• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 추계 학술논문 발표대회
• /
• pp.107-108
• /
• 2017

The purpose of this study is to derive the optimum water absorbing curing time. It was found that the cement paste compressive strength was increased with the water absorbing ratio up to 40%, but the compressive strength was slightly lower when the catch level was over 50%. It is considered that the superfluous water did not react and remained in the inside of the specimen, causing microcracks in the inside due to the high temperature curing, resulting in a decrease in strength. Therefore, it is considered that the optimum catcher curing time for improving the strength through catcher curing is when the catcher reaches 40%.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.27-28
• /
• 2019

In this study, the characteristics of compressive strength of ultra high strength concrete supplied with moisture from outside by vacuum water absorbing curing method were investigated. Specimens were prepared by replacing the binder(Silifa fume and GGBS) by 25 wt% with respect to the weight of cement at W/B 0.16. Each specimen was subjected to water Vacuum absorbing curing time 0 min, 30 min, 60 min, 90 min and 120 minutes immediately after the demolding. Curing was performed at $20^{\circ}C$ Air-dry curing, $90^{\circ}C$ steam curing, $90^{\circ}C$ steam curing and $180^{\circ}C$ autoclave curing. Experimental results showed that water absorbing degree increased with increasing water absorbing curing time, and BS25 sample had higher water absorbing degree than SF25 sample at same time. Compressive strength tended to increase up to about 40% in water absorbing degree, but compressive strength decreased again in water absorbing more than 40%.

• 펄프종이기술
• /
• 제40권1호
• /
• pp.47-54
• /
• 2008

As the demands of environment protection increases, the pulp mold container is developed to substitute for EPS (expanded polystyrene) as a shock absorbing packaging material. The water-absorbing ratio and mechanical properties such as tensile strength and compressive strength of pulp mold are important factors to evaluate its shock absorbing characteristics. Influences of mixing ratios of ONP (old newspaper) and OCC (old corrugated container) on physical properties of pulp mold were investigated at various conditions of temperature and relative humidity. The optimum mixing ratio of ONP and OCC was also searched based on physical properties. The results showed that when relative humidity was increased from 60% to 90%, the water absorption ratio of pulp mold increased significantly, tensile strength decreased 20$\sim$30%, and compressive strength decreased 10$\sim$20%. In addition, the optimum mixing ratio of ONP and OCC was found to be 50%:50%.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2007년도 춘계학술대회논문집
• /
• pp.285-297
• /
• 2007

As the demands of environment protection increase, the pulp mold container is developed to substitute for the plastic cushion materials like EPS(expanded poly styrene). The water-absorbing ratio, tensile strength and compressive strength of pulp mold are important factors to evaluate its shock absorbing characteristics. The study was performed to investigate the effects of the mechanical property changes on the various conditions of temperature and relative humidity for pulp mold containers made of mixed materials on ONP(old newspaper) and OCC(old corrugated container). This study also is evaluated the optimized mixing ratio of materials for making pulp mold by analyzing the changes of physical properties according to a various procured temperature and relative humidity conditions. The results show that the water absorption ratio of sample increased significantly, and tensile strength decreased $20{\sim}30%$, compressive strength decreased $10{\sim}20%$ by increasing relative humidity condition. And the results show that the ONP 50% and OCC 50% was optimized mixing ratio according to the samples.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.211-216
• /
• 2002

Recently, the more the PET bottles are needed, the more waste PET bottles were produced. So, if there was no suitable recycling, that was contaminate our environment and use up the natural resources. This paper deals with the artificial lightweight aggregate(ALA), made of waste PET bottles, and the properties of concrete replaced with ALA. As a result of experiment, it is shown that the specific gravity of PBLA is 1.39, the unit volume weight is 844 kg/$cm^3$, and absorbing rate is 0. In absorbing rate test, the rate is 10 % increased by replacing of 20 % PBLA and the mixture rate for water and cement is 44.6 % and 51.2 %, in case target strength for 240kgf/$cm^2$, and 270kg/$cm^2$, by added PBLA 75 % and 50 % respectively. So, to obtain a certain target strength, appropriate W/C ratio is required the replacement ratio of PBLA.

• 한국지반신소재학회논문집
• /
• 제22권4호
• /
• pp.35-42
• /
• 2023

본 연구에서는 유기오염물의 흡수가 가능한 차수재의 반응재료에 대하여 지중 매입 재료로서의 적용성을 평가하기 위해 오염물의 접촉에 의한 강도 특성 변화를 평가하였으며, 강도 평가는 일축압축시험 결과를 이용하였다. 시험 결과, 오염물 종류에 따른 반응재료의 강도는 물 > TCE > TPH의 순서로 확인되었다. 그러나 폴리노보넨의 구성비가 12% 이하에서는 TPH의 강도가 TCE에 비하여 크게 나타났다. 물로 접촉된 반응재료는 폴리노보넨의 구성비가 작을수록 강도가 지속적으로 감소하였지만, TCE 및 TPH와 접촉된 반응재료의 강도는 폴리노보넨의 구성비가 30%에서 21%까지 작아질수록 증가하다가 이후에는 감소하였다. 즉, 지중에서 발생되는 응력 조건에 따라 오염물의 접촉에 의한 강도를 고려하여 반응재료의 최적 구성비가 적용되어야 한다.

• 한국건축시공학회지
• /
• 제9권5호
• /
• pp.63-70
• /
• 2009

본 연구는 실리카와 칼슘의 수열합성 반응에 의해 제조하는 흡음형 경량기포콘크리트의 개발에 관한 일련의 연구이다. 원료는 석탄화력발전소의 부산물로 발생되는 바텀애시를 미분화한 것을 실리카원으로 사용하였고, 1종보통포틀랜드시멘트, 알루미나 시멘트, 소석회를 칼슘원으로 사용하였다. 경화체 내에서 연속기포를 형성하기 위하여 기포제를 이용하여 발포한 기포를 슬러리와 혼합한 후 몰드에 타설하는 선발포 방식으로 시험체를 제조하였다. 실험인자는 물분체비, 기포제 희석비, 기포 혼입비로 설정하였고 이들 요인이 흡음형 기포콘크리트의 압축강도, 절건밀도, 전공극률, 연속공극률, 흡음성능에 미치는 영향을 검토하였다. 실험결과 기포콘크리트의 흡음성능은 거의 모든 실험 수준에서 흡음재료를 위한 NRC의 요구성능을 만족하는 것으로 나타났다. 기포비는 가장 지배적인 인자이고 이 연구에서 기포콘크리트의 모든 특성에 현저하게 영향을 끼치는 것으로 나타났다. 물분체비는 압축강도와 절건밀도 뿐만 아니라 전공극률과 연속공극률에 거의 영향을 끼치지 않았고 기포제 희석비는 거의 모든 특성에 영향을 주지 않았다. 흡음성능과 흡수시간 및 연속공극률의 상관관계 분석결과 흡수시간은 연속공극률과의 상관성이 높은 것으로 나타났다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.460-463
• /
• 2003

In this paper, we present the properties of water absorption of elastic epoxy for high voltage. The ratio of water absorption shows linearly increase according to ${\sqrt}t$ till 66 hours. And rigid epoxy is 0.053 [%], elastic epoxy at addictives 35 [phr] is 0.309 and it at addictives 70 [phr] is 0.44 [%]. The reason where absorption of elastic epoxy is high is because of micro void. It can be confirmed by SEM analysis. Dieletric constant increased linearly by addictives' concentration and tans is also increased by addictives' concentration.

• Elastomers and Composites
• /
• 제47권2호
• /
• pp.141-147
• /
• 2012

실리콘 수지는 소수성이 강한 고분자이기 때문에 수분을 흡수하는 기능이 전혀 없다. 하지만 고흡수성 수지(Super Absorbent Polymer)를 첨가제로 사용하면 기존의 실리콘보다 월등한 흡수성을 갖게 된다. 본 연구에서는 무정형 형태의 입자 크기가 다른 아크릴계 고흡수성 수지 3가지를 선택하여 배합비를 설정하고 2액형 타입의 의료용 실리콘 소재에 적용해서 수분을 흡수하는 기능을 갖는 새로운 실리콘 소재를 개발하였다. 고흡수성 수지의 첨가에 의한 실리콘 수지의 제조시 입자 사이즈와 함량을 달리하면서 인장, 인열, 압축, 경도에 대한 기계적 물성 변화를 알아보았으며, 시간에 따른 실리콘 수지의 흡수성을 측정하였다. 또한 전자 현미경을 통해 고흡수성 수지의 입자형태와 실리콘 수지와의 분포도를 관찰하였다.

• 한국재료학회지
• /
• 제25권11호
• /
• pp.590-597
• /
• 2015

In this article, poly methyl triethoxy silane was compounded with an inorganic waterproof admixture at a certain ratio to improve the performance of gypsum products; a new type of high-efficiency compound water-proofing additive was also investigated. Furthermore, the waterproof mechanism and the various properties on the hardened gypsum plaster were investigated in detail by XRD and SEM. The results show that the intenerate coefficient of gypsum plaster increased to more than 0.9; the water absorbing rate decreased to less than 10 %. Both the bending strength and the compressive strength of gypsum plaster increased by various degrees. The intenerate coefficient reached a maximum value of 0.73 and the strength of the samples showed almost no change when 5% cement alone was added. In this new type of the high-efficiency compound with waterproof additive, the optimal technological parameters for formulas were obtained to be: 5% cement, 18 % mineral powder, and 0.8% poly methyl triethoxy silane, to compound gypsum plaster. Meanwhile, the production of high performance gypsum as a building material has become possible.