The effect of load and sliding speed on abrasive wear characteristics of glass fiber/polyurethane (GF/PUR) composites were investigated at ambient temperature by pin-on-disc friction test. The friction coefficient, cumulative wear volume and surface roughness of these materials against SiC abrasive paper were determined experimentally. Experimental results showed that the surface roughness of the GF/PUR composites was increased as applied load was higher in wear test. The cumulative wear volume tended to increase nonlinearly with increase of sliding distance and depended on applied load and sliding speed for these composites. It could be verified by scanning electric microscopy (SEM) photograph of surface tested that major failure mechanisms were lapping layers, ploughing, delamination, deformation of resin and cracking.

• Tribology and Lubricants
• /
• v.32 no.1
• /
• pp.32-37
• /
• 2016

The wear characteristics of metal ball and seat in a metal-seated ball valve significantly affect the performances such as leakage and valve torque. In this work, the wear characteristics of metal ball and seat are experimentally investigated. A stainless steel ball and seat with a high corrosion-resistant coating are prepared and a component level test was performed. The hardness and surface roughness of specimens cut from the metal ball and seat are measured before and after the test using a micro-Vickers hardness tester and confocal microscopy, respectively. In order to assess the wear characteristics, the surfaces of the specimens are carefully examined after the test. The confocal microscope data show that the surface roughness values of both the ball and seat increase by a factor of 3-4, which may lead to an increase in valve torque. However, the wear of the seat is found to be more significant than that of the ball. In addition, a comparison of the surfaces of the ball and seat before and after testing revealed that adhesive and abrasive wear are the major wear mechanisms. The results of this study may aid in the design of metal-seated ball valves from the tribological point of view.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.16 no.4
• /
• pp.9-15
• /
• 2017

In hot forming process, the dies in which excessive worn or crack occurs is reused after repair. Generally hot forming dies are recycled through a welding repair method. Welding repair methods are highly dependent on the skills of engineer. It causes process defects such as dimensional defects and structural defects. Recently, the metal 3D printing method has been applied to the repair of used dies. The aim of this study is to evaluate the wear characteristics of AISI H13 tool steel repaired by 3D printing method. Three kinds of wear specimens were fabricated by using 3D printing, welding, and initial material. A pin-on-disk wear test was carried out to evaluate the wear characteristics. From the result of wear test, the wear characteristics of 3D printing method was superior to that of the welded material, and was similar to that of the initial material.

• Fashion & Textile Research Journal
• /
• v.18 no.1
• /
• pp.27-37
• /
• 2016

This study examined consumer perceptions towards outdoor wear differentiation and product attributes for outdoor wear differentiation to develop an outdoor wear differentiation strategy. It also investigated how consumer's evaluated product attributes according to consumer's demographic characteristics. Data were acquired from a survey of 454 adult respondents aged over 20 that was analyzed with descriptives, frequency, t-test, one-way ANOVA, factor analysis, and reliability. The results were as follows. First, it showed that consumers did not have a positive or a negative perception toward outdoor wear differentiation, and they thought outdoor wear should be differentiated. Those married and older tended to think that outdoor wear should be differentiated more than that for those single and younger. Consumer evaluations were significantly different on the necessity of outdoor wear differentiation according to age and total income. Second, consumers assessed that color, pattern and textiles had similar characteristics among outdoor wear brands; in addition, brand recognition and brand image had very different characteristics. Third, product attributes for outdoor wear differentiation were service and store, product quality, brand and popularity, and product designs with mean values of product quality, product design, service and store, and brand and popularity, respectively. Fourth, consumers were significantly different in the importance assessment of product attributes for differentiation according to gender, marital status and age.

• Tribology and Lubricants
• /
• v.19 no.4
• /
• pp.223-229
• /
• 2003

The sliding wear characteristics of the crane sheave were investigated using a pin-on-disk rig tester. The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication and dry condition. The results of wear test showed that an annealed-casted have lower, also the wear curves are linearly increased with increasing of sliding distance. For the specific wear rate of annealed-casted, the wear resistance was increased with decreasing diameter of wire. The wear of a wire and a disk have a different mechanism, the one is the abrasive wear due to fatigue wear under lubrication, another is the adhesion wear under dry condition.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.124-130
• /
• 1998

The wear characteristics and wear mechanisms of dental composite resins were investigated. Composite resins such as Metalii, Silux Plus, Heliomolar and Palfique Estelite were selected as specimens and contents of filler in specimens in order to analyze the effect of Prepolymerized Particle Fillers in friction and wear characteristics. Ball on flat wear tester was used for a wear test. Friction and wear tests are carried out at room temperature. The friction coefficient of Metafil was quite high relatively, and the wear resistance of Silux Plus and Palfique Estelite was better than that of Metafil and Hellomolar at the same experimental condition. The main wear mechanism is plastic flow and abrasive wear by crack propagation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.11
• /
• pp.1873-1880
• /
• 2003

The sliding wear characteristics of the crane sheave were investigated using a pin on disk rig tester. The experiment was conducted using a high carbon steel wire that was upper material, also carbon steel castings that was disk material. There are various operating conditions in this work. At the room temperature, we carried out the wear test under a grease lubrication and dry condition. The results of wear test showed that an annealed-casted have lower, also the wear curves are linearly increased with increasing of sliding distance. For the specific wear rate of annealed-casted, the wear resistance was increased with decreasing diameter of wire. The wear of a wire and a disk have a different mechanism, the one is the abrasive wear due to fatigue wear under lubrication, another is the adhesion wear under dry condition.

• Tribology and Lubricants
• /
• v.16 no.4
• /
• pp.302-307
• /
• 2000

The fretting wear characteristics of STS304 steel in seawater were investigated experimentally. A fretting wear tester was designed to be suitable for this fretting test. This study was focused on the effects due to the combination of normal load, slip amplitude and number of cycles and corrosive environment as the main factors of fretting. The results of this study showed that the wear volume increased abruptly at slip amplitude between 70 $\mu\textrm{m}$∼100 $\mu\textrm{m}$ by fracture of oxide layers but above that slip amplitude the wear volume increased steadily.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.107-113
• /
• 1996

This paper presents the experimental results on the cutting performance and wear characteristics of CBN ball end-mill. The influence of cutting fluids and rake angles on the tool performance is reported. It i found that the neat cutting oil is beneficial to obtain good surface roughness and 30 .deg. of rake angle gives the minimum tool wear. The microscopic investigations reveal that the coated carbide endmills wear by fracture whereas the CBN endimills wear by attritious mode.

• Transactions of Materials Processing
• /
• v.23 no.1
• /
• pp.29-34
• /
• 2014

The damage level of the die surface was predicted by estimating the surface roughness with a finite element analysis and the wear characteristics. Wear and friction tests were conducted to compare the wear characteristics for three kinds of surface treatments - CrN, TiAlN and AlCrN coatings. A prediction model was derived from the surface roughness results with respect to contact pressure and sliding speed which were obtained from the wear test. Surface roughness values for the damage regions of the die surface were compared between the experiments and the prediction model, which shows fairly good agreement with each other.