• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.303-304
• /
• 2006

The mechanical properties of ferrous powder metallurgy (P/M) materials are directly related to their microstructure. Ferrous P/M materials with sufficient hardenability will develop microstructures containing significant percentages of martensite in the as-sintered condition. Recently, sinter-hardening has developed into a highly cost effective production method through hardened P/M parts without the need for additional heat-treatments. This paper reviews the advances of sinter-hardening as well as some key processing parameters such as sintering temperature, cooling rate, tempering required to produce high quality sinter-hardened components. Specific topics including effect of alloying elements, alloying methods, and the Characterization and observation of microstructure are discussed.

• 열처리공학회지
• /
• 제11권2호
• /
• pp.99-110
• /
• 1998

The effects of pre-heat treatment(Q/T) on microstructure and hardness of SCM435 structural steel nitrided by micro-pulse plasma was investigated. The quenching and tempering temperatures for obtaining matrix hardness of SCM435 steel on range of HRC30 to HRC40 desired for machine parts were about $860^{\circ}C$ and $500^{\circ}C$ respectively. The case depth of SCM435 nitrided at $480^{\circ}C$ for 5 hours was independent of pre-heat treatment condition and was approximately $150{\mu}m$. However, hardness and compactness of nitrified layer on Q/T treated specimen were more heigher than annealed specimen. The case depth increased linearly with the increase of nitriding temperature, however, the hardness of nitrified layer decreased with the temperature. Phase mixture of ${\gamma}^{\prime}$-phase($Fe_4N$) and ${\varepsilon}$-phase($Fe_3N$) were detected by XRD analysis in the nitrified layer formed at optimum nitriding condition, and only single ${\gamma}^{\prime}$-phase was detected in the nitrified layer formed at higher nitriding temperature such as $540^{\circ}C$. The optimum nitriding temperature was approximately $480^{\circ}C$ which is lower than tempering temperature for preventing softening behavior of SCM435 matrix during nitriding process and the surface hardness of nitrified layer obtained by optimum preheat treatment condition was about Hv930.

• 한국산업융합학회 논문집
• /
• 제9권1호
• /
• pp.51-59
• /
• 2006

The study is diagnosis about fatigue failure phenomenon of heating coil spring (sup9) and heat treatment method that is used to crusher. Because more than 80~90% of damage announcement of breakdown of machine and construction is been caused in fatigue present state, fatigue failure became important leading person at design. Calculated design load is imposed repeatedly that fatigue breakdown is safe. Is phenomenon that change load is imposed in the construction continuously. Used coil spring applies heat 30minute by Quenching temperature $860^{\circ}C$ if see manufacturing process and temperature of gasoline of $50^{\circ}C$ keep after quench that know tempering a $460^{\circ}C$ 90minute a product be. If doto apply heat $950^{\circ}C$ material at rolling process historically before quenching, austenite formation clay pipe being done AGS(Austenite Grain Size) by 2.5~4 become. Apply heat quenching 30minute by $820^{\circ}C$ by improvement method and after quench that keep $50^{\circ}C$ in oil tempering if do $450^{\circ}C$, 90minute spring ideal formation sorbite formation of the river form and condition that satisfy most more than AGS 7 appeared. Also, we can secure authoritativeness through MT since shot peening processing.

• 한국농공학회지
• /
• 제17권1호
• /
• pp.3677-3684
• /
• 1975

A newly devised dryer with heated air for the farm products, especially suited for high water content materials such as red pepper, Beer ground, each Vegetables, and Low water content materials such as Rough rice was tested for its thermal efficiency and drying mechanism, and the optimum conditions for each sample were established. In order to improve the present rural situation of drying farm products which entirely dependent upon natural solar radiation, a study upon an economic multi-parpose dryer was conducted. A series of drying tests were run first with red pepper which is one of the important cash crop in Korean farm. And successive series of tests were also run with such proaucts as garlic, sweet potatoes, green onion, radish, Beer ground and Rough rice. The results from the above experiment in drying system with heat dryer can be summarized as follows. 1. Drying duration could be shortened by the tempering effect in high water content crop such as red pepper and beer ground. 2. The color changes occured in around 20% water content in red pepper. The degree of color change was heavily affected by high temperature and short drying duration. 3. The drying condition of red pepper was most favourable at the temperature of 85$^{\circ}C$ in early stage and 80$^{\circ}C$ in middle stage and 75$^{\circ}C$ at the final stage, and with the air rate of 0.81㎥/sec and with sample amount of 200kg. 4. The drying condition of Rough rice(I.R.667) was most favourable at the templature of 40$^{\circ}C$ in early stage and 35$^{\circ}C$ in middle stage and final stage and with the air rate of 0.2㎥/sec and with sample amount of 75kg. 5. In order to prevent the color change of red pepper and to assure high efficiency in drying mechanism, it was necessary to lower the temperature as the time passes in drying process. 6. For vege tables, the drying rate were short in early stage and there was also tempering effect. However, for garlics, Constant drying rates through the early and final stages were observed and there were no tempering effects. 7. The drying condition or capability were as follows; Sample drying temp($^{\circ}C$) amount of material(kg) drying time(hr) Red pepper 85 200 9 Garlic 85 150 7 Sweet potato 85 200 6 Green Onion 85 200 4 Carrot 85 200 4 Radish 90 250 4 Rough rice(I.R.667) 35 75 4 Beer ground 90 320 3 Considering the above result of experiments, if this kind of dryers were distributed Korean farm and the optimun process were practiced in rural area, it would certainly help them improving the qualites of their product preventing their undue losses, and thus assuring an increase of Korean farm income and promotion of their living standards.

• 열처리공학회지
• /
• 제6권2호
• /
• pp.59-69
• /
• 1993

Bending fracture strength test and impact strength test were made for VC coated die steels treated by immersing in molten borax bath and for hardened steels which were quenched and tempered, in order to clarify the effect of VC coating at $1000^{\circ}C$. The material used in this investigation was representative cold and hot work die steels STD11, STD61. The results obtained are as follows. 1) The bending fracture strength of VC coated die steel (STD11, STD61) was lessened with increasing the thickness of the VC coated layer. 2) With increasing the immersing time (imcreasing the thickness of the VC coated layer) the maximum hardness was obtained at 480 minutes holding, after that holding time hardness was decreased. 3) The impact strength of the VC coated die steel was not decreased. In the casse of STD11, it was higher than that of the quenched condition especially at low tempering temperature, and vice versa at high tempering temperature. However in the case of STD61 shows the result to the contrary.

• 열처리공학회지
• /
• 제3권4호
• /
• pp.10-22
• /
• 1990

A study has been investigated on the effect of mechanical properties (tension strength, rotary bending fatigue strength, wear resistance, hardness) according to the carbide particle size variation by the treatment of 1) quenching tempering, and 2) quenching, subzero treatment and tempering. The material used in this investigation was a typical bearing steel, high C high Cr, AISI E 52100. The result obtained in this study were as follows : (1) Finer the carbide particle size increasing the hardness and retained austenite in same quenching condition. (2) Finer the carbide particle size reduced the tension and rotary bending fatigue which were resulted from austenite grain growth and carbide precipitation on grain boundry that induced by carbide refine heat treatment. (3) Finer the carbide particel size increasing the wear resistance which were resulted by uniform distribution of carbide and increased hardness induced by microstructural uniform hardenability of matrix. (4) When the carbide particles were refinded, subzero treatment is effective only wear resistance and hardness.

• 열처리공학회지
• /
• 제13권6호
• /
• pp.405-411
• /
• 2000

The effects of added elements, such as Co or Nb, on wear properties of high speed steel by powder metaliurgy(PM-HSS) had been eluminated in auther's previous paper. In addition, it is generally known that the wear properties of materials have been influenced by heat-treating conditions as well. Therefore, a study has been done to clarify the effects of heat-treating conditions on wear properties of PM-HSS. The wear tests have been performed under the same conditions as the previous paper using heat-treated PM-HSS(5%Co-1%Nb) with different quenching and tempering temperatures. The result of this paper shows that wear resistance of PM-HSS is improved with relatively high quenching temperature. However, tempering temperature is not sensitive to the wear resistance in the range of high quenching temperature. It may be deduced by the fact that the shear strength of matrix by strengthening mechanisms due to not only the quenching aging but also dispersion-hardening is improved.

• 대한안전경영과학회:학술대회논문집
• /
• 대한안전경영과학회 2009년도 추계학술대회
• /
• pp.471-481
• /
• 2009

This study is deal with the high frequency induction hardening (HF at $850^{\circ}C$, 120kHz & 50kW condition) SM45C steel. (1) The HF specimen which was tempered at $150^{\circ}C$, did not appear any tempering effect. A brittle fracture occurred at rounded area of the tensile specimen. AE amplitude distribution showed between 45~60dB. (2) The HF specimen which was tempered at $300^{\circ}C$, slip and fracture occurred at the hole area of the tensile specimen. As it passes the yield point, the AE energy increased intermittently and AE amplitude distribution showed between 70~85dB. In addition, after the maximum tensile load, it showed high amplitude and energy distribution. The AE amplitude showed between 45~70dB. (3) The HF specimen which was tempered at $450^{\circ}C$, a brittle fracture occurred as if it is torn in the direction of $45^{\circ}$ on parallel area over the both sides of the tensile specimen, which led to several peak to be appeared in AE energy. It was found that the AE amplitude was relatively low and the AE energy was high.

• 한국기계기술학회지
• /
• 제13권2호
• /
• pp.93-100
• /
• 2011

This study deals with the high frequency induction hardening (HF at $850^{\circ}C$, 120kHz & 50kW condition) SM45C steel. (1) The HF specimen, which was tempered at $150^{\circ}C$, did not show any tempering effect. A brittle fracture occurred at rounded area of the tensile specimen. AE (acoustic emission) amplitude distribution showed between 45dB and 60dB. (2) A slip and fracture occurred at the hole area of the HF specimen which was tempered at $300^{\circ}C$. As they pass the yield point, the AE energy is increased intermittently and AE amplitude distribution exists between 70dB and 85dB. In addition, after imposing the maximum tensile load, AE signals showed high amplitude and energy distribution. The AE amplitude showed between 45dB and 70dB. (3) A brittle fracture occurred at HF specimen which was tempered at $450^{\circ}C$ as if it is torn in the direction of $45^{\circ}$ on parallel area over the both sides of the tensile specimen, which lead to several peak appeared in AE energy. It was found that the AE amplitude was relatively low and the AE energy was high.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1999년도 제3회 압연심포지엄 논문집 압연기술의 미래개척 (Exploitation of Future Rolling Technologies)
• /
• pp.172-179
• /
• 1999

As the martensite structure cause fracture failure during drawing from 5.5mm rod to 3.05mm dia. wire without additional heat treatment, the optium cooling condition to inhibit the occurrence of martensite was investigated. In order to get SAE9254+V quality, the effects of alloying element, vanadium on the mechanical properties were investigated. Based upon CCT and TTT curves and the results form cooling test in mill, optimun cooling was found in the condition of the laying head temp of 780$^{\circ}C$ and of the conveyor speed at 0.15m/sec with the whole cover closed. The wire rods produced under the condition showed the best mechanical properties of 120kg/$\textrm{mm}^2$ in TS and 50% in RA, having an excellent drawability. In vanadium added steels, tensile strength was improved without degrading elongation and charpy impact value. That means the strengthening by vanadium is mainly due to the grain refinement by the fine precipitates during tempering process.