• Journal of Sensor Science and Technology
• /
• v.16 no.6
• /
• pp.428-433
• /
• 2007

$SnO_{2}$-based thick film ethanol gas sensors were fabricated on alumina substrates and their ethanol gas sensing characteristics were investigated. The film sintered at $400^{\circ}C$ for 2 hrs. showed the highest sensitivity to ethanol gas and the sensitivity of the film to 1000 ppm ethanol gas in air was 97 % at an operating temperature of $250^{\circ}C$. The addition of $Fe_{2}O_{3}$ to $SnO_{2}$ enhanced the sensitivity by changing the type and number of surface acidic/basic sites.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.05a
• /
• pp.82-83
• /
• 1994

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.125-130
• /
• 1999

After $SnO_2$ fine powder by precipitation method, Ca as crystallization inhibitor and Pd as catalyst were added to $SnO_2$ raw material by various methods. Thick film device was fabricated on the alumina substrate by mixing ethylene glycol and such mixed powders. The sensing characteristics of the device for methane gas were investigated. The most excellent gas sensing property was shown by the thick film device fabricated by Method 3 in which Ca and Pd doped $SnO_2$ powder is prepared by mixing $SnO_2$ powder, 0.1 wt% Ca acetate and 1 wt% $PdCl_2$ in deionized water and by calcining the mixture, after $Sn(OH)_4$ is dried at $110^{\circ}C$ for 36h. The sensitivity of the sensor fabricated with $SnO_2$-0.1 wt%Ca acetate-1wt%$PdCl_2$ powder heat-treated at $700^{\circ}C$ for 1h was about 86% for 5,000 ppm methane in air at $350^{\circ}C$ of the operating temperature. Response time and recovery were also excellent.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.2 s.43
• /
• pp.59-63
• /
• 2007

This paper presented a low-cost thick film gas sensor module, which was based on simple PCB (Printed Circuit Board) process. The proposed sensor module included a $NO_2/H_2$ gas sensor, a relative humidity sensor, and a heating element. The $NO_2/H_2$ gas and relative humidity sensors were realized by screen-printing $SnO_2,\;BaTiO_3$ nano-powders on IDTS (Interdigital Transducer) of a PCB substrate, respectively. At first 1% $H_2$ gas flowed into the sensor chamber. After 4 min, air filled the chamber while $H_2$ gas flow stopped. This experiment was performed repeatedly. The Identical procedure was used for the $NO_2$ detection. The result for sensing $H_2$ gas showed the increase of voltage from 0.8V to 3.5V due to the conductance increase and its reaction response time by hydrogen flow was 65 sec. $NO_2$ sensing results showed 2.7 V voltage drop due to the conductance decrease and its response time was 3 sec through a voltage monitoring.