• Journal of the Korean Wood Science and Technology
• /
• v.47 no.2
• /
• pp.200-209
• /
• 2019

To improve the water resistance of melamine-urea-formaldehyde (MUF) resins, different levels of blocked polymeric 4,4 diphenyl methane diisocyanate (B-pMDI) were blended with MUF resins to prepare B-pMDI/MUF hybrid adhesives, and their adhesion performances were evaluated for the surface lamination of fancy veneer on plywood. FT-IR spectra showed that the de-blocked -NCO groups reacted with the -OH of hydroxymethyl groups of the MUF resins to form urethane bonds at 2% B-pMDI/MUF, which was detected before and after their hydrolysis. The mass loss after the hydrolysis consistently decreased as the B-pMDI level increased, indicating an improvement in the water resistance. As the B-pMDI level increased, the activation energy of hybrid adhesives decreased, which improved the reactivity of the hybrid adhesives. Additionally, the water resistance improvement of the hybrid adhesives increased the tensile shear strength of the surface laminated plywood in semi-water proof and water-proof by 23 % and 8 %, respectively, at 2% B-pMDI level. This was likely due to the urethane linkages in the hybrid adhesives. However, the formaldehyde emission from plywood panels bonded with the hybrid adhesives increased in the dry state, indicating incomplete curing of the hybrid adhesives.

• Journal of the Korean Wood Science and Technology
• /
• v.9 no.3
• /
• pp.16-23
• /
• 1981

This study has been carried out to make a comparative study for the adhesive control methods specifically developed for application to formaldehyde. The method for formaldehyde determination used in this report is the improved chromo tropic acid determination. The results are summarized as follows: 1. The soaking treatment in aqueous solution of urea wok the most scavenging effect on the formaldehyde release from a plywood sample glued with a urea formaldehyde adhesive, and other removal treatment such as resorcinol, albumine-, and hardener-treatment gave significant reduction too. 2. In glue shear strength of dry test, 2% of resorcinol treatment and soaking treatment showed the highest strength and all the other treatment met the standard, but in hot water soaking test, 2% of resorcinol treatment gave the best results, on the other hand, adding the hardener showed the lowest strength and failed in meeting the standard. 3. Air dried moisture content of all treated plywood met the standard which calls for 13% or bellow. 4. In this comparative study, we can make a strong combination each other or go into the details of one treatment for the best result through the more study.

• Journal of Photoscience
• /
• v.6 no.4
• /
• pp.177-181
• /
• 1999

The photochemical transformation of carbon monoxide in aqueous ammonia solution has been investigated at 25${\pm}$0.1$^{\circ}C$ using 184.9 nm UV light. Amination and carbonylation processes were carried out by irradiating the aqueous ammonia solution saturated with carbon monoxide, and the formation of formamide, urea, hexamethylenetetramine, formaldehyde, glyoxal and hydrazine was observed. The formation of hydrazine was affected by the presence of ammonia, and the formation of carbonyl compounds such as formaldehyde and glyoxal was influenced by the presence of carbon monoxide. The formation of formamide, urea and hexamethylenetetramine was affected by both ammonia and carbon monoxide. The initial quantum yields of the products were determined and probable mechanisms for the photochemical reaction were presented on the basis of product analysis.

• Journal of Adhesion and Interface
• /
• v.13 no.2
• /
• pp.85-88
• /
• 2012

In this paper, the curing reaction of UF resins was investigated by a real time FT-IR method. The curing temperature range of the UF resin was $25{\sim}200^{\circ}C$. It was found that the reactions of UF resin at different temperatures resultedin resins with different cross-linked structures. A real time FT-IR spectroscopy can be considered as a good routine analytical tool for following the progress of UF resin curing.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2000.04a
• /
• pp.259-260
• /
• 2000

알데히드류는 실내 가정의 건축물 단열재, 실내가구의 칠, 접착제, 하드보드, 악취 제거제, 제지 등 생활 용품에서 공업용품에 이르기까지 광범위하게 사용되며, 그 사용량도 증가되고 있다. 특히, formaldehyde는 urea-와 Phenol-formaldehyde 수지를 합성하는 주요 화합물질이다. 알데히드류 중 포름알데히드는 1ppm 또는 그 이하의 농도로 노출될 경우, 눈, 코, 목의 자극을 유발하고, 농도에 따라서 피부 알레르기, 두통, 메스꺼움, 흥부 압박감, 기관지염, 폐염 및 폐부종을 야기하며, 동물 실험결과, 미국 환경보호처에서는 인체 발암 가능성 물질로 분류하고 있다(US EPA, 1999). (중략)

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2002.05a
• /
• pp.457-460
• /
• 2002

현재 건축단열재, 흡음재, 바닥재로 사용되는 panel 성형, 제작하기 위해 다종의 유기고분자 matrix가 사용되고 있으며 polyurethane, vinyl acetate, urea-formaldehyde resin 또는 melamine-formaldehyde, phenol-form aldehyde resin 등을 사용하고 있으나 이러한 고분자 matrix를 사용한 건축용 panel의 경우 화재시 유독 gas와 더불어 급격한 화재전파의 매개체로 사용될 수 있어 난연제 첨가로 이러한 현상을 억제하고 있다.(중략)

• Journal of Sericultural and Entomological Science
• /
• v.27 no.2
• /
• pp.47-53
• /
• 1985

The studies on the reaction of Urea-Formaldehyde(UF) resin with silk fabric were studied, and the final results summarized as below; 1. The pH and UF molar ratio for preparing liquid resin was found at pH 4-5 and UF molar ration 1:2 and above. 2. The weight gains were increased with respect to increase in concentration of UF resin solution, while moisture regains were decreased. 3. The weight gains were significant high in case of wet pick up 70%. 4. The weight gains were increased with respect to increase in curing temperature and the amount of catalyst((NH4)2SO4) found was 2.5% on the weight of Dimethylol urea and Hydrochloric acid was 1%, Tartaric acid was 10%. 5. The effect of different catalyst on wash fastness of UF resin was good where as in case of acidic catalyst was significantly high. 6. The weight gains with different catalyst was high where as in case of potential acid catalyst was significantly high. 7. The crease recovery are increased with the increase of the weight gain of silk fabric and also stiffness are increased.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.4
• /
• pp.31-36
• /
• 2006

This study was conducted to improve the bond strength of plywood bonded with F/U molar ratio urea-formaldehyde (UF) resins modified with the selected FGMDI prepolymer contents for various purposes. The amount of FGMDI was mixed with liquid UF resin at 0 wt% (as control), 2 wt%, 5 wt%, 10 wt%, 25 wt%, and 50 wt% based on the resin solids. As results, in bonding strength, plywood with F/U molar ratio of 1.4 showed the highest value in Type 2 test and all molar ratio UF resins modified with over 25 wt% of the FGMDI showed more than $11kgf/cm^2$, which was satisfied the minimum requirement of KS standard, $7.5kgf/cm^2$, after Type1.5 testing. As F/U molar ratio was increased and the FGMDI addition in the UF resin was increased, average reduction rate of Type 1.5 bonding strength compared with Type 2 was significantly decreased.

• Journal of Korean Society of Forest Science
• /
• v.94 no.6
• /
• pp.476-480
• /
• 2005

Agricultural straws such as rice and barley were used as partial replacement of raw materials for particleboard (PB) manufacture. A melamine-urea-formaldehyde (MUF) resin, based on 5 percent melamine addition of the resin solids weight, was synthesized in the laboratory for the bonding of PB. PBs were made using two straw particles based on 10, 20, 30, 40% oven dry weight addition with MUF resin. PBs were tested for physical and mechanical properties, and water soak dimensional stability. The results indicated that as rice and barley straws addition level were increased, the properties of IB, MOR and dimensional stabilities such as thickness swell and water absorption were decreased. Overall, the agricultural straws can be used at 15% substitution of raw materials for PB manufacture.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.5
• /
• pp.29-41
• /
• 2006

This study was to investigate the effect of adding additive as tannin, rice husk and charcoal, for reducing the formaldehyde emission level, on the adhesion properties of urea-formaldehyde (UF) resin for particleboard. We controlled the hot-pressing time, temperature and pressure to determine the bonding strength and formaldehyde emission. Blends of various UF resin/additives (tannin, rice husk and charcoal) compositions were prepared. To determine and compare the effect of additives (tannin, rice husk and charcoal) content, 0, 5, 10 and 15%, by weight of UF resin, were used. $NH_4Cl$ as hardener added. To determine the level of formaldehyde emission, we used the desiccator, perforator and 20 L-small chamber method. The formaldehyde emission level decreased with increased additions of additive (except rice husk). Also, increased hot-pressing time decreased formaldehyde emission level. At a charcoal replacement ratio of only 15%, the formaldehyde emission level is under F ✩ ✩ ✩ ✩ grade (emit < $0.3mg/{\ell}$). Curing of the high tannin additive content in this adhesive system indicated that the bonding strength increased. But, in the case of rice husk and charcoal, the bonding strength was much lower due to the inorganic substance. Furthermore, rice husk was poor in bonding strength as well as formaldehyde emission than tannin and charcoal.