• Journal of the Korean Wood Science and Technology
• /
• v.12 no.1
• /
• pp.38-43
• /
• 1984

Water soluble urea-melamine-phenol copolymer adhesive manufactured with 80 percent of urea resin contents was manufactured by different molar ratio for a high temperature curing type, and their properties and strengthes were examined through manufactures of plywood with Kapur (Dryobalanops spp.) veneers. The results are summarized as follows: 1. Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.78 to 0.84 and their moisture contents met the KS requirement. 2. In dry and wet shear strength, $U_{80}M_{10}P_{10}$ copolymer resin showed the highest value and urea resin was the lowest, indicating that melamine and phenol were effective for increasing glue shear strength of urea resin. 3. In case of glue shear strength after boiling test, phenolic resin was the nest and melamine was not so effective as phenol on reinforcement of boiling water resistance of urea resin.

• Journal of Korean Society of Forest Science
• /
• v.60 no.1
• /
• pp.51-57
• /
• 1983

Properties and glue shear strength of each water soluble rues-phenol copolymer adhesive and phenolic resin adhesive were examined as a high temperature curing binder through the manufacture of plywood made of Kapur veneer. The former has different molar ratio and the latter was made from different catalyst method. The results are summarized as follows: 1) Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.67 to 0.82 and their moisture contents met the K.S. standard 2) In dry and wet shear strength, adhesives with 60 percent of non volatile content showed higher values than those with 50 percent except phenolic resin. Urea-phenol copolymer resin with 20 percent of phenol content exhibited the highest, and that with 70 percent the lowest. Filling effect of wood flour on the bonding strength is great in urea-phenol copolymer resin with more than 50 percent of phenol content, especially significant in 50 percent of non volatile content including alkali catalyst phenolic resin. Alkali and acid catalyst methods were the highest among the adhesive manufacture methods. In wet strength, urea resin belongs to the lowest group. 3) In glue shear strength after boiling and drying test, no method for manufacturing phenolic formaldehyde resin adhesive was stronger than alkali and acid catalyst methods. Phenolic resin made from alkali catalyst method needs a wood flour filler to improve the bonding quality. Urea-phenol copolymer resin with 10 percent of phenol content showed the reasonable water resistance.