG arc welding process. API X-100 steel of base metal was of 16.9mm thickness, and butt welding applied. After welding, full penetration weld was acquired by 1-pass welding. A root porosity and the lack of fusion was observed in some welding conditions. By the mixing the melted wire, acicular ferrite, polygonal ferrite, pro-eutectoid, aligned side plate, and bainite structures were observed at the weld metal. From the observation of hybrid weld, unmixed zone had more Ni and Cr. The unmixed zone was a 1/3 area of the weld metal. As the mechanical test of the hybrid welding, tensile test and impact test applied. From the tensile test, all of the welding except SM70S was fractured at the base metal. The result of the impact test at -30 degree C led 60J~320J of the absorbed energy. The result of the low-absorbed energy might be from the coarse equiaxed structures of the weld metal.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.8 no.4
• /
• pp.123-133
• /
• 2004

The evaluation standard method of weld zone in rails is not exhibited in case of the domestic and the outside about ultrasonic inspection method. therefore, practical affairs a mans on the ground know very little about evaluation method of pass and failure. This paper discuss about ultrasonic exploration of weld zone in railway rails to know practical affairs a mans that the first, "problem and improvement direction of domestic track construction specifications applied according to a place ordering" and the second, "the method applied of ultrasonic exploration test of weld zone in railway rails".

• Journal of Advanced Marine Engineering and Technology
• /
• v.36 no.8
• /
• pp.1076-1082
• /
• 2012

Today the welding for LNG carrier is known to be possible using arc and plasma arc welding process. But because of the lower energy density, arc welding is inevitable to multi-pass welding for thick plate and has a limit of welding speed compared to laser which is high energy density heat source. When thick plate is welded, weld defect by multi-pass welding and heat-affected zone by high heat-input were formed. Therefore one-pass welding by key-hole has been considered to work out the problems. It is possible for Laser, electron beam, plasma process to do key-hole welding. Nowadays, plasma process has been used for welding membrane of cargo tank for LNG carrier instead of arc process. Recently, many studies have examined to apply laser process to welding of membrane. In this paper, weldability, microstructure and mechanical properties of stainless steel for LNG carrier welded by fiber laser were compared to those by plasma. As a result, although the laser welding has several times faster speed, similar properties and smaller weld and heat affected zone were obtained. Consequently, this study proves the superiority of fiber laser welding for LNG carrier.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.390-395
• /
• 2002

The experimental and numerical study has been conducted on the sleeve repair welding of API 5L X65 pipeline. SMA W and GTAW were applied to weld the sleeve. The macrostructure and hardness of repair welds have been examined. The [mite element analysis of the multi-pass sleeve-fillet welding has been conducted to validate the experiment and investigate the effects of in-service welding conditions. The effect of gas flow rate on the hydrogen cracking was investigated. The effect of internal pressure on residual stresses and plastic strain was investigated. The allowable heat input was predicted considering the maximum temperature of inner surface of pipe and cooling rate at CGHAZ.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.118-127
• /
• 1997

With the trend towards welding automation and robotization, mathematical models for studying the influence of various variables on the weld bead geometry in gas metal arc (GMA) welding process are required. Partial penetration, single-pass bead-on-plate welds using the GMA welding process were fabricated in 12mm mild steel plates employed four different process variables. Experimental results has been designed to investigate the analytical and empirical formulae, and develop mathematical equations for understanding the relationship between process variables and weld bead geometry. The relationships can be usefully employed not only for open loop process control, but also for adaptive control provided that dynamic sensing of process output is performed.