• JSTS:Journal of Semiconductor Technology and Science
• /
• v.17 no.2
• /
• pp.245-251
• /
• 2017

Niobium doped zirconium oxide (Nb-Zr-O:NZO) thin films were fabricated on Si substrates by a sol-gel technique with an annealing temperatures of $500{\sim}1000^{\circ}C$ in air ($N_2:O_2=3:1$) for 20 minutes. It was found that the NZO film is based on tetragonal $ZrO_2$ polycrystalline structure with the Nb 5+ ion state and there is almost no diffusion of Nb or Zr to Si substrate. The relative dielectric constant for the NZO film with the Nb composition of 30 mol% and annealed at $800^{\circ}C$ was around 40. The root mean roughness was 1.02 nm. In addition, the leakage current of NZO films was as low as $10^{-6}A/cm^2$ at 4.4 V.

• Journal of the Semiconductor & Display Technology
• /
• v.6 no.4
• /
• pp.65-68
• /
• 2007

An epitaxial NiSi structure on Si (001) substrate was studied by using density functional theory (DFT). Orhorhombic and B2-NiSi structures were compared first. B2 structure was further considered as it has same crystal structure as Si and the lattice mismatch between B2 and Si is small, compared to orthorhombic-NiSi. The lattice parameters of x- and y-direction in B2-NiSi structure were modified to match with those in Si (001). The size reduction of the lattice parameter of B2-NiSi to match with that of Si increased the lattice parameter of z-direction by 10.5%. Therefore, we propose that an optimum structure of NiSi for epitaxial growth on Si (001) is a tetragonal structure.

• Journal of the Korean Ceramic Society
• /
• v.22 no.1
• /
• pp.40-46
• /
• 1985

The effect of calcining temperature ranged from $700^{\circ}C$ to 110$0^{\circ}C$ on sintering characteristics of morphotropic $Pb(Zr_{0.53}Ti_{0.47})O_3 doped with $Nb_2O_5$ has been investigated. The ratio of sintered grain size to calcined grain size decreased as the calcining temperature increased. The hardness as well as the sintered density of the samples reached a maximum at about 90$0^{\circ}C$. The X-ray diffraction pattern of the sintered sample showed both tetragonal and rhombohedral phases. The tetragonal phases intensity increased with the calcining temperature going through a maximum at about 90$0^{\circ}C$ while the rhombohedral phase intensity remained uneffected. The both intensity were about the same at 90$0^{\circ}C$ The dielectric constant of the sintered samples reached a maximum um while the dielectric dissipation factor showed a minimum at the calcining temperature of about 100$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1035-1039
• /
• 1999

Ferroelectric properties and reliability characteristics of(111) and (100) preferentially oriented tetragonal Pb(Zr0.2Ti0.8)O3 (PZT) thin film capacitors have been investigated as a function of the top electrode thickness. The (111) preferentially oriented film exhibits 180$^{\circ}$domain switching process with better squareness of hysterisis loop and abrupt change of small singal capacitance-voltage comparing to the (100) preferentially oriented film having 90$^{\circ}$ domain switching process. The domain swithcing process of tetragonal phase PZT is different from that of rhobohedral phase. The film with thinner top electrode shows less initial switching polarization due to less compressive stress but it exhibits better endurance characteristics due to enhancing partial switching region.

• Journal of the Korean Ceramic Society
• /
• v.25 no.4
• /
• pp.321-328
• /
• 1988

The sintering phenomena, electrical resistivity, dielectric and piezoelectric properties of lead titanate ceramics modified by the partial substitution of La for Pb and Mn for Ti, (Pb1-1.5xLax)(Ti1-yMny)O3 ceramics, have been investigated. In (Pb1-1.5xLax)(Ti1-yMny)O3 system, with increasing lanthanum content, the realtive bulk density increased, but the Curie point and tetragonality (c/a) decreased. The tetragonal-to-cubic phase transition boundary existed in the range of 0.20

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.341-346
• /
• 1992

The effects of CaO addition on the low temperature degradation behavior of 2.5Y-TZP ceramics were investigated. Y2O3-CaO-ZrO2 ceramics were prepared from the commercial Y-TZP powder added within 1 mol% of CaO. Fully tetragonal phase could be obtained at each composition under sintering condition of 1500$^{\circ}C$ for 1 hour. As the amount of CaO increased, grain size was decreased. From the result of heat treatment at 200$^{\circ}C$, volume fraction of monoclinic phase formed on the surface of each specimen was decreased with higher CaO amount. Stability of tetragonal ZrO2 phase for low temperature heat treatment was increased by CaO addition without the degradation of mechanical properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1991.10a
• /
• pp.20-23
• /
• 1991

In this study, 0.05Pb(Mn$\_$1/3/Nb$\_$2/3/)O$_3$+ 0.95Pb(Zr/Ti)O$_3$+x[wt%]Cr$_2$O$_3$piezoelectric ceramics were fabricated by Hot-press method, and its structural, dielectrical, piezoelectrical properties, temperature stability and aging characteristics were investigated. Among the MPB and tetragonal compositions, the specimens with 0.2, 0.3 and 0.4 [wt%] Cr$_2$O$_3$ additive amount had the poisson ratio more than 1/3. At tetragonal phase, the aging was small, and the temperature stability was improved by Cr addition. The specimen most suitable to the HF device substrate was the one with the composition of 47/53 (Zr/Ti) an 0.4 [wt%] Cr$_2$O$_3$addition.

• Journal of the Mineralogical Society of Korea
• /
• v.9 no.1
• /
• pp.35-42
• /
• 1996

Polycrystalline ZrH2 in tetragonal crystal system has been compressed in a modified Bassett-type diamond anvil cell up to 36.0 GPa at room temperature. X-ray diffraction data did not indicate any phase transitions at the present pressure range. The pressure dependence of the a-axis, c-axis, c/a and molar volume of ZrH2 was determined at pressures up to 36.0 GPa. Assuming the pressure derivative of the bulk modulus (K0') to be 4.11 from an ultrasonic value on Zr, bulk modulus (K0) was determined to be 160Gpa by fitting the pressure-volume data to the Birch-Murnaghan equation of state. Same sample was heated at $500^{\circ}C$ at the pressure of 9.8 GPa in a modified Sung-type diamond anvil cell. Unloaded and quenched sample revealed that the original tetragonal structure transforms into a hexagonal structured phase with a zero-pressure molar volume change of ~115.5%.

• Journal of the Korean Ceramic Society
• /
• v.45 no.2
• /
• pp.126-131
• /
• 2008

In this study, we prepared zirconia gel by the sol-gel method and investigated its photoluminescence properties by varying pyrolysis temperature. The addition of acetic acid into a Zr-alkoxide solution resulted in forming the bidentate ligands with Zr ions and producing a stable gel. At the pyrolysis temperature of $350^{\circ}C$, the zirconia nanocrystals with tetragonal structure gradually appeared in the gel. The PL intensity of the zirconia gel increased with increasing the pyrolysis temperature up to $350^{\circ}C$, but decreased above the temperature. Concurrently, its PL peak wavelength continuously shifted from ${\sim}440\;nm$ to ${\sim}550\;nm$ with the temperature. The PL characteristics of the zirconia gels were closely associated with decomposition of residual organic groups, the formation of the zirconia nanocrystals, and the tetragonal to monoclinic phase transformation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.527-530
• /
• 2002

A lot of efforts have been focused on the optimization of PIT parameters for Bi-2223/Ag wire. In this paper, initial annealing of Bi-2223/Ag wire to transform Bi-2212 orthorhombic from Bi-2212 tetragonal Precursor was investigated. This initial annealing step at low oxygen partial pressure were to transform Bi-2212 orthorhombic structure and to reduce the formation of second phases at superconducting wire. However Bi-2223 Phases were appeared at higher annealing temperature. Critical currents(Je) of Bi-2223/Ag tapes were sintered at low oxygen Partial pressure were higher than that of the wires sintered at atmosphere condition. In order to investigate the effect of rolling reduction ratio, Bi-2223/Ag HTS tapes were rolled with different reduction ratio. There were no clear difference of Je and filaments shape with various rolling reduction ratio.