• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.201-208
• /
• 2013

In this study, effect of different amounts of sulfur and vulcanization accelerators in the acrylonitrile styrene-butadiene rubber (AN-SBR)/silica compounds on the properties of tire tread compound were studied. As a result, cure rate and degree of cross-linking of the compounds were increased due to enhanced cross-linking reactivity by the increased amounts of sulfur and vulcanization accelerators. Also, abrasion resistance and the mechanical properties such as hardness and modulus of the compounds were improved by enhanced degree of cross-linking of the compounds. For the dynamic properties, tan ${\delta}$ value at $0^{\circ}C$ was increased due to the increase of glass transition temperature ($T_g$) by enhanced degree of cross-linking of the compound, and tan ${\delta}$ value at $60^{\circ}C$ was decreased. Initial cure time ($t_1$) showed the linear relationship with tan ${\delta}$ value at $60^{\circ}C$. This result is attributed that reduced initial cure time ($t_1$) of compounds by applying increased amount of curatives can form cross-linking in early stage of vulcanization that may suppress development of filler network. This result is verified by observation on the surface of annealed compounds using AFM (atomic force microscopy). Consequently, decreased initial cure time is considered a very important parameter to reduce tan ${\delta}$ at $60^{\circ}C$ through reduced re-agglomeration of silica particles.

• Elastomers and Composites
• /
• v.54 no.4
• /
• pp.330-334
• /
• 2019

Cryogenic crushing techniques have been employed for recycling waste rubber articles and for extracting residual organic additives present in rubber samples. Rubber particulate derived from tire tread abrasion is one of the key components of road dust. Therefore, in this work, we prepared rubber particulates using a cryogenic crusher and characterized their shapes as well as size distributions according to the type of rubber. The rubber particulates exhibited uneven surfaces with the presence of some small pieces. The order of the particle size distribution was observed to be: NR > BR > SBR. Subsequently, carbon black was added; this led to a decrease in the particle size and the shape becoming rougher. The crushed particulates of the carbon black-filled samples comprised agglomerated shapes of small pieces, which were similar in shape to that of wear debris in tire tread. It was discovered that crosslink density was one of the principal factors that led to the formation of small crushed particulates. The small particulates obtained by cryogenic crushing can be utilized as model rubber particulates for researching micro dust.

• Elastomers and Composites
• /
• v.58 no.2
• /
• pp.87-94
• /
• 2023

Abrasion tests of an SBR compound were conducted using four different types of abrasion testers (cut and chip, Lambourn, DIN, and LAT100). The abrasion test results were analyzed in terms of size distributions and morphologies of the wear particles. Most wear particles were larger than 1000 ㎛. The wear particle size distributions tended to decrease as the particle size decreased. Except for the Lambourn abrasion test, the wear particles smaller than 212 ㎛ were rarely generated by the other three abrasion tests, implying that small wear particles were produced through friction by introducing talc powder. Shapes of the wear particles varied depending on the abrasion testers. The wear particles generated from the Lambourn abrasion tester had stick-like shapes. The cut and chip abrasion test showed a clear abrasion pattern, but the DIN abrasion test did not show any specific abrasion pattern. The Lambourn and LAT100 abrasion tests showed irregular abrasion patterns.

• Journal of Veterinary Clinics
• /
• v.22 no.2
• /
• pp.100-107
• /
• 2005

This study was carried out to investigate the physical and chemical properties of teat cup liners. The hardness of the liners was $50\~67$, and their fatigue to failure 38-1,185 cycles. The elongation and tensile strength of these liners were about $134 kgf/cm^2\;and\;473\%$, respectively. The infrared spectrum and the gas chromatogram revealed that the liner A was consisted of NR, SBR, and BR, with a composition ratio of 60:20:20 (part per hundred rubber). The raw rubber materials used for liners B to G, on the other hand, were NBR only. However, the liner H was made of silicon rubber. The thermogravimetric analysis showed that the liners tested in this study contained raw rubber material, carbon black, organic compounds and metallic compounds.