• 한국응용과학기술학회지
• /
• 제37권1호
• /
• pp.49-55
• /
• 2020

In this study, isophorone diisocyanate (IPDI) and dimethylolbutanoic acid (DMBA) were used on the basis of poly caprolactone diol (3M, 3.5M, 4M, 4.5M) for the synthesis of water-based polyurethanes for coating on skin layers of leather. Tensile strength, elongation, and adhesive strength of the prepared samples were measured. As a result of measuring the tensile strength, the tensile strength was found to be 4.09 kgf / ㎟ when 3 moles were applied, and 1.071 kgf / ㎟ when 4.5 moles were applied. Elongation was 366 % when 3 moles of PCL were applied, and 709 % at 4.5 moles. Adhesive strength was 2.887 kgf / cm when 3 moles of PCL was applied and 0.998 kgf / cm when 4.5 moles were applied.

• 한국응용과학기술학회지
• /
• 제36권2호
• /
• pp.524-530
• /
• 2019

본 연구에서는 가죽 스킨층에 코팅용으로 사용할 수용성 폴리우레탄의 합성을 위해 polyrupopylene mono methyl ether (PM)를 기반으로 폴리 에테르 폴리올인 폴리 프로필렌 글리콜과 이소포론 디 이소시아네이트 (isophorone diisocyanate, IPDI)를 합성 하였다. 예비 중합체의 합성 후, 점도 상승을 억제하기 위해 $40^{\circ}C$에서 1M, 2M, 3M 및 4M으로 PM을 첨가하고 중화 반응 및 사슬연장 반응을 수행하여 폴리 우레탄 시료를 준비 하였다. 준비된 시료의 인장강도와 연신율, 접착강도를 측정한 결과로 인장강도는 PM 이 1M 일 때 2.109 kgf/mm2, 4M 에서 1.721kgf/mm2, 연신율은 PM이 1M일 때 496%, 4M 에서 522%, 접착력은 PM이 1M 일 때 1.114 kgf/cm, 4M 에서 0.99 kgf/cm 로 확인 되었다.