• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.7 s.238
• /
• pp.947-954
• /
• 2005

The purpose of this study is to develop failure pressure evaluation models, which are applicable to straight pipes and elbows containing an internally wall thinning defect induced by flow-accelerated-corrosion (FAC). In this study, thus, three dimensional finite element (FE) analyses are performed to investigate the dependences of failure pressure of internally wall thinned pipe on the defect shape, the pipe geometry, and the defect location and bend radius of elbow. Also, the existing failure pressure assessment models for externally wall thinned pipes are examined. Based on these, the new models for assessing failure pressure of piping components with an internally wall thinning defect are proposed. Comparison of failure pressure, predicted by proposed models, with FE analysis result shows good agreement regardless of pipe type, defect shape, and defect location and bend radius.

• Journal of the Korean Society of Safety
• /
• v.18 no.4
• /
• pp.28-34
• /
• 2003

In the present study, three-dimensional finite element analysis was performed to investigate the effects of internal wall thinning defect on the failure pressure of elbow in the piping system and to develop the failure pressure evaluation model. From the results of finite element analysis, the failure pressure was derived by employing local stress criteria, and the effects of thinning location, bend radius, and defect geometry on the failure pressure of internally wall thinned elbow were investigated. Also, based on these investigations and previous model developed to estimate the failure pressure of elbow with an external pitting defect, the failure pressure evaluation model to be applicable to the elbow containing an internal thinning defect was proposed and compared with the results of finite element analysis. The failure pressure calculated by the model agreed well with the results of finite element analysis.

• Journal of the Korean Society of Safety
• /
• v.30 no.1
• /
• pp.144-149
• /
• 2015

This study aims to quantitatively evaluate failure pressure of wall-thinned elbow under combined load along with internal pressure, by conducting real-scale burst test and finite element analysis together. For quantitative evaluation, failure pressure data was extracted from the real-scale burst test first, and then finite element analysis was carried out to compare with the test result. For the test, the wall-thinning defect of the extrados or intrados inside the center of 90-degree elbow was considered and the loading modes to open or close the specimen maintaining a certain load or displacement were applied. Internal pressure was applied until failure occurred. As a result, when the bending load was applied under the load control condition, the intrados of the defect was more affected by failure pressure than the extrados, and the opening mode was more vulnerable to failure pressure than the closing mode. When the bending load was applied under the displacement control, it was hardly affected by failure pressure though it was slightly different from the defect position. The result of the finite element analysis showed a similar aspect with the test. Moreover, when major factors such as material properties and pipeline thickness were calibrated to accurate values, the analytical results was more similar to the test results.

• Nuclear Engineering and Technology
• /
• v.55 no.3
• /
• pp.947-957
• /
• 2023

Curved cylindrical structures such as elbows have a non-uniform thickness distribution due to their fabrication process, and as a result have a number of complex mode shapes, including circumferential and axial nodal patterns. In nuclear power plants, material degradation is induced in pipes by flow accelerated erosion and corrosion, causing the wall thickness of carbon steel elbows to gradually thin. The corresponding frequencies of each mode shape vary according to the wall thinning state. Therefore, the thinning state can be estimated by monitoring the varying modal characteristics of the elbow. This study investigated the varying modal characteristics of artificially thinned carbon steel elbows for each thinning state using numerical simulation and experimental methods (MRIT, Multiple Reference Impact Test). The natural frequencies of specified mode shapes were extracted, and results confirmed they linearly decreased with increasing thinning. In addition, by comparing single FRF (Frequency Response Function) data with the results of MRIT, a concise and cost effective thinning estimation method was suggested.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.9
• /
• pp.1293-1298
• /
• 2010

In most power plants, wall thinning in carbon-steel pipes due to flow-accelerated corrosion is one of the major aging phenomena, and it reduces the load-carrying capacity of the piping system. Various types of wall-thinning defects were manufactured in real-scale elbows, and monotonic in-plane bending tests were performed under internal pressure to evaluate the failure behavior of the elbows. In this paper, the behavior of elastic and plastic limit leads of locally thinned elbows in a real-scale failure test is presented. The loads determined on the basis of TES (twice elastic slope) were considered to be the limit loads of locally thinned elbows so that the integrity of the thinned elbows could be maintained, even when a small amount of plastic deformation might have occurred.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.26 no.5
• /
• pp.321-328
• /
• 2006

In this study, the deformation oi wall thinning elbow is measured and the position of the internal thinning defect is found out by shearography. Shearography is an optical method which has applied to nondestructive testing (NDT) and the strain/stress and deformation analysis. This technique has the merit of the directly measuring the first derivative of displacement with sensitivity which can be adjusted by handling the tilt mirror in the interferometer. In this paper, we tested carbon steel pipe locally wall thinned and loaded internal pressure and the shearography was applied to measure the out-of-plane deformation of wall thinning elbow and to investigate the internal thinning defect of it. From the results, it was confirmed that this technique is proper to the practical application on the pipe line system with internal defect.

• Corrosion Science and Technology
• /
• v.6 no.3
• /
• pp.112-119
• /
• 2007

This paper presents the importance of corrosion control and protection technology with a real case study of heater tube rupture damaged by High temperature H2S-H2 corrosion in the refinery. The heater was operated at the Hydrocracking unit and the operation temperature and pressure was $340^{\circ}C$ and $18kg/cm^{3}$ respectively. Top side of the convection tube was thinned by high temperature hydrogen sulfide and hydrogen gas as a uniform corrosion and finally ruptured under operation pressure. Damaged area (Convection tube zone) was blocked by protection wall, so it was impossible to inspect with conventional nondestructive examination. Instead the elbow area which is out of the protection wall was inspected regularly to evaluate the corrosion rate of convection tube indirectly. However the operation temperature and the phase of the process stream was different between inside the chamber and outside the chamber. As a result, it caused severe corrosion to the horizontal convection tube inside the chamber comparing to the elbow outside the chamber. Finally convection tube was corroded more rapidly than the elbow and ruptured after 13 years operation. Because of the rupture, the heater was totally burned and the operation was stopped for 3 months until it has been reconstructed. To prevent this kind of corrosion problem and accident, corrosion control should be strengthened and protection technology should be improved.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.27-28
• /
• 2006

This study performs to investigate deformation of wall thinning pipe and to find out the position of the internal thinning defect by shearography. Shearography is one of optical methods those have applied to nondestructive testing (NDT) and the strain/stress analysis. This technique has the merit of the directly measuring the first derivative of displacement, sensitivity of which can be adjusted by the handling of optical component in interferometer. In this paper, we tested carbon steel pipe locally wall thinned and loaded internal pressure and developed the nondestructive out-of-plane deformation analysis technique fur internal thinning defect of elbow by shearography. From the results, it was confirmed that this technique is proper to the practical application on the pipe line system with internal defect.