• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.241-242
• /
• 2002

Wear behavior or SiC-particle reinforced aluminum matrix composites (MMC) were investigated by pin-on-disk tests in vacuum with various pressures, argon, and air with various levels of humidity. The wear rate of 2024Al and MMC increased in the following order: in a vacuum at $5.0{\times}10^{-4}$ Pa, at 1.0Pa, in argon at 0% RH, in argon at 60% RH, in argon at 90% RH, in air at 0% RH, in air at 60% RH and in air at 90% RH. In other words, the influence or environment on wear becomes stronger in the following order: moisture, oxygen, and a combination of moisture and oxygen. In various environments, the difference of the wear rate of 2024Al and MMC was compared. In argon and air at 0% RH, the wear rates of MMC were higher than that of 2024Al. In contrast, in argon and air at 60, 90% RH, the wear rates of MMC were lower than that of 2024Al.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.45-52
• /
• 2002

The tribological role of mass transfer layer was studied with silver coatings under various ranges of load and sliding speed. Silver coating was performed with a functionally gradient coating method. Tests were performed in dry sliding conditions, using a ball-on-disk contact configuration, at the load of 0.0196-17.64 N and the sliding speed of 20-1,000 mm/s in ambient air. Optical microscope and EPMA analyses showed that contact surfaces were covered with the mass transfer layers of agglomerated wear particles depending upon the contact conditions, and they greatly influenced the tribological characteristics of the surfaces. However, the formation of mass transfer layer was suppressed as the sliding speed increased, and above a critical sliding speed, no mass transfer layer was able to form. For building up a general framework of tribological behavior of the coated silver films, all test data were summarized on a map whose axes are contact pressure and sliding speed.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.235-239
• /
• 2002

The objective of the experiment is to investigate the effect of microstructures of gray cast iron oil wear characteristics of automotive disc brakes. Six different gray cast iron rotors were manufactured by changing carbon equivalent and cooling rate. The change of DTV (disc thickness variation) before and after wear tests was measured to examine the wear properties according to the microstructures of gray iron discs since the DTV generation is caused by the circumferential uneven wear. Experimental results showed that the morphology of graphite flake and hardness in gray cast iron were crucially associated with the change of DTV. In particular, the DTV changes of rotor decrease when the length and area fraction of graphite flake in brake rotors increase and hardness of brake discs reduces.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.169-176
• /
• 2002

Axial crushing behavior of cylindrical shell Is utilized in the braking of the high-velocity impacting object. In this paper, truncated cone shape brake device is introduced. That is, thickness of the shell is increased gradually from the impacting end to the other end. A detailed experimental investigation on the quasi-static axial crushing behavior of truncated cone type brake devices has been performed. Specimens of various shape were tested to check the influence of design parameters such as length, radius, mean thickness, and conical angle of cylinder. Influence of the material properties were also investigated by adopting aluminum, low carbon steel, and stainless steel as constructing materials. By analyzing deformation procedures of the specimens, it is seen that conical angle influence the deformation mode and the sequence of the wrinkles generation. Braking distance and mean braking force of each specimen were predicted based on the crushing load measured from the tests.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2004년도 학술대회지
• /
• pp.339-349
• /
• 2004

The method for fatigue life prediction of ball bearing is proposed applying the algorithm of contact fatigue prediction based on stress analysis. In order to do this, a series of simulation such as initial surface stress analysis, EHL analysis, subsurface stress analysis and fatigue analysis are conducted from the loading at each ball location calculated for a bearing subjected to external bearing load and contact shape function. And uniaxial fatigue tests are performed to obtain fatigue parameter of AISI 52100 steel. It was found that since stress is usually higher at the inner raceway contact than at the outer raceway contact, fatigue failure occurs on the inner raceway first. When the fatigue life calculated in the stress-based method are compared with $L_{50}$ life of L-P model, Crossland criterion for the radial load increment is similar to $L_{50}$ life and Dang Van criterion for the axial load increment is similar. In the case of EHL contact. there is no difference of fatigue life between dry contact and EHL contact, when maximum Hertz pressure exceeds 2.5GPa.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2004년도 학술대회지
• /
• pp.31-36
• /
• 2004

In this paper, fretting wear tests were conducted in air at room temperature (RT) and in water at high temperature and high pressure (HTHP) environment to analyze the wear characteristic. As for the supporting condition between the tube and spring/dimple, the gap of 0.2 mm in air at RT and the normal force of 10 N and the slip of $50\;{\mu}\;m$ in water at HTHP were applied. Four different shapes of spring/dimple specimen (type A, B, C, D) were used. Detail eaxamination of wear scar was also performed using SEM micrographs. As a result, in the case of the spring of truncated wedge, severer wear occurs than the others. Protrusion part was found and larger in air at RT. It is thought that the difference in the wear volume and the protrusion is caused by the different wear mechanism corresponding to the different environment.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2004년도 학술대회지
• /
• pp.37-40
• /
• 2004

The impact/sliding wear tests have been performed in high temperature high pressure water in order to evaluate the effect of spring shape on the wear behavior of a spring supported tube for nuclear fuel fretting study. The results indicate that the tube wear volume and the size of the wear scar are closely related to each spring shape. From the analysis of the wear scar, it is possible to extract the real worn area (Aw) from the size of the wear scar (At). In addition, we found that the wear volume has a linear relation with the real worm area rather than the size of wear scar and this was only determined by each spring shape in the high temperature and pressure water condition. From the above results, it is possible to evaluate the wear resistant spring using the correlation between the variation of the real worn area and the wear behavior at each spring.

• 한국분말재료학회지
• /
• 제13권4호
• /
• pp.250-255
• /
• 2006

Wear behaviors of gas atomized and extruded Al-Si alloys were investigated using the dry sliding wear apparatus. The wear tests were conducted on Al-Si alloy discs against cast iron pins and vice versa at constant load of 10N with different sliding speed of 0.1, 0.3, 0.5m/s. In the case of Al-Si alloy discs slid against the cast iron pins, the wear rate slightly increased with increasing the sliding speed due to the abrasive wear occurred between Al-Si alloy discs and cast iron pins. Conversely, in the case of cast iron discs against Al-Si alloy pins, the wear rate decreased with increasing the sliding speed up to 0.3m/s. However, the wear rate increased with increasing the sliding speed from 0.3m/s to 0.5m/s. It could be due to adhesive wear behavior and abrasive wear behavior_between cast iron discs and Al-Si alloy pins.

• KSTLE International Journal
• /
• 제4권2호
• /
• pp.47-51
• /
• 2003

Sliding wear tests have been carried out in room temperature air and water in order to compare the wear resistance of Zr-xNb-xSn alloys of various alloying elements (Nb and Sn). The main focus was to quantitatively compare the wear properties of the recently developed Zr-xNb-xSn alloys with the commercial ones using the evaluation parameters of the wear resistance with the consideration of the worn area. As a result, the recently developed alloys had a similar wear resistance compared with the commercial ones. The dominant factor governing the wear resistance was the protruded volume of the wear debris that was formed on the worn area in the air condition, but the accommodation of the plastic deformation on the contact area in water. In addition, the worn area size appeared to be very different depending on the tested alloys. To evaluate the wear resistance of each test specimen, the ratio of the wear volume or the protruded volume to the worn area ($D_e$ or $D_p$) is investigated and proposed as the evaluation parameters of the wear resistance.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.183-190
• /
• 1997

The wear behaviors of $Al_2O_3-40%TiO_2$ deposited on casting aluminum alloy(ASTM A356) by plasma spray against SiC ball have been investigated experimentally. Friction and wear tests are carried out at room temperature. The friction coefficient of $Al_2O_3-40%TiO_2$ coating is lower than that of pure $Al_2O_3$ coating(APS). It is found that low friction correspond to low wear and high friction to high wear in the experimental result. The thickness of $Al_2O_3-40%TiO_2$ coatings indicated the existence of the optimal coating thickness. It is found that a voids and porosities of coating surface result in the crack generated. As the tensile stresses in coating increased with the increased friction coefficient. The columnar grain of coating will be fractured to achieve the critical stress. It is found that the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tensile and compressire under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. This crack propagation above interface is observed in SEM.