$SnO_{2}$-based thick film ethanol gas sensors were fabricated on alumina substrates and their ethanol gas sensing characteristics were investigated. The film sintered at $400^{\circ}C$ for 2 hrs. showed the highest sensitivity to ethanol gas and the sensitivity of the film to 1000 ppm ethanol gas in air was 97 % at an operating temperature of $250^{\circ}C$. The addition of $Fe_{2}O_{3}$ to $SnO_{2}$ enhanced the sensitivity by changing the type and number of surface acidic/basic sites.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1994년도 춘계 학술발표 강연 및 논문 개요집
• /
• pp.82-83
• /
• 1994

• The Korean Journal of Ceramics
• /
• 제5권2호
• /
• pp.125-130
• /
• 1999

After $SnO_2$ fine powder by precipitation method, Ca as crystallization inhibitor and Pd as catalyst were added to $SnO_2$ raw material by various methods. Thick film device was fabricated on the alumina substrate by mixing ethylene glycol and such mixed powders. The sensing characteristics of the device for methane gas were investigated. The most excellent gas sensing property was shown by the thick film device fabricated by Method 3 in which Ca and Pd doped $SnO_2$ powder is prepared by mixing $SnO_2$ powder, 0.1 wt% Ca acetate and 1 wt% $PdCl_2$ in deionized water and by calcining the mixture, after $Sn(OH)_4$ is dried at $110^{\circ}C$ for 36h. The sensitivity of the sensor fabricated with $SnO_2$-0.1 wt%Ca acetate-1wt%$PdCl_2$ powder heat-treated at $700^{\circ}C$ for 1h was about 86% for 5,000 ppm methane in air at $350^{\circ}C$ of the operating temperature. Response time and recovery were also excellent.

• 마이크로전자및패키징학회지
• /
• 제14권2호
• /
• pp.59-63
• /
• 2007

간단한 PCB 공정을 기반으로 하여 저가형의 후막 가스 센서 모듈을 제안하고자 한다. 제안된 센서 모듈은 $NO_2/H_2$ 가스 센서와 습도센서, 그리고 히터를 포함한다. $NO_2/H_2$ 가스와 상대 습도 센서들은 각각 $SnO_2$와 $BaTiO_3$ 나노 입자들을 PCB 기판에서의 IDT(interdigital Transducer)에 프린팅 함으로써 제작되었다. 처음에 1% $H_2$ 가스를 센서 쳄버에 공급하고 4분 후 $H_2$가스 공급을 멈추고 공기를 주입시켰으며, 이러한 동작을 반복적으로 수행하였다. 마찬가지로 $NO_2$로 감지하도록 같은 동작을 실행하였다. $H_2$ 가스에 대한 결과는 도전성의 증가로 인하여 0.8V에서 3.5V로 증가함을 볼 수 있었으며, $H_2$ 가스를 주입한후의 반응 시간은 65초였다. $NO_2$ 가스의 경우는 도전성이 감소함으로써 2.7 V의 전압강하가 일어 났으며, 반응시간은 3초였다.