• Journal of the Korean Wood Science and Technology
• /
• v.27 no.3
• /
• pp.39-50
• /
• 1999

This research was carried out to investigate the development of fire-retardancy treatment technology and performance evaluation of fire-retardant treated plywoods. Radiata pine, keruing, dillenia, calophyllum and terminalia veneers were treated by normal(conventional) pressure soak(NPS) and vacuum-pressure-soak(VPS) using 20% water solution of diammonium phosphate. Then, 4.8mm thick, 3ply plywoods were fabricated with combination of fire-retardant treated, untreated or water-immersion types and several composition types of radiata pine and keruing veneers, i,e. the uniform and the mixed types in species composition, and the homogenious and the alternate layer types in veneer treatment. In composed species, the retention and the treatment effects of fire-retardant chemicals III radiata pine was still greater than those of keruing. The effect of VPS treatment was larger than that of NPS treatment, however, adhesive bonding strength and bending strength of plywoods treated by these two methods were not necessarily lowered, compared to those of untreated plywood. And also, fire endurance performance of the urea melamine resin-bonded plywood was greater than that of the phenol resin-bonded plywood. In result, the appropriate combination in veneer species and layer as well as alternate fire-retardant treatments would be more efficiently available in service.

• Journal of the Korea Furniture Society
• /
• v.14 no.2
• /
• pp.21-29
• /
• 2003

This study was carried out to investigate characteristics of plywood overlaid with softwood veneers densified by resin impregnation and compression. The resin impregnability of Korean pine veneer under atmospheric pressure soaking was greater than that of larch, and impregnability of melamine resin was slightly greater than phenolic resin. It was suggested that resin impregnation ratio was affected by density and thickness of veneer. The largest melamine resin impregnation ratio of 50.7% was obtained with 1.26mm thick Korean pine veneer, and the lowest phenolic resin impregnation ratio of 11.7% with 3.41mm thick larch veneer. Therefore, it was suggested that the vacuum-pres sure-soak treatment is required at thick larch veneer. In densifying resin-impregnated veneers, densification ratio from 13.4 to 31.2% was obtained by high pressure from 15.6 to $20.8kgf/cm^2$. Impregnation of melamine resin also showed relatively greater at densification than that of phenolic resin. So it showed the degree of densification of about 20% or greater. It was seemed that adhesive bonding strength of plywood(base panel) which was directly pressed and overlaid with resin-impregnated veneer was affected by resin tackiness after resin impregnation followed by semi-drying. In laboratory scale, melamine resin impregnation was more favorable for the development of adhesive bonding strength owing to moisture control.