• Geomechanics and Engineering
• /
• v.34 no.1
• /
• pp.103-113
• /
• 2023

This study focused on understanding the relationship between the design of a tunnel boring machine disc cutter ring and its rock-breaking efficiency, as well as the applicable conditions of different cutter ring types. The discrete element method was used to establish a numerical model of the rock-breaking process using disc cutters with different ring types to reveal the development of rock damage cracks and variation in cutter penetration load. The calculation results indicate that a sharp-edged (V-shaped) disc cutter penetrates a rock mass to a given depth with the lowest load, resulting in more intermediate cracks and few lateral cracks, which leads to difficulty in crack combination. Furthermore, the poor wear resistance of a conventional V-shaped cutter can lead to an exponential increase in the penetration load after cutter ring wear. In contrast, constant-cross-section (CCS) disc cutters have the highest quantity of crack extensions after penetrating rock, but also require the highest penetration loads. An arch-edged (U-shaped) disc cutter is more moderate than the aforementioned types with sufficient intermediate and lateral crack propagation after cutting into rock under a suitable penetration load. Additionally, we found that the cutter ring wedge angle and edge width heavily influence cutter rock-breaking efficiency and that a disc cutter with a 16 to 22 mm edge width and 20° to 30° wedge angle exhibits high performance. Compared to V-shaped and U-shaped cutters, the CCS cutter is more suitable for soft or medium-strength rocks, where the penetration load is relatively small. Additionally, two typical case studies were selected to verify that replacing a CCS cutter with a U-shaped or optimized V-shaped disc cutter can increase cutting efficiency when encountering hard rocks.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.2
• /
• pp.55-60
• /
• 1996

Tripitaka Koreana were made during Coryo Dynasty from 1236 to 1251 A.D. Buddhist scriptures were engraved on 81.340 wooden plates. Some plates were varnished with Rhus lacquer, but most of them were uncoated. Macroscopically, most of the plates appeared intact due to the storage in a well-ventilated wooden house. Because, they were irregularly used for printings with ink, it can be assumed that they were repeatedly exposed to ink-water and drying processes. The present were made to examine the changes of wood cell structures occurred during long-term aging deterioration processes in these dry archaeological wooden plates. Light, scanning and transmission electron microscopes were employed for this study. Wedge-shaped cracks and delamilations were found from the lumen side toward the compound middle lamellae and they progressed toward primary or secondary walls. A large amount of hypae in vessels and the degradation of vessel-ray pit walls by the fungal hyphae were observed. When compared to the recent wood, the birefringence of wood fibers was considerably lower or completly disappeared, suggesting the degradation of crystalline cellulose in these wood samples. The degradation of the cell wall could be also revealed the calculation of crystallinity with X-ray diffraction and the size of crystalline region was estimated.

• Nuclear Engineering and Technology
• /
• v.17 no.3
• /
• pp.193-199
• /
• 1985

Iodine-induced stress corrosion cracking tests of Zircaloy-4 cladding were undertaken using the modified infernal pressurization method. The effects of iodine concentration and applied stress were studied. The critical iodine concentration for SCC was found to be about 0.2 mg/$\textrm{cm}^2$ at 603$^{\circ}$K. The threshold stress was dependent on the test temperature and the mechanical properties of the specimen. The fracture surface showed that the crack propagated stepwise iron one grain to others until the material was unstable and then ruptured mechanically. The initial region showed the transgranular feature and the wedge-shaped cracks. As the crack proceeded, the transgranular and ductile-tearing mired feature appeared in the middle region.