• Bulletin of the Korean Chemical Society
• /
• v.25 no.5
• /
• pp.687-693
• /
• 2004

Composite membranes with a titania layer were prepared by soaking-rolling method with the titania sol of nanoparticles formed in the sol-gel process and investigated regarding the vapor permeation of various organic mixtures. The support modification was conducted by pressing $SiO_2$ xerogel of 500 nm in particle size under 10 MPa on the surface of a porous stainless steel (SUS) substrate and designed the multi-layered structure by coating the intermediate layer of ${\gamma}-Al_2O_3$. Microstructure of titania membrane was affected by heat-treatment and synthesis conditions of precursor sol, and titania formed at calcination temperature of 300$^{\circ}C$ with sol of [$H^+$]/[TIP]=0.3 possessed surface area of 210 $m^2$/g, average pore size of 1.25 nm. The titania composite membrane showed high $H_2/N_2$ selectivity and water/ethanol selectivity as 25-30 and 50-100, respectively. As a result of vapor permeation for water-alcohol and alcohol-alcohol mixture, titania composite membrane showed water-permselective and molecular-sieve permeation behavior. However, water/methanol selectivity of the membrane was very low because of chemical affinity of permeants for the membrane by similar physicochemical properties of water and methanol.

• Membrane Journal
• /
• v.21 no.3
• /
• pp.229-235
• /
• 2011

In this study, mesoporous titania/alumina membranes were prepared by sol-gel method. Pore structure and phase composition of titania/alumina membranes could be changed by calcination temperature. The addition of alumina into titania membranes retarded anatase-to-rutile phase transformation, resulting in stabilization of pore structures. The 5 time dip-coated membrane calcined at $450^{\circ}C$ is about $10.3{\mu}m$ in thickness with an average pore size of 5 nm. Hydrogen and nitrogen permeances through the membrane were $17.1{\times}10^{-7}mol/m^2{\cdot}s{\cdot}Pa$ and $4.7{\times}10^{-7}mol/m^2{\cdot}s{\cdot}Pa$, respectively. These data were explained by the Knudsen diffusion mechanism.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2004.05a
• /
• pp.39-42
• /
• 2004

Ceramic membranes have attracted a great attention because they have excellent resistance to most organic solvents and can be used over a wide temperature range. Especially, titania (titanium oxide, TiO$_2$) shows excellent chemical resistance and can be used both acidic and alkali solutions, and therefore, titania is one of the most promising materials for the preparation of porous membranes; titania membranes having pore sizes in the range of nanofiltration (NF) to ultrafiltration (UF) membrane have been prepared by the sol-gel process (Tsuru 2001).(omitted)

• Membrane and Water Treatment
• /
• v.6 no.3
• /
• pp.251-262
• /
• 2015

In this work the preparation and characterization of a membrane containing a uniform mesoporous Titanium oxide top layer on a porous stainless steel substrate has been studied. The 316 L stainless steel substrate was prepared by powder metallurgy technique and modified by soaking-rolling and fast drying method. The mesoporous titania membrane was fabricated via the sol-gel method. Morphological studies were performed on both supported and unsupported membranes using scanning electron microscope (SEM) and field emission scanning microscope (FESEM). The membranes were also characterized using X-ray diffraction (XRD) and $N_2$-adsorption / desorption measurement (BET analyses). It was revealed that a defect-free anatase membrane with a thickness of $1.6{\mu}m$ and 4.3 nm average pore size can be produced. In order to evaluate the performance of the supported membrane, single-gas permeation experiments were carried out at room temperature with nitrogen gas. The permeability coefficient of the fabricated membrane was $4{\times}10^{-8}\;lit\;s^{-1}\;Pa^{-1}\;cm^{-1}$.

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.52-56
• /
• 1997

The Pt doped $TiO_2$ composite membranes were prepared by the sol-gel process. The Pt doped titania sol was peptized with hydrochloric acid in the pH range of 1.23 to 1.32 at 5$0^{\circ}C$. The average particle size of the Pt doped titania sol was shown to be below 15nm and well dispersed in the solution. XPS show the Pt elements continuous and homogeneous dispersed in the $TiO_2$ membrane. The mean particle size of the Pt doped $TiO_2$ composite membrane has smaller than that of the undoped $TiO_2$ composite membrane. The average pore size of the Pt doped $TiO_2$ composite membrane was increased from 58 to 193 $\AA$ with firing temperature changed from 550 to 85$0^{\circ}C$. It was observed that the Pt doped $TiO_2$ composite membranes showed crack-free and homogeneous microstructue as well as narrow particle size distribution up to above 75$0^{\circ}C$.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2004.11a
• /
• pp.50-53
• /
• 2004

• Journal of Hydrogen and New Energy
• /
• v.18 no.1
• /
• pp.40-45
• /
• 2007

Methylene blue(MB) was photocatalytically degraded with one-body photoanode and solar simulator to investigate the possible application to both environmental purification and photoelectrochemical cell for hydrogen production. Photoactive titanium dioxide was formed on both sides of Ti plate following steps such as rinsing-annealing-calcination or anodizing(20 V, 30 V)-annealing($350^{\circ}C$, $450^{\circ}C)$ after etching. The prepared titania plate($2cm{\times}2\;cm$, ca 1.6 mg $TiO_2$ on the basis of $1\;{\mu}m$ thickness) was used to degrade MB(10 ppm in 200 mL solution). The reaction tended to follow the Langmuir-Hinshelwood kinetics with zero order. Comparative experiments with Degussa P25 showed the same zero order kinetics when 2 mg of P25 had been used, while the first order kinetics when 200 mg used. This concludes the feasibility of the prepared titania plate as a material for the purification of low-level harmful organics and an electrode or a membrane for photoelectrochemical system for hydrogen production.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2003.07a
• /
• pp.95-97
• /
• 2003

The main purpose of this work is to investigate the performance of membranes for treatment of dyeing wastewater. The microfiltration (MF) membranes (titania-blended polysulfone & alumina) were prepared. The nanofiltration (NF) and reverse osmosis (RO) membranes were kindly supplied by the Sae-Han. In order to reuse the wastewater for dyeing, the effluents were treated by the high flux RO and the fouling resistant RO (FRM) membranes. Also, the NF membrane was used for water reuse in rinsing.

• Membrane Journal
• /
• v.19 no.1
• /
• pp.47-53
• /
• 2009

The aim of this paper is to prepare metal/ceramic composite ultrafiltration membranes by coating inorganic particles on a metallic hollow fiber filter. The diameter and the pore size of the filter was 2.0 mm and $2{\sim}8{\mu}m$. The metal/ceramic composite ultrafiltration membranes were obtained by a coating process of silica and titania sols on top of the metallic filter. For this purpose the method of fast freeze drying and dip-coating were used. It was found that the pore size of the membrane was about 50 nm from SEM and PMI characterization. The pore size was controlled by changing the size of the particles, sintering period and temperature.

• Korean Journal of Materials Research
• /
• v.4 no.3
• /
• pp.319-328
• /
• 1994

Aluminium and titanium precursors containing $\beta$-diketonate ligands were used for the synthesis of polymeric sols of alumina and titania by sol-gel methods. To prepare polymeric sols by solgel processing, we synthesized modified precursors having chelating organic ligands. With these precursors it was found to be possible to control both hydrolysis and polycondensation reaction rates which resulted in ultrafine particles few nms of average size. The optimum molar ratio of acid to alkoxide for alumina sol was 0.3-0.4 and that of water to alkoxide &as 1. On the other hand, the corresponding ratios for titania sol were found be 0.25-0.20 and 1 respectively. Dynamic light scattering measurements indicated that the average particle size in both sols was in the order of few nms. SEM photographs were taken to observe crack-free and smooth surfaces of coated membranes after sintering at $450^{\circ}C$. Alumina coated membrane on a slide glass had about 4-4.5$\mu \textrm{m}$, thickness and titania coated one had 2-2.5$\mu \textrm{m}$, thickness. And according to TEM photographs, the grain size of titania was smaller than 30nm and that of alumina was in the range of few $\AA$s to 2nms. An X-ray diffraction study revealed that alumina was $\gamma$ phase and titania was anatase crystal.