• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.123-123
• /
• 2015

0.087 wt.% Gd-lean duplex stainless steels were inert arc-melted and cast in a mold. The micro-hardnesses of the rolling, transverse, short transverse directions were 258.5, 292.3, 314.7 HV, respectively. The 33% cold rolled specimen had the crystallographic texture that mainly (100) pole was concentrated to normal direction and (110) pole was concentrated in the center of normal and rolling directions. The corrosion potential and corrosion rate in artificial sea water were in the range of $105.6-221.6mV_{SHE}$, $0.59-1.06mA/cm^2$, respectively. The friction coefficient and wear loss of the 0.087 wt.% Gd-lean duplex stainless steels in artificial sea water were about 67% and 65% lower than in air, whereas, the wear efficiency was 22% higher. The corrosion and wear behaviors of the 0.087 wt.% Gd-lean duplex stainless steels significantly depended on the gadolinium phases.

• Journal of Power System Engineering
• /
• v.6 no.1
• /
• pp.74-81
• /
• 2002

The characteristics of corrosion resistance for the surface of ductile cast iron(GCD40) by plasma nitriding process have been studied in terms of electrochemical polarization behaviors including corrosion potential($E_{corr}$), anodic polarization trends, polarization resistance($R_p$), and also have been studied microstructures, hardness and specific wear of nitrided layer Nitrided layer showed an enhanced hardness values in all the plasma nitriding condition investigated. In the result of wear test, specific wear of nitrided specimens were much decreased than that of non-treated specimens. In the results of XRD, ${\gamma}'phase\;and\;{\varepsilon}$ phase were detected in nitrided surface. And it was found that ${\varepsilon}$ phase was decreased and ${\gamma}'phase$ was increased respectively, as the nitriding time became longer. In the test of corrosion resistance, natural potentials in all the nitrided specimens were towards noble directions than in the case of non-treated specimens. The measurement of electrode potentials revealed that corrosion resistivity of plasma nitrided specimens were higher than in the case of the non-treated specimens.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.205-206
• /
• 2002

In this paper we examined the contribution of mechanical and electrochemical factors in corrosive wear for Zr-alloy against $Al_2O_3$ ball in $Na_2SO_4$ solution. Normal load and the area of metallic specimen was varied to change the corrosion behavior. At the commence of sliding, the potential drop took place, which increased with load due to the great exposure of fresh surface. Wear volume was linearly proportional to load. The corrosion factor was about 15%. By increasing the Aa/Ac ratio, corrosion factor to total wear decreases and saturates above Aa/Ac=0.15.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.22 no.6
• /
• pp.895-900
• /
• 2013

Several plasma spray and metallurgical surface coatings such as $Al_2O_3$, $Cr_2O_3$, WC-Ni, and chromizing coating have been examined for their application in environments with high temperature, wear, and corrosion. The chromizing coating is different from others coatings in the manufacturing process the surface. These coatings' characteristics were tested experimentally, and the results were compared. WC-Ni shows good performance against thermal barrier, wear, and corrosion and is one of the best candidates for the environment considered herein. These coatings were studied for their application in the steel manufacturing industry. The most commonly required functions in this industry are thermal and wear resistance.

• Korean Journal of Metals and Materials
• /
• v.49 no.10
• /
• pp.747-753
• /
• 2011

In order to improve the corrosion resistance of Fe-20Cr-1.7C-1Si hardfacing alloy without a loss of wear resistance, the effect of Ni addition was investigated. As expected, the corrosion resistance of the alloy increased with increasing Ni concentration. The wear resistance of the alloy did not decrease, even though the hardness decreased, up to Ni concentration of 5 wt.%. This was attributed to the fact that the decrease in hardness was counterbalanced by the strain-induced martensitic transformation. The wear resistance of the alloy, however, decreased abruptly with increases of the Ni concentration over 5 wt.%.

• Corrosion Science and Technology
• /
• v.11 no.6
• /
• pp.280-285
• /
• 2012

Aluminum is on active metal, but it is well known that its oxide film plays a role as protective barrier which is comparatively stable in air and neutral aqueous solution. Thus, aluminum alloys have been widely applied in architectural trim, cold & hot-water storage vessels and piping etc., furthermore, the aluminum alloy of AC8A have been widely used in mold casting material of engine piston because of its properties of temperature and wear resistance. In recent years, the oil price is getting higher and higher, thus the using of low quality oil has been significantly increased in engines of ship and vehicle. Therefore it is considered that evaluation of corrosion resistance as well as wear resistance of AC8A material is also important to improve its property and prolong its lifetime. In this study, the effect of solution and tempering heat treatment to corrosion and wear resistance is investigated with electrochemical method and measurement of hardness. The hardness decreased with solution heat treatment compared to mold casting condition, but its value increased with tempering heat treatment and exhibited the highest value of hardness with tempering heat treatment temperature at $190^{\circ}C$ for 24hrs. Furthermore, corrosion resistance increased with decreasing of the hardness, and decreased with increasing of the hardness reversely. As a result, it is suggested that the optimum heat treatment to improve both corrosion and wear resistance is tempering heat treatment temperature at $190^{\circ}C$ for 16hrs.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.2
• /
• pp.119-127
• /
• 2004

In order to develop the corrosion and wear resistance of stainless steels, effects of plasma-nitriding on the surface characteristics of stainless steels containing Nb were investigated by utilizing a potentiostat. It was found that plasma nitriding at $350^{\circ}C$, compared with $500^{\circ}C$, produced a good corrosion resistance as nitriding time increased, whereas stainless steel containing low Nb content showed that pitting potential and corrosion potential decreased.

• Tribology and Lubricants
• /
• v.40 no.3
• /
• pp.97-102
• /
• 2024

The next-generation Molten Salt Reactor is known for its high safety because it uses nuclear fuel dissolved in high-temperature molten salt, unlike traditional solid atomic fuel methods. However, the high-temperature molten salt causes severe corrosion in internal structural materials, threatening the reactor's safety. Therefore, it is crucial to investigate the high-temperature corrosion resistance and wear performance of materials used in reactors to ensure safety. In this study, the high-temperature corrosion resistances and wear performances of corrosion samples in a NaCl-MgCl2-KCl (20-40-40 [wt%]) molten salt are investigated to evaluate the applicability of economically viable stainless steels, 316SS and 304SS. Hastelloy C276 and a new alloy containing a small amount of Nb are used as reference samples for comparative analysis. The mass loss, mass loss rate per unit volume, and surface roughness of each sample are measured to understand the corrosion mechanisms. Scanning electron microscopy and energy-dispersive spectroscopy analyses are employed to analyze the corrosion mechanisms. Wear tests on the corroded samples are also conducted to assess the extent of corrosion. Based on the experimental results, we predict the lifespans of the materials and evaluate their suitability as candidate materials for molten salt reactors. The data obtained from the experiments provide a valuable database for structural materials that can enhance the stability of molten salt reactors and recommend high-temperature corrosion-resistant materials suitable for next-generation reactors.

• Journal of the Korean Institute of Gas
• /
• v.3 no.3 s.8
• /
• pp.39-44
• /
• 1999

In the study, corrosion characteristics under various corrosion environments(neutral solution, acid solution), for various hinge materials(SM20C, BsC3 and STC4H), were investigated by immersion test, and the behaviour of fretting wear under atmosphere was studied. In immersion test, corrosion potential of those materials showed to be noble in the sequence of $0.5\%HNO_3$> underground water> $0.5\%\;H_2SO_4$ solution, and potential of a sole material, except BsC3, was more noble than these of mixed materials. In same material SM20C, the fretting wear loss of rotary materials increased about 1.9 times to that of moving materials, because of surface hardening by frictional force.

• Corrosion Science and Technology
• /
• v.12 no.3
• /
• pp.142-148
• /
• 2013

Safety is a major concern in Nuclear Power Plants (NPPs). Piping systems in NPPs are very complex and composed of many components such as tees, elbows, expanders and straight pipes. The high pressure and high temperature water flows inside piping components. As high speed water flows inside piping, the pipe wall thinning occurs in various reasons such as FAC (Flow Accelerated Corrosion), LDIE (Liquid Droplet Impingement Erosion) and Flashing. To inspect the wall thinning phenomenon and protect the piping from damages, piping components are checked by UT measurement in every overhaul. During every overhaul, approximately 200~300 components (40,000~60,000 UT data) are examined in NPPs. There are some methods from EPRI for evaluating wear rate of components. However, only few studies have been conducted to find out the raw data reliability for the wear rate evaluation. Securing the reliable raw data is the key factor for a reasonable evaluation. This paper suggests the reliability analysis method for the repeatedly measured data for wear rate evaluation.