본 실험에서는 리튬 이차 박막전지의 음극물질로 주석 산화물 박막을 RF magnetron sputter을 이용하여 증착하였다. RF power와 공정 압력을 각각 $2.5W/cm^2$와 10mTorr로 고정시키고 박막 중의 산소량을 조절하기 위해 산소 분압을 $0\~100\%$까지 조절하여 실험하였으며, 산소량을 더 줄이기 위해 주석 금속 칩을 사용하여 조절하였다. 산소량을 줄여 줌으로써 비가역적으로 형성되는 리튬산화물의 량을 줄이고 고용량의 $SnO_x$음극 박막을 제조하였다. 그 중 $SnO_{1.43}$일 때 가장 큰 가역용량(약$ 500{\mu}Ah/cm^2{\mu}m$) 얻었다.

• 환경위생공학
• /
• 제15권2호
• /
• pp.18-26
• /
• 2000

In order to improve the quality of Kamju(sikhae), Korean traditional sweat fermentated rice drink, Kamju made with laboratory fermenting from both covered barley malt and that added to commercial $\alpha-amylase$ and commercial sikhae can were investigated and analyzed ad follows 1. The amylase activities in L-malt(laboraory made malt), C-malt(commercial malt) were 25,065 units, 20,498 units at $60^{\circ}C$ and when heating at $60^{\circ}C$ for one hour their heat stability was getting lower and while at $70^{\circ}C$ after 2 hours both their heat stability was under 21%. 2. The external appearance, of all samples, in beating test, flipper, springer and leaker test were excellent and good valued. On the open test of sample can, head space was 7.9~9.0mm, net weight 247~250g, 432~435g, pH 4.96-5.76, Brix 13.2~14.0 and vacuum degree was 29~35cmHg. 3. The sucrose content of sample 1~5 was 8,57~10.01% highest ammount than sample 6(0.91%) 7(0.43%) and maltose content of sample 1~5 was 0.65~1.41% lower than 6 was 7.91% and 7 was 8,36%. The good traditional flavor texture and saccharides components content of glucose of sample 1~5 was 1.09~1.51, 6(3.86%), 7(3.97%), fructose content of sample 1~5 was 0.45~0.95%, 6(2.76%), 7(2.81%), maltotriose and raffinose of sample 1~5 were 0.04~0.291, 6(0.61%), 7(2.81%), and solid content of sample 1~5(3.1~3.8) was lower than 6(10.25%), 7(10.09%). 4. The result of sensory test as measured as lemone yellow of sample 6 and milky of sample 7, and weetness, flavor, color, traditional texture and sensory value for sample 1~5(3.1~3.8) was lower degree than that for 6(4.5), 7(4.0). 5. Among the heavy metals analyzed from sample cans, tin, iron and lead content for sample 1~5 were 31.95~36.71ppm, 5.84~6.39ppm and 0.075~0.09ppm while their content of sample 6.7, tin, 32.91ppm, 32.87ppm, iron 5.51ppm, 5.41ppm and lead, 0.074ppm, 0.079ppm.

• 한국표면공학회지
• /
• 제24권2호
• /
• pp.88-95
• /
• 1991

The tin-lead alloy was electrodeposited in the low range of peak current density in order to investigate the change of composition and microstructure of them. The Pb content of alloy deposits, which was decreased with increasing average current density, was relatively lower than that of D.C. plated alloy deposit. The preferred orientation of alloy deposit was changed with increasing peak current density and the surface morphology of alloy deposits was closely related to the preferred orientation of them.

• 대한화학회지
• /
• 제28권5호
• /
• pp.293-301
• /
• 1984

단일 희석법을 이용한 X-선형광분광법으로 주석, 슬랙중 $Ta_2O_5$와 $Nb_2O_5$, $ZrO_2$등을 정량분석하였다. 이 방법은 표준 검정 곡선을 직선으로 되게끔 수학적으로 보정하는 것이다. 시료의 조성과 비슷한 한개의 합성표준시료와 분석시료를 무수물의 $Li_2B_4O_7$으로 묽혀서 각각 시료가 1%, 2%, 3%되게 한다. 묽힌 시료들을 $1150^{\circ}C$에서 30분간 용융하여 유리화된 구슬을 만든 다음, 곱게 갈아서, 다시 유압기로 압축하여 분석시편을 만든다. 이 시편을 사용하여 X-선 세기를 측정하고, 원소의 특성 X-선 세기에 관한 J. Scherman의 식으로부터 유도한 식에 대입하여 분석 결과를 계산했다. 이들 분석결과들을 표준검정곡선법으로 얻은 기준값과 잘 일치하며, 결과에 대한 재현성도 좋음을 보여 주었다.

• 대한화학회지
• /
• 제28권5호
• /
• pp.302-308
• /
• 1984

이중희석법을 이용한 X-선 분광법으로 주석-슬랙 중 $Ta_2O_54, $Nb_2O_5$ 및 $ZrO_2$등을 정량하였다. 주석시료와 이것과 조성이 비슷한 한개의 합성표준시료를 무수 $Li_2B_4O_7$으로 희석하여 희석된 시료중 이들의 함량이 1.00%, 2.00%, 3.00% 되게 잘 혼합하였다. 혼합시료를 $1,150^{\circ}C$에서 30분간 용융하여 유리상태로 만들었다. 다시 잘 분쇄하고, 유압기를 이용하여 Pellet로 만들어 분석 시편으로 사용했다. 형광 X-선 세기를 측정하여 희석식에 대입하여 각 시료에서 분석성분의 함량을 계산하였다. 이중희석법으로 얻은 분석결과들은 대표적인 분석법인 표준검정 곡선법에 의한 값들과 혀용오차범위내에서 잘 일치하고 있다. 아울러 단일희석법에 의한 결과와도 잘 일치하고 있으며 각 분석결과에 대한 재현성도 좋음을 보여 주었다.

• Nuclear Engineering and Technology
• /
• 제54권6호
• /
• pp.2230-2243
• /
• 2022

The tin tailing processing industry in Malaysia has operated with minimal regard and awareness for material management and working environment safety, impacting the environment and workers in aspects of radiation and heavy metal exposure. RIA was conducted where environmental samples were analyzed, revealing concentrations of ²²⁶Ra, ²³²Th and ⁴⁰K between the range of 0.1-10.0, 0.0-25.7, and 0.1-5.8 Bq/g respectively, resulting in the AED exceeding UNCEAR recommended value and regulation limit enforced by AELB (1 mSv/y). Ra_eq calculated indicates that samples collected pose a significant threat to human health from gamma-ray exposure. Assessment of heavy metal content via pollution indices of soil and sediment showed significant contamination and enrichment from processing activities conducted. As and Fe were two of the highest metals exposed both via soil ingestion with an average of 4.6 × 10^-3 mg/kg-day and 1.4 × 10^-4 mg/kg-day, and dermal contact with an average of 5.6 × 10^-4 mg/kg-day and 6.0 × 10^-4. mg/kg-day respectively. Exposure via accidental ingestion of soil and sediment could potentially cause adverse non-carcinogenic and carcinogenic health effect towards workers in the industry. Correlation analysis indicates the presence of a relationship between the concentration of NORM and trace elements.

• Transactions on Electrical and Electronic Materials
• /
• 제18권1호
• /
• pp.21-24
• /
• 2017

Usually, the oxygen vacancy is an important factor in an oxide semiconductor device because the conductivity is related to the oxygen vacancy, which is formed at the interface between oxide semiconductors and electrodes with an annealing processes. ZTO is made by mixing n-type ZnO and p-type $SnO_2$. Zink tin oxide (ZTO), zink oxide (ZnO) and tin oxide ($SnO_2$) thin films deposited by RF magnetron sputtering and annealed, to generate the oxygen vacancy, were analyzed by XPS spectra. The contents of oxygen vacancy were the highest in ZTO annealed at $150^{\circ}C$, ZnO annealed at $200^{\circ}C$ and $SnO_2$ annealed at $100^{\circ}C$. The current was also increased with increasing the oxygen vacancy ions. The highest content of ZTO oxygen vacancies was obtained when annealed at 150. This is the middle level in compared with those of ZnO annealed at $200^{\circ}C$ and $SnO_2$ annealed at $100^{\circ}C$. The electrical properties of ZTO followed those of $SnO_2$, which acts a an enhancer in the oxide semiconductor.

• Journal of Biosystems Engineering
• /
• 제29권1호
• /
• pp.65-70
• /
• 2004

This study was carried out to verify and predict the soil informations such as the contents of organic matter(OM) and Mg and pH of the soil. The predictability of spacial variation in the paddy field was examined by analyzing the various soil information. The prediction models for the OM pH, and Mg, were developed using inverse distance weighted (IDW), triangulated irregular network(TIN) and Kriging model. The determination of coefficients of linear and spherical Kriging models were 0.756 and 0.578, respectively, and were very low in comparison with other soil information. For IDW and TIN model, the determination of coefficients were 1.000 and hence the performance of the models was found to be excellent. The developed models were validated using unknown soil sample obtained In 2000 and 2001. From the analysis of relationship between the measured pH and predicted 0.9353. For prediction of Mg, the determination of coefficient is more than 0.8. Since the determination of coefficients of developed models for OM were relatively low, it may be difficult to predict the content of OM using the developed models. For further study, the additional works to enhance the performance of the prediction models for soil information are required.

• 한국재료학회지
• /
• 제5권8호
• /
• pp.1045-1049
• /
• 1995

유기금속분해법(MOD, Metal Organic Decomposition)에 의하여 ITO 박막을 제조하고 SnO$_2$의 조성과 소성온도의 변화에 따른 박막의 특성변화를 고찰하였다. SnO$_2$의 양이 변하여도 ITO는 In$_2$O$_3$의 결정구조를 유지하고 있었으며, 이로부터 Sn이 In자리를 치환하여 고용체를 형성함을 알 수 있었다. SnO$_2$를 9wt.% 첨가 하였을때 비저항이 2.5$\times$$10^{-3}$$\Omega$-cm로 가장 낮은 값을 보였으며, 이는 타 연구자들의 결과치 보다 약 10배정도 큰 값이다. 이러한 비저항값의 차이는 작은 입경으로 인한 이동도의 감소 때문인 것으로 판단되었다. 투광도는 SnO$_2$의 첨가량 및 소성온도에 크게 의존하지 않았으며 가시영역에서 90% 이상을 보였다. 광흡수단으로부터 계산된 optical energy gap은 4.51-4.96eV 이었다.

• 한국식품과학회지
• /
• 제27권5호
• /
• pp.742-747
• /
• 1995

현재 국내에서 유통되고 있는 캔 및 병 오렌지쥬스를 20, 30, 40, $50^{\circ}C$에서 24주 동안 저장하면서 4주 간격으로 개봉하여 중금속(Sn, Fe, Pb) 함량, 비타민 C 함량, 갈색도와 pH의 변화를 조사하였다. 병쥬스에서는 Sn, Fe, Pb 모두 저장 중 그 함량 변화가 거의 일어나지 않았으나 캔쥬스는 중금속 용출에 대한 온도의 영향이 두드러지게 나타났다. 즉, Sn농도는 16주 후 저장 전의 $2.7{\sim}13.1$배로 증가하였고, Fe농도는 24주 후 $4.3{\sim}5.2$배로 증가하였으며 Pb농도는 24주 후 $1.1{\sim}2.9$배로 증가하였다. 캔쥬스의 총 비타민 C 잔존율은 24주 후 $20^{\circ}C$에서는 큰 변화가 없었으나 $30{\sim}50^{\circ}C$에서는 $13{\sim}76%$로 감소하였고, 병쥬스의 경우는 $4{\sim}80%$로 감소하였다. 캔쥬스의 갈색도는 24주 후 $40^{\circ}C$ 이하에서는 조금 증가하였으나 $50^{\circ}C$에서는 완전히 변색되었으며 병쥬스의 경우는 모든 온도에서 캔쥬스보다 좀 더 변색되었다. 오렌지쥬스의 pH는 $40^{\circ}C$ 이하에서 포장용기에 상관없이 저장 중 거의 변화가 없었으나 $50^{\circ}C$에서는 24주 후 캔용기의 팽창과 함께 pH의 급격한 증가를 나타냈다. 국내에서 유통되고 있는 캔쥬스의 품질유지를 위한 유통기한을 재검토해야 될 것이다.