• 한국표면공학회지
• /
• 제48권6호
• /
• pp.315-321
• /
• 2015

Rare-earth zirconates, such as $La_2Zr_2O_7$ and $Gd_2Zr_2O_7$, have been investigated as one of the candidates for replacing conventional yttria-stabilized zirconia (YSZ) for thermal barrier coating (TBC) applications at higher turbine inlet temperatures. In this study, double-ceramic-layer (DCL) TBCs of YSZ 1st layer and $La_2Zr_2O_7$ top coat layer are fabricated by suspension plasma spray with serial liquid feeders. Microstructures, hardness profiles, and thermal durability of DCL-TBCs are also characterized. Fabricated DCL-TBCs of YSZ/$La_2Zr_2O_7$ exhibit excellent properties, such as adhesion strength (>25 MPa) and electrical thermal fatigue (~1429 cycles), which are comparable with TBCs fabricated by atmospheric plasma spray.

• 한국전기전자재료학회논문지
• /
• 제26권8호
• /
• pp.614-619
• /
• 2013

Recently, remote phosphor is reported for white LED enhancing of phosphor efficiency compared with conventional phosphor-based W-LED. In this study, Remote phosphor was produced by screen printing coating on glass substrate with phosphor contents rated paste and heat treatment. The paste consists of phosphor, lowest softening glass frit and organic binders. Remote phosphor can be well controlled by varying the phosphor content rated paste. After mounting remote phosphor on top of blue LED chip, CCT, CRI, and luminance efficiency were measured. The measurement results showed that CCT, CRI, and luminance efficiency were 6,645, 68, and 1,16l m/W in phosphor 80 wt.% remote phosphor sintered at $600^{\circ}C$.

• 한국가스학회지
• /
• 제18권4호
• /
• pp.35-43
• /
• 2014

무기질 바닥마감재로 기존 위험물 저장시설의 유기질계 바닥재의 문제점을 극복할 수 있다. 하지만 기존 시공된 바닥재를 제거하는데 있어서 제거기와 바닥재의 물리적 충돌에 의해 불꽃이 발생될 수 있다. 이러한 위험물 저장시설에서의 폭발에 의한 화재가 발생할 수 있는 위험요소를 억제하도록 기존 바닥재를 제거하지 않고 시공할 수 있다. 또한, 상도제는 대전방지제가 함유되어 있어 위험물 저장시설에 있어서 바닥마감재 시공 후 발생될 수 있는 정전기에 의한 2차적 피해를 억제 할 수 있어 효과적이다. 따라서 본 연구에서 개발된 무기질 바닥마감재는 점검자의 안전 관리적 측면과 경제적 측면에 효과가 있을 것으로 기대된다.

• Bulletin of the Korean Chemical Society
• /
• 제25권9호
• /
• pp.1371-1378
• /
• 2004

A porous stainless steel (SUS) as a substrate of silica composite membranes for hydrogen purification was used to improve mechanical strength of the membranes for industrial application. The SUS support was successfully modified by using submicron Ni powder, $SiO_2$ sols with particle size of 500 nm and 150 nm in turns. Silica top layer was coated on the modified supports under various preparation conditions such as calcination temperature, dipping time and repeating number of dipping-drying process. The calcination temperature for proper sintering was between H ttig temperature and Tamman temperature of the coating materials. Maximum hydrogen selectivity was investigated by changing dipping time. As repeating number of dipping-drying process increased, permeances of nitrogen and hydrogen were decreased and $H_2/N_2$ selectivity was increased due to the reduction of non-selective pinholes and mesopores. For the silica membrane prepared under optimized conditions, permeance of hydrogen was about $3\;{\times}\;10^{-5}\;cm^3{\cdot}cm^{-2}{\cdot}s^{-1}{\cdot}cmHg^{-1}$ combined with $H_2/N_2$ seletivity of about 20.

• Journal of Information Display
• /
• 제4권2호
• /
• pp.1-6
• /
• 2003

In this paper, we demonstrate that the organic electrophosphorescent device is driven by the organic thin film transistor with spin-coated photoacryl gate insulator. It was found that electrical output characteristics in our organic thin film transistors using the staggered-inverted top-contact structure showed the non-saturated slope in the saturation region and the sub-threshold nonlinearity in the triode region, where we obtained the maximum power luminance that was about 90 $cd/m^2$. Field effect mobility, threshold voltage, and on-off current ratio in 0.45 ${\mu}m$ thick gate dielectric layer were 0.17 $cm^2/Vs$, -7 V, and $10^6$ , respectively. In order to form polyimide as a gate insulator, vapor deposition polymerization process was also introduced instead of spin-coating process, where polyimide film was co-deposited by high-vacuum thermal evaporation from 4,4'-oxydiphthalic anhydride (ODPA) and 4,4'-oxydianiline (ODA) and cured at 150${\sqsubset}$for 1hr. It was also found that field effect mobility, threshold voltage, on-off current ratio, and sub-threshold slope with 0.45 ${\mu}m$ thick gate dielectric films were 0.134 $cm^2/Vs$, -7 V, and $10^6$ A/A, and 1 V/decade, respectively.

• 한국재료학회지
• /
• 제29권2호
• /
• pp.87-91
• /
• 2019

We report on stretchable electrochromic films of poly(3-hexylthiophene) (P3HT) fabricated on silver nanowire (AgNW) electrodes. AgNWs electrodes are prepared on polydimethylsiloxane (PDMS) substrates using a spray coater for stretchable electrochromic applications. On top of the AgNW electrode, poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) is introduced to ensure a stable resistance over the electrode under broad strain range by effectively suppressing the protrusion of AgNWs from PDMS. This bilayer electrode exhibits a high performance as a stretchable substrate in terms of sheet resistance increment by a factor of 1.6, tensile strain change to 40 %, and stretching cycles to 100 cycles. Furthermore, P3HT film spin-coated on the bilayer electrode shows a stable electrochromic coloration within an applied voltage, with a color contrast of 28.6 %, response time of 4-5 sec, and a coloration efficiency of $91.0cm^2/C$. These findings indicate that AgNWs/PEDOT:PSS bilayer on PDMS substrate electrode is highly suitable for transparent and stretchable electrochromic devices.

• 한국의류학회지
• /
• 제30권3호
• /
• pp.447-457
• /
• 2006

본 연구의 목적은 뉴욕의 플리마켓에서 구입한 매우 흥미로운 퀼트 텍스타일을 관찰함으로서 시작되었다. 흔하지 않은 스타일의 실크 인서트(Silk inserts)들로 구성된 이 퀼트를 본 연구자로 하여금 그 역사적 가치를 조명하고 문서기록을 남기며 보존처리하여 텍스타일 역사의 발전에 도움을 주는 것에 의의를 두고 있다. 본 연구의 방법으로는 관련된 문헌고찰과 뉴욕의 메트로폴리탄 박물관 J. R. Burdick 콜렉션을 방문하여 퀼트의 패치들이 silk insert라는 분석을 내렸고 Burdick의 연구(제작연대 1910$\∼$1912)에 의문을 갖고 연구자가 조사를 진행하여 이 연구과제에 사용된 silk inserts의 제작연대가 1934년경부터 1939년경이라는 결론을 내렸다. 다음 단계로는 이 직물의 상태를 분석하였는데, 실크 섬유의 상태가 바느질을 견디지 못하는 상태로 판단해 보존처리 방법으로는 접착제 Elvace 46575(vinyl acetate copolymer resin emulsion)를 Stabiltax에 코팅처리하여 직물을 강화처리하였다. 본 연구는 문서처리 되지 않은 미확인 직물의 역사적 의미 발견과 보존처리를 통해 후대의 텍스타일 연구자들에게 정보를 제공한다는 측면에서 가치가 있다고 사료된다.

• 멤브레인
• /
• 제22권2호
• /
• pp.120-127
• /
• 2012

본 연구에서는 혼합 자일렌에서 에틸벤젠을 분리하기 위하여 제올라이트 분리막을 이용하였다. 마이크로웨이브 합성 온도에 변화를 주어 제조한 TS-1 제올라이트 결정을 알루미나 튜브에 성장시키기 위해 3-chloropropyltrimethoxysilane를 코팅 후 TS-1 nano seed를 안착시키고 마이크로웨이브 합성법을 이용한 2차 성장을 통해 3~4 ${\mu}m$의 두께를 가지는 얇은 TS-1 제올라이트 분리막을 제조하였다. 제조한 분리막을 이용하여 에틸벤젠/메타자일렌/파라자일렌이 혼합된 혼합 자일렌으로부터 에틸벤젠을 분리하였다. 마이크로웨이브 합성 온도가 증가할수록 제올라이트 결정의 크기가 비례하여 증가하였다. 또한 반응기의 온도가 $200^{\circ}C$에서 가장 높은 투과 플럭스와 선택도를 가졌다. 가장 좋은 에틸벤젠 분리 성능을 보인 분리막은 마이크로웨이브 합성 온도가 $170^{\circ}C$인 분리막이고 선택도 값은 2.64였다(에틸벤젠 투과 플럭스 : 1703.0 mol/$m^2{\cdot}s{\cdot}Pa$).

• Korean Chemical Engineering Research
• /
• 제48권5호
• /
• pp.660-667
• /
• 2010

본 연구에서는 고분자 막을 이용하여 6대 온실가스 중 가장 높은 지구온난화지수를 갖는 육불화황(sulfur hexafluoride, $SF_6$)의 회수에 관한 연구를 실시하였다. 막 소재로 이미드 계열의 Matrimid 5218 소재를 건/습식 상전이 법을 이용하여 중공사 형태로 제조하고, 표면 실리콘 코팅 후 모듈을 제조하였다. 제조된 중공사 막은 전자주사현미경 관찰을 통하여 외부 표면에 치밀한 선택층과 망상구조의 하부로 이루어진 비대칭 구조를 확인하였다. 막의 기체투과 특성 확인을 위하여 온도와 압력 변화에 따른 $N_2$, $SF_6$ 단일 기체투과를 실시하였으며, 운전 조건에 따라서 0.78~1.36 GPU의 $N_2$ 투과도와 2.44-5.08의 $N_2/SF_6$ 선택도를 나타냈었다. 제조된 모듈의 혼합기체 분리거동 관찰을 위하여 10 vol.% $SF_6$ 농도를 갖는 $N_2/SF_6$ 혼합기체를 이용하여 온도, 압력, retentate 유량을 달리하여 실시하였으며, 실험을 통하여 압력과 온도 증가 및 retentate 유량 감소에 따라서 회수된 가스 중에 $SF_6$의 농도는 증가되어 최고 37.5 vol.%를 나타낸 반면 회수율은 감소되는 경향을 나타내었으며, 동일한 온도와 압력에서 retentate 유량 증가에 따라서 $SF_6$ 농도는 감소되는 반면 회수율이 증가하여 최고 89%의 회수율을 나타내었다.

• 디자인학연구
• /
• 제13권4호
• /
• pp.233-242
• /
• 2000

1990년대는 유압굴삭기의 전통적 조형이 새롭게 모색 및 재해석되는 시기로 판단되었으며, 이는 2가지 방향으로 정리될 수 있다. 하나는 유압굴삭기의 전통적 이미지에 관한 부정적 해석에서 기인한 '탈(post-heavy equipment)중기적' 경향이며, 다른 하나는 고유성 유지와 개선이라는 긍정적 해석에서 기인한 '후기(late-)중기적' 경향이다. 이는 동일한 현상을 다양하게 바라볼 수 있는 패러다임과 관련하는 것으로 사료된다. 이 시기에 개발 및 시판된 8개 연구대상 모델 중 유압굴삭기의 조형 경향은, 일본 색채디자인연구소에서 개발한 이미지스케일 3상한에서 2상한으로 변화였으며, 예외적으로 코벨코는 1상한까지 이동하는 경향이 있었다. 이는 탈중기적 이미지를 디자인 전략으로 채택하고 있는 코벨코만의 경우였다. 아울러, 인적(入的)공간으로서의 캐빈의 변화는 장비 전체의 변화에서보다 좀더 1상한으로 이동하고 있는데, 이는 물적(物的)공간과 시각적 차별화를 위한 것으로 사료되었다.