• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.563-564
• /
• 2009

Ultra-High Performance Concrete (UHPC) compared to normal concrete is exhibiting extremely high strength characteristics with compressive strength and tensile strength reaching 200MPa and 15MPa, respectively. The mechanical characteristics of UHPC can be thus exploited advantageously in the construction of structure through the reduction of the cross-sectional area and fabrication of slim and light-weight of the structural members. In the case where the structural member is made of UHPC, the occurrence of crack can be prevented by releasing the restraint provided by the form in due time. This research performs parametric study of the failure characteristics of concrete such as failure energy and softening curve suggested by the viscous crack model approximating the failure of concrete. The scope of this research contains the results of tests performed to investigate the strength of UHPC during early elapsed time.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.61-64
• /
• 2006

Comparing with traditional high performance concrete, ultra high performance concrete (UHPC) has the property of high-tenacity. However, drying shrinkage and autogenous shrinkage can be arisen as the major defect to UHPC. In this study, therefore, it was tested to reduce drying shrinkage and autogeneous shrinkage by adding expanding admixture (EA) and shrinkage reducing agent (SRA). As a result, for a case drying shrinkage, the shrinkage was decreased by 94% when EA was exchanged, and it was decreased by 64% when SRA was added. For the case of autogenous shrinkage, the mortar was expanded at early age and the shrinkage was decreased by 87% when EA was exchanged, and the shrinkage was decreased by 70% when SRA was added.

• Advances in concrete construction
• /
• v.8 no.1
• /
• pp.21-31
• /
• 2019

The rich recipe of ultra high performance concrete (UHPC) offers the higher mechanical, durability and dense microstructure property. The variable like cement/sand ratio, amount of supplementary cementitious material, water/binder ratio, amount of fiber etc. alters the UHPC hardened properties to any extent. Therefore, to understand the effects of these variables on the performance of UHPC, inevitably a stage-wise development is required. In the present experimental study, the effect of sand/cement ratio, the addition of finer material (fly ash and quartz powder) and, hybrid fiber on the fresh, compressive and microstructural property of UHPC is evaluated. The experiment is conducted in three phases; the first phase evaluates the flow value and strength attainment of ingredients, the second phase evaluates the efficiency of finer materials (fly ash and quartz powder) to develop the UHPC and the third phase evaluate the effect of hybrid fiber on the flow value and strength of ultra high performance hybrid fiber reinforced concrete (UHP-HFRC). It has been seen that the addition of fly ash improves the flow value and compressive strength of UHPC as compared to quartz powder. Further, the usage of hybrid fiber in fly ash contained matrix decreases the flow value and improves the strength of the UHP-HFRC matrix. The dense interface between matrix and fiber and, a higher amount of calcium silicate hydrate (CSH) in fly ash contained UHP-HFRC is revealed by SEM and XRD respectively. The dense interface (bond between the fiber and the UHPC matrix) and the higher CSH formation are the reason for the improvement in the compressive strength of fly ash based UHP-HFRC. The differential thermal analysis (DTA/TGA) shows the similar type of mass loss pattern, however, the amount of mass loss differs in fly ash and quartz powder contained UHP-HFRC.

• Steel and Composite Structures
• /
• v.42 no.3
• /
• pp.325-351
• /
• 2022

This paper studies the lateral impact behavior of ultra-high performance fiber-reinforced concrete (UHPFRC) filled double-skin steel tubular (UHPFRCFDST) columns. The impact force, midspan deflection, and strain histories were recorded. Based on the test results, the influences of drop height, axial load, concrete type, and steel tube wall thickness on the impact resistance of UHPFRCFDST members were analyzed. LS-DYNA software was used to establish a finite element (FE) model of UHPFRC filled steel tubular members. The failure modes and histories of impact force and midspan deflection of specimens were obtained. The simulation results were compared to the test results, which demonstrated the accuracy of the finite element analysis (FEA) model. Finally, the effects of the steel tube thickness, impact energy, type of concrete and impact indenter shape, and void ratio on the lateral impact performances of the UHPFRCFDST columns were analyzed.

• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.283-290
• /
• 2015

This paper proposes a method for predicting flexural strength of hybrid steel fiber-reinforced ultra-high strength concrete beams. It includes an experimental test framework and associated numerical analyses. The experimental program includes flexural test results of hybrid steel fiber-reinforced ultra-high strength concrete beams with steel fiber content of 1.5% by volume. Tensile softening characteristics play an important role in the structural behavior of steel fiber-reinforced ultra high performance concrete. Tension softening modeling is carried out by using crack equation based on fictitious crack and inverse analysis in which load-crack mouth opening displacement relationship is considered. The comparison of moment-curvature curves of the numerical analysis results with the test results shows a reasonable agreement. Therefore, the numerical results confirms that good prediction of flexural behavior of steel fiber-reinforced ultra high strength concrete beams can be achieved by employing the proposed method.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.45-49
• /
• 1995

The fundamental properties of High Performance Concrete(HPC) were studied using high flowable portland cement which was developed at the Sangyong Cement Ind. Co.,Ltd. The results obtained are as follows. (1)The slump of HPC using high flowable portland cement maintains for 120min. (2)Ultra high strength greater than 800kg/$\textrm{cm}^2$ can be designed without using silica fume and other additives. (3)The value of drying shrinkage and adiabatic temperature rise of HPC are less than those of concrete made with OPC.

• Computers and Concrete
• /
• v.29 no.6
• /
• pp.407-418
• /
• 2022

This paper numerically investigates the effect of changes in the mechanical properties (displacement, strain, and stress) of the ultra-high-performance concrete (UHPC) without rebar and the reinforced concrete (RC) using steel re-bars. This reinforced concrete is mostly used in the concrete bridge decks. A mixture of sand, gravel, cement, water, steel fiber, superplasticizer, and micro silica was used to fabricate UHPC specimens. The extended finite element method as used in the ABAQUS software is applied for considering the mechanical properties of UHPC, RC, and ordinary concrete specimens. To calibrate the ABAQUS, some experimental tests have been carried out in the laboratory to measure the direct tensile strength of UHPC by the compressive-to-tensile load converting (CTLC) device. This device contains a concrete specimen and is mounted on a universal tensile testing apparatus. In the experiments, three types of mixed concrete were used for UHPC specimens. The tensile strength of these specimens ranges from 9.24 to 11.4 MPa, which is relatively high compared with ordinary concrete specimens, which have a tensile strength ranging from 2 to 5 MPa. In the experimental tests, the UHPC specimen of size 150×60×190 mm with a central hole of 75 mm (in diameter)×60 mm (in thickness) was specially made in the laboratory, and its direct tensile strength was measured by the CTLC device. However, the numerical simulation results for the tensile strength and failure mechanism of the UHPC were very close to those measured experimentally. From comparing the numerical and experimental results obtained in this study, it has been concluded that UHPC can be effectively used for bridge decks.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.5
• /
• pp.125-132
• /
• 2019

Ultra-high performance concrete (UHPC) has high compressive and tensile strengths due to the particle packing, and its ductile behavior can be ensured by utilizing steel fibers. However, since the UHPC members exhibit different characteristics of crack behavior and tensile behavior from normal concrete, the tension stiffening and cracking characteristics of the UHPC should be accurately modeled for the design and analysis of the UHPC members. In this study, uniaxial tension tests was conducted on the UHPC members with strands, where the test variables were diameter and reinforcing ratio of strands. Detailed analyses were also conducted to identify the tensile characteristics and crack behavior of the UHPC members. By comparing the test results with current code provisions and other models proposed by existing researchers, their applicability for estimation of crack behavior of the UHPC members was examined.

• Structural Engineering and Mechanics
• /
• v.82 no.1
• /
• pp.81-92
• /
• 2022

Ultra-high performance fiber reinforced concrete (UHPFRC) is a composite building material with high ductility, fatigue resistance, fracture toughness, durability, and energy absorption capacity. The aim of this study is to develop a nonlinear finite element model that can simulate the response of the UHPFRC beam exposed to impact loads. A nonlinear finite element model was developed in ABAQUS to simulate the real response of UHPFRC beams. The numerical results showed that the model was highly successful to capture the experimental results of selected beams from the literature. A parametric study was carried out to investigate the effects of reinforcement ratio and impact velocity on the response of the UHPFRC beam in terms of midpoint displacement, impact load value, and residual load-carrying capacity. In the parametric study, the nonlinear analysis was performed in two steps for 12 different finite element models. In the first step, dynamic analysis was performed to monitor the response of the UHPFRC beam under impact loads. In the second step, static analysis was conducted to determine the residual load-carrying capacity of the beams. The parametric study has shown that the reinforcement ratio and the impact velocity affect maximum and residual displacement value substantially.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.351-357
• /
• 2022

In this study, offshore modular pier system using the ultra-high performance concrete was developed for the offshore construction environment. For the application of offshore modular pier system, the design, fabrication, and construction performance evaluation were performed using ultra-high performance concrete a compressive strength 120 MPa or more and a direct tensile strength 7 MPa or more. For offshore piers previously constructed with precast concrete, it was intended to verify the idea and possibility of solving errors due to position or vertical deformation during the driving of the foundation pile part during the construction stage. Furthermore, a offshore modular pier system was fabricated with ultra-high performance concrete for the construction performance evaluation. The results showed that a offshore modular pier system secured about 9 % of sectional performance of load bearing capacity under ultimate load conditions. If the offshore modular pier system developed through this study is utilized in the future, it is judged that competitiveness due to sufficient durability and constructability can be secured.