• 한국세라믹학회지
• /
• 제35권4호
• /
• pp.319-324
• /
• 1998

Sol-gel derived phosphate water-sioluble glasses containing Cu were prepared. Powder-shape of glasses were added in D.I water used polyethylene bottle. After solution contained glass powder were submerged in water bath on 25$^{\circ}C$ their dissolution behavior/characteristics bactericidal effect and cytotoxicity test were evaluated. The maximum amount of Cu(35 mol%) via sol-gel method was more 5 mol% increased than that with melting process. The stage of total dissolution was more dominant than that of selective leaching dur-ing dissolution due to dissolved amount of glasses increased linearly with time. The ratio of Cu+ to {{{{ {Cu }^{2+ } }} was 3:7 so that the structure of glasses is more predominant 2-dimension chain structure than 3-dimenshion po-lymeric structue. The stage of total dissolution was more dominant than that of selective leaching during dissolution. Bactericidal effect against all bacteria showed that solutions which contained 40 ppm and 100 ppm of Cu killed 80 percentages of bacteria within 2 hours and 100 percentages of those within 12 hours. The results of cytotoxicity test for L929 cells showed no cytotoxicity were observed within 96 hours for dis-solved solution that contains 40 ppm and 100 ppm of Cu.

• 한국재료학회지
• /
• 제12권7호
• /
• pp.545-549
• /
• 2002

Potassium-Calcium-Phosphate glasses in range $XCaO\cdot(50-X)K_2O$ \cdot $50P_2$$O^{5}$were investigated. Glass transition temperature(Tg) of prepared glasses were below $520^{\circ}C$, thermal expansion coefficient from $270.3$\times$10^{7}$ to $604.5$\times$10^{7}$/$^{\circ}C$. The structure of XCaO.(50-X)$K_2$O\cdot$50P_2$$O^{5}$ glasses were examined by FT-IR spectroscopy indirectly. As CaO was increased, Ts, Tg, P-O-P bonding strength and chemical durability were increased. Glass surface change was observed with increasing dissolution time using bulk specimen, weight loss and pH change were measured as function of the dissolution time.

• 한국세라믹학회지
• /
• 제32권10호
• /
• pp.1093-1102
• /
• 1995

Water-soluble phosphate glasses containing Ag or Cu ion were prepared through melting process. Then the powdered glass samples were dissolved in D.I. water at room temperature with changing the dissolution time. In terms with the glass composition, dissolution characteristics, bactericidal effects and cytotoxicities were investigated. Dissolved amounts increased uniformly with dissolution time, and the dissolution rate was higher for ternary glass than for binary glass and with less metal oxide amount. And the dissolution rate of the glass with Ag ion was higher than that with Cu ion, and the bactericidal effect of the glass with Ag ion was also greater. Solution with more than 25 ppm of Ag was observed to have strong cytotoxicity to L929, and solutions of lower Ag concentration or with Cu seemed to have little cytotoxicity.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.13-22
• /
• 1997

은 이온과 구리 이온을 동시에 함유하는 살균용 인산염계 수용성 유리를 용융법으로 제조하였다. 분말상의 유리 시편을 상온의 증류수에 넣어 조성과 시간에 따른 용해 특성을, bulk상 시편에 대해서는 용해 전.후의 표면변화를 각각 관찰하였고, 살균 효과 및 세포독성을 평가하였다. 은 이온:구리 이온=1:1인 조성에서 최대 용해량을 나타내었으며 용해거동은 초기부터 total dissolution이 지배적이었다. 시간의 경과에 따라 용해는 진행이 되지만, 표면에 생성되는 새로운 층은 관찰되지 않았다. Pseudomonas sp, e. coli, staphylococcus aureus, 및 salmonella균에 대한 살균 효과는 용해량의 증가에 따라 증가하여 우수한 살균효과를 나타내었다. L929 세포에 대한 독성 실험 결과, 은 이온의 농도가 10ppm이상에서만 독성을 나타내었다.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.251-260
• /
• 1988

$10Li_2O$.$(90-x)B_2O_3$.$xSiO_2$ 기초유리에 $Al_2O_3$ 또는 $MoO_3$를 첨가한 유리를 열처리한 후 열수 또는 산처리하여 이온교환성 다공질 유리를 제조하였다. 그리고 $Al_2O_3$ 또는 $MoO_3$ 첨가가 분상과 양이온교환능(CEC)에 미치는 영향을 조사하였다. 이들 유리의 분상최적조건은 48$0^{\circ}C$, 10시간 열처리하였다. 분상은 $Al_2O_3$ 10mol%까지는 급격히 억제되고 그 이후에는 분상억제 효과가 완화되었다. 양이온교환능의 최대값은 $1OLi_2O$.$45B_2O_3$.$45SiO_2＋7.5Al_2O_3$ 조성유리를 열수처리한 다공질유리에서 약 252meq/100g을 나타냈으며 이 유리의 세공평균반경은 약 16.3A이었다. $MoO_3$ 첨가는 분상과 용출속도를 증가시켰다. $MoO_3$첨가에 의해 다공질유리의 세공반경과 세공용적이 크게 증가하는 것으로 보아 $MoO_3$는 유리의 붕산염상중의 실리카 농도를 낮추고 용출처리중 실리카를 수용성 착체로 형성시키는 효과가 있다고 생각된다.

• 대한화장품학회지
• /
• 제37권4호
• /
• pp.347-350
• /
• 2011

바이오필름은 부유 미생물이 피부 표면에 부착되어 형성된 미생물 집락이며 형질적 생화학적 특성에서 부유상태와는 차이가 있다. 바이오필름으로 증식하는 미생물은 부유 상태의 미생물 보다 숙주의 방어나 항생제에 대한 저항성이 훨씬 높기 때문에 바이오필름이 형성되면 감염 상태를 치료하기 위해 더욱 많은 항생제를 사용해야 한다. 따라서 감염된 세균의 내성을 피하면서 치료를 하기 위해서는 단순히 세균을 사멸하는 것이 아니라 표적을 달리하는 새로운 전략이 필요하다. 이번 연구에서는 아토피 등 염증성 피부 질환의 원인균의 S. aureus의 바이오필름을 억제하는 기작에 초점을 맞추어 연구를 진행하였다. 이 연구의 목적은 S. aureus의 바이오필름의 형성을 억제하여 피부질환을 조절할수 있는 후보 물질을 찾는 데에 있다. 슬라이드글라스를 human placental 콜라겐으로 코팅고 시험 물질과 함께 배양하여 억제된 바이오필름의 양을 crystal violet 염색법으로 측정하여 정량적으로 측정하였다. 이 실험에서는 표준균인 S. aureus ATCC 6538 strain이 사용되었다. 실험 결과 편백다당체가 바이오필름의 형성을 강하게 억제하였으며 녹차다당체와 황촉규근은 오히려 바이오필름의 형성을 촉진하였다. 자일리톨은 1 %의 낮은 농도에서는 바이오필름을 촉진하나 그 이상의 높은 농도인 3 %와 5 %에서는 억제하여 농도 의존적인 결과를 보였다.