• Journal of Adhesion and Interface
• /
• v.7 no.3
• /
• pp.16-25
• /
• 2006

Water vapour permeable and water resistant film was laminated to made footwear woven fabric and non-woven fabrics by screen type with thermosetting reactive hot melt adhesive. Optimum conditions of each process were investigated, and the properties of film laminated fabric with optimum conditions are evaluated. The results are as follows. Thermosetting reactive polyurethane hot melt is retain proper heat resistance differently thermoplastic hot melt. Optimum melting adhesive process conditions are as follows ; drum temperature $95^{\circ}C$, hose temperature $97^{\circ}C$, feeding pipe temperature $100^{\circ}C$, screen temperature $105^{\circ}C$, pressure of opposite roller $1kgf/cm^2$, pressure of laminating roller $3kgf/cm^2$, finishing speed 15 m/min, melting temperature $120^{\circ}C$, cooling time 20 s, pressing temperature $130^{\circ}C$, pressing time 30 s. As the thickness of film was increased, the water vapour permeability was decreased but water resistance was increased, and the effect of film is dominant over all the others in the air permeability.

• Journal of Adhesion and Interface
• /
• v.7 no.3
• /
• pp.26-33
• /
• 2006

Nylon fabrics were corona treated with different current intensity (5, 10, 15, 20 A) and feeding speed (5, 10, 15 m/min). We confirmed the change of nylon fabrics surface using X-ray diffraction apparatus, scanning electron microscopy (SEM) and X-ray photoelectron spectrometer (ESCALAB). And the change of physical properties through measuring the tensile strength, tear strength, bonding and wet bonding strength. Thermosetting reactive polyurethane hot melt adhesive was used in the adhesion of nylon fabrics. Functional groups were introduced on nylon fabric surface by treating the fabrics in air atmosphere with corona discharge, and the result adhesion was improved. Bonding strength of the nylon fabric treated with corona was increased with increasing current intensity and decreasing feeding speed.

• Journal of Adhesion and Interface
• /
• v.8 no.3
• /
• pp.16-23
• /
• 2007

Polyester fabrics and knits were corona treated with different current intensity (5, 10, 15, 20 A) and feeding speed (5, 10, 15 m/min). We confirmed the surface change of polyester fabrics and knits using scanning electron microscopy (SEM) and X-ray photoelectron spectrometer (XPS). And the change of physical properties through measuring the tensile strength, dry and wet bonding strength. Thermosetting reactive polyurethane hot melt adhesive was used in the adhesion of polyester fabrics and knits. Functional groups were introduced on PET fabrics and knits surface by treating the PET fabrics and knits in air atmosphere with corona discharge, and take placed unevenness, the result adhesion was improved. When consider both dry and wet bonding strength, we think that appropriate conditions in the PET fabrics corona treatment are feeding speed 10 m/min, current intensity 15 A and appropriate conditions in the mesh type PET knits corona treatment are feeding speed 10 m/min, current intensity above 10 A.