• 한국의류학회지
• /
• 제22권4호
• /
• pp.525-534
• /
• 1998

Cotton fabrics were finished with mixture of BTCA(1,2,3,4,-butanetetracarboxylic acid) and polyalkyleneoxide-modified amino-functional silicone by pad-dry-cure process to achieve better DP performance with a higher retention of physical properties as compared to those of finished with BTCA alone. The results indicated that BTCA improved the wrinkle recovery but reduced significantly the tensile and tear strength of the treated fabrics. Whereas silicone imparted a lower wrinkle recovery, a lower loss of tensile strength than BTCA, in addition improved considerably the tear strength owing to reduction in inter-fiber and/or inter-yarn frictional forces. The concentration and curing temperature needed to enhance physical properties were as follows; for BTCA treatments 6%, at 18$0^{\circ}C$, for silicone treatments 1% at 14$0^{\circ}C$. This optimum concentration of silicone was observed by using the mixture of BTCA and silicone. The wrinkle recovery and DP rating of cotton fabrics treated with mixture of 4% BTCA and 1% silicone at a curing temperature of 17$0^{\circ}C$ was similar to those of treated with 6% BTCA at a curing temperature of 18$0^{\circ}C$, and other performance properties observed were; an increase in tensile strength, extension, toughness, abrasion resistance and moisture regain due to the reduction of BTCA concentration and curing temperature, futhermore an improvement in bending and surface properties due to the lubricating effect of silicone. On the other hand 1% aqueous silicone solution showed the lowest surface tension. Such nonionic surface activity resulted in a more uniform and rapid deposition of BTCA on the fiber or fabric.

• 대한치과보철학회지
• /
• 제41권5호
• /
• pp.551-564
• /
• 2003

Statement of problem : Magnesium oxide may increase pH of alginate, and supply magnesium ions to the polymerization reaction of alginate. Purpose : This study was designed to evaluate the influence of incorporation of magnesium oxide to alginate composition. Material and Method : Seven kinds of experimental alginates were prepared and used for the experiments. Components with unchanging concentrations were sodium alginate 15%, calcium sulfate 14%, sodium phosphate 2%, and zinc fluoride 3%. Contents of magnesium oxide were varied as 0%, 1%, 2%, 3%, 4%, 5%, 6%. Diatomaceous earth were added to each experimental groups as balance to be 100%. Control group was a MgO 0% group. Working time, setting time, elastic recovery strain in compression, compressive strength and tear resistance were measured were measured. Sample size for each groups were 10. Arithmetic means were used as each groups representative values. Regression test between MgO contents and results, Duncan's multiple range test, and One-way ANOVA test were done between groups at level of 0.05. Results : 1 Magnesium oxide made the working time and setting time as longer(p<0.0001). 2 Magnesium oxide did not alter the elastic recovery(p>0.05). 3. Magnesium oxide contents between 2% and 4% exhibited the lowest strain in compression on alginates(p<0.0001). 4. Magnesium oxide made the compressive strength and the tear resistance stronger(p<0.0001). Conclusion : These results mean that setting time of alginate maybe controlled and that mechanical properties maybe improved by the incorporation of magnesium oxide into alginate, without any reduction of elasticity.

• Elastomers and Composites
• /
• 제40권1호
• /
• pp.12-21
• /
• 2005

본 연구에서는 CSM 에멀젼의 물성을 향상시키고자 금속성 가교제인 magnesium carbonate 및 calcium hydroxide를 첨가하여 가교밀도, 열적특성, 표면자유에너지 그리고 인장강도, 파단신율 및 인열강도 특성을 고찰하였다, 금속성 가교제인 magnesium carbonate 및 calcium hyroxide 양이 증가함에 따라 CSM 에멀젼 필름은 가교밀도는 증가하였고, 이에 내수성과 $T_g$ 값도 증가하였다. 금속성 가교제로 magnesium carbonate를 첨가하였을 때 calcium hydroxide에 비해서 다소 높은 가교밀도와 $T_g$ 값을 보였다. 하지만 CSM 에멀젼 필름의 표면에너지 및 기계적 특성들은 다소 다른 거동을 보였다. Magnesium carbonate 0.75% 그리고 calcium hydroxide 1.0% 첨가한 경우가 가장 높은 표면 자유에너지 값과 인장강도 및 인열강도를 보였으나, 그 이상의 양을 첨가하였을 경우에는 오히려 감소함을 확인하였다. 그러므로 본 연구에서 CSM 에멀젼의 물성을 향상시키는데 적용되는 금속성 가교제로서 calcium hydroxide 보다 magnesium carbonate가 더 적당하며, 0.75% 첨가하였을 때 보다 향상된 물성을 얻을 수 있었다.

• 품질경영학회지
• /
• 제16권1호
• /
• pp.43-48
• /
• 1988

Most of silicone used for water repellent finish is MHP (methyl hydrodiene polysiloxane), which is formed by hydrolysis and condensation polymerization of MHD (methyl hydrodiene dichlorosilane: Me H Si $Cl_2$). The cross-linking theory explains the water repellent mechanism of MHP. The silicone finish on fiber could improve in handle, softness, abrasion resistance, soil repellency, tear strength and crease resistance, as well as water repellency. According to using method silicone-water repellent finishing agents, could be devided into air dry type and curing type. MHP is the typical curing type of water repellent finishing agent, and this type requires the curing temperature above $150^{\circ}C$ at least. High curing temperature is the very drawback of this curing type. For this reason, there has been global interest in the lowering of its temperature. The objective of this study is to investigate merits of alkali treatment for silicone finishing by ANOVA and LSD (least significant difference).

• Elastomers and Composites
• /
• 제7권1호
• /
• pp.45-52
• /
• 1972

As a series of the studies of EPDM-Polymer blends, the experiments are concentracted to the investigation of the physical properties of the EPDM-NBR blends. The results are shown as follows; 1. As EPDM addition ratio is increased, the physical properties such as resistance to ozone and aging have also improved, on the other hand, elongation and abrasion resistance decreased. 2. Tear strength is less influenced by blending and character after aging exhibited the same result. 3. Tensile strength decreased with increase in EPDM contents, especially the ratio of EPDM/NBR are 50/50 and 75/25.

• Elastomers and Composites
• /
• 제37권2호
• /
• pp.86-98
• /
• 2002

본 연구에서는 실리카/카본블랙 혼합사용과 카본블랙 단독 사용의 경우 상온 또는 고온에서의 인장강도(modulus) 및 인열저항성, 내cutting성, 내crack성을 비교 평가하였다. 실리카와 카본블랙의 함량비 및 단계배합 방법을 통해 NR 가황물을 제조하였으며, 충전제의 함량은 60phr로 고정하였고, semi-EV 가황시스템을 적용하여 실험을 실시하였다. 실리카의 분산은 25phr이하일 때 양호하였으며, 실리카/카본블랙의 함량비가 25/35인 경우 인열에너지, 내crack특성, 내cutting특성이 가장 우수하였다. 충전제로써 카본블랙 단독사용과 실리카/카본블랙(25/35) 혼합사용의 경우를 비교해 보면, 열화에 따른 modulus 및 인장강도, 인열에너지는 실리카/카본블랙(25/35)을 사용한 시편이 더 낮은 감소율을 나타내었다. Cutting특성에서는 카본블랙 단독 사용보다는 실리카/카본블랙(25/35) 혼합사용의 경우가 더 높은 cutting 저항성을 나타내었다. 내crack 특성 또한 실리카/카본블랙(25/35)을 혼합사용한 경우가 온도에 따른 더 높은 변형에너지 완화율(Gp)에도 불구하고 더 낮은 크랙성장속도를 나타내었다.

• 폴리머
• /
• 제35권4호
• /
• pp.342-349
• /
• 2011

실리카의 표면 개질제인 vinyltriethoxysilane(VTEOS)의 함량에 따른 실리카로 보강된 실리콘 고무의 기계적 물성 변화 및 내열성, 내유성, 압축 영구줄음률, 반발탄성 및 가교밀도 변화를 연구하였다. 결과로 VTEOS의 함량이 2.0 phr까지 증가함에 따라 경도는 상승하였으나 인장강도 파단신율, 인열강도가 감소하였다. 내열시험에서는 VTEOS의 함량이 증가될수록 경도변화, 인장강도 변화율, 파단신율 변화율이 크게 감소하였다. VTEOS 2.0 phr에서 가장 우수한 내열특성을 나타내었다. 또한 VTEOS의 함량이 증가될수록 실리콘 고무의 내유성이 증진되었으며, VTEOS 미첨가 시보다 경도 하락폭이 크게 낮았으며, 파란신율 변화율은 약 2배 이상 감소하였다. 반발탄성도 VTEOS의 함량이 증가될수록 우수하였으며, 압축 영구줄음률 역시 VTEOS가 증가될수록 감소하였다. 가교실험 결과 VTEOS가 증가될수록 최대 토크값와 가교밀도가 크게 향상되었다.

• Elastomers and Composites
• /
• 제34권4호
• /
• pp.341-349
• /
• 1999

본 연구에서는 산화방지제의 종류에 따라 천연고무 가황물이 어떠한 내열성과 내크랙성을 가지는지를 평가해 보았다. 가교시스템에 의한 영향을 방지하기 위해 촉진제/황 비율을 0.25로 고정하여 실험을 실시하였다. 페닐렌디아민계 산화방지제는 가교에 참여하여 가교밀도를 증가시킴으로 가황물의 인장강도를 향상시키는 것으로 나타났고, 분산성의 차이에 의해 인열강도는 산화방지제에 따라 거의 2배의 차이가 있음을 보였다. 인열에너지는 인열강도와 유사한 경향을 보였는데 불규칙한 크랙경로를 나타낸 페닐렌디아민계 산화방지제가 첨가된 가황물이 가장 우수하였다. Pure shear test에서도 페닐렌디아민계 신화방지제가 첨가된 가황물이 낮은 크랙 성장 속도와 높은 탄성율에 따른 높은 변형에너지 완화율을 가진 것으로 나타났다. 고무배합물 속에서 뛰어난 분산성과 높은 가교밀도를 보인 페닐렌디아민계 산화방지제가 첨가된 가황물이 우수한 내열성과 내크랙성을 가짐을 알 수 있었다.

• Macromolecular Research
• /
• 제14권2호
• /
• pp.187-193
• /
• 2006

Organoclay, was applied as a filler, in place of carbon black and silica, to a natural rubber (NR)/butadiene rubber (BR) blend. A compounding method was used to disperse and separate the layered silicates. The effect of a coupling agent on the vulcanizates was evaluated using both the silica and organoclay filled compounds. After the compounding processes were completed, the XRD diffraction peaks disappeared, but then reappeared after vulcanization. The scorch times for the organoclay-filled compounds were very short compared to those for carbon black and silica-filled compounds. The organoclay-filled compounds showed high values of tensile strength, modulus, tear energy, and elongation at the break. When ranked by viscosity, the compounds appeared in the following order: silica > silica (Si-69) > organoclay > organoclay (Si-69) > carbon black. Fractional hysteresis, tensile set, and wear rates were very consistent with the viscosity of the vulcanizates. The Si 69 coupling agent increased reversion resistance, the maximum torque values in the ODR, modulus, and wear resistance, but decreased elongation at the break, fractional hysteresis, and tension set of the vulcanizates.

• 한국공간구조학회논문집
• /
• 제8권2호
• /
• pp.55-62
• /
• 2008

막 구조는 형태의 다양성, 막의 가벼움과 내구성, 투광성 및 균질성 때문에 현대 건축물에 다용하게 사용되어 새로운 건축세계를 열어가고 있다. 본 논문은 대공간 건축 구조물에 주로 사용되는 유리섬유 막 재료의 역학적 특성에 대한 연구이다. 현재 주로 사용되는 건축용 막 재료의 종류에는 PVC, PVF, PVDF, PTFE, ETFE 막재들이 있다. 본 연구에서는 이러한 건축용 막재료에 대한 역학적 시험 방법을 정립하고, PTFE 코팅 유리섬유 막재에 대한 인장강도, 인열강도 및 반복하중 시험 등을 실시하여 건축용 막 재료의 역학적 특성을 분석하고자 한다.