• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.170-175
• /
• 2001

It was possible to grow the $Al_{2}O_{3}$ based $Y_{3}A_{5}O_{12}(YAG),ZrO_{2}$ binary and ternary eutectic fibers using micro-pulling down method with a growing rate of 0.1~15 mm/min. While $Al_{2}O_{3}/ZrO_{2}$ showed cellular-lamellar structure, $Al_{2}O_{3}$/YAG and $Al_{2}O_{3}$/YAG/$ZrO_{2}$ternary eutectic fibers showed homogeneous Chinese script lamellar structures. The microstructures of $Al_{2}O_{3}/ZrO_{2}$ binary eutectic fibers changed with solidification rate from lamellar pattern to cellular structure. The interlamellar spacing agreed with the inverse-square-root dependance on pulling rate according to $\lambda$=$kv_p\;{-1/2}$. $Al_{2}O_{3}/ZrO_{2}$ binary eutectic fibers recorded the highest tensile strength of about 1560MPa at room temperature. $Al_2O_3/YAG/ZrO_2$ternary eutectic fiber showed excellent thermal stability to $1200^{\circ}C$ without significant decrease. The maximum strength of ternary eutectic fibers recorded were 1100MPa at $25^{\circ}C$ and 970MPa at $1200^{\circ}C$, respectively.

• Proceedings of the KWS Conference
• /
• 1992.10a
• /
• pp.122-124
• /
• 1992

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.202-209
• /
• 2005

Phase evolution, microstructure and the electrical properties such as $k_p$ and $Q_m$ of $Pb(Mg_{1/3}Nb_{2/3})O_3[PMN]-Pb(Mn_{1/3}Nb_{2/3})O3[PM'N]-PbZrO_3[PZ]-PbTiO_3[PT]$ quaternary system were investigated within the compositional ranges $0{\leq}y{\leq}0.125$, y+z=0.125, and $0.39{\leq}x{\leq}0.54$ of the formula $Pb_{0.97}Sr_{0.03}[Mg_{1/3}Nb_{2/3})_y\;(Mn_{1/3}Nb_{2/3})_z\;(Zr_{x}Ti_{1-x})_{1-(y+z)}]O_3$. In the case of increasing Mn/(Mg+Mn) ratio for a fixed Zr/Ti ratio of 47.5/52.5, phase relation remained unchanged but the grain size drastically decreased, and the electrical properties changed as following: both $k_P$ and $Q_m$ reached the peak values at $Mn/(Mg+Mn)\cong0.3l7$ and gradually decreased; $\varepsilon33^T$ showed a monotonic decrease; P-E hysteresis loop gradually changed to asymmetrical one, and $E_i$ increased in correspondence. With increasing Zr/Ti ratio for a fixed Mn/(Mg+Mn) ratio of 0.317, on the contrary, the cell parameter $(\alpha^2c)^{1/3}$ gradually increased, and tetragonal-rhombohedral morphotropic phase boundary appeared in the range of $51/49{\leq}Zr/Ti{\leq}54/46$. the meantime, the grain size substantially increased, and the electrical properties changed as following: $k_P$ and $\varepsilon33^T$ reached peak values at Zr/Ti=51/49 and 48/52, respectively, and then gradually decreased; change of $Q_m$ was adverse to $k_P$; both $E_C\;and\;E_i$ considerably decreased while $P_S$ moderately increased. For the system 0.125(PMN+PM'N)-0.875PZT studied, the composition Mn/(Mg+Mn)=0.3l7 and Zr/Ti=51/49 revealed some promising electrical properties for piezoelectric transformer application such as $k_P=0.58,\;Q_m\cong1000$, and $\varepsilon^T_{33}=970$, as well as dense and fine-grained microstructure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.3
• /
• pp.169-175
• /
• 2012

Purpose: In this study, brazing characteristics of $ZrO_2$ and Ti-6Al-4V brazed joints with increasing temperature were investigated. Materials and methods: The sample size of the $ZrO_2$ was $3mm{\times}3mm{\times}3mm$ (thickness), and Ti-6Al-4V was $10mm(diameter){\times}5mm(thickness)$. The filler metal consisted of Ag-Cu-Sn-Ti was prepared in powder form. The brazing sample was heated in a vacuum furnace under $5{\times}10^{-6}$ torr atmosphere, while the brazing temperature was changed from 700 to $800^{\circ}C$ for 30 min. Results: The experimental results shows that brazed joint of $ZrO_2$ and Ti-6Al-4V occurred at $700-800^{\circ}C$. Brazed joint consisted of Ag-rich matrix and Cu-rich phase. A Cu-Ti intermetallic compounds and a Ti-Sn-Cu-Ag alloy were produced along the Ti-6Al-4V bonded interface. Thickness of the reacted layer along the Ti-6Al-4V bonded interface was increased with brazing temperature. Defect ratios of $ZrO_2$ and Ti-6Al-4V bonded interfaces decreased with brazing temperature. Conclusion: Thickness and defect ratio of brazed joints were decreased with increasing temperature. Zirconia was not wetting with filler metal, because the reaction between $ZrO_2$ and Ti did not occur enough.

• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.630-638
• /
• 1992

Ta2O5 alloying into 3 mol% Y2O3-stabilized tetragonal ZrO2 polycrystals (3Y-TZP) increased the degradation during aging at 265℃ and the fracture toughness; both are determined by the amount of transformed m-ZrO2. It was proposed that the mechanism underlying the t→m transformation when aged at low temperatures is attributed to the reorientation of (Zzr'V ). complexes parallel to [111] lattice direction, which is accompanied by a relaxation of TZP lattice during annealing at low temperature. A small strain which results from the reorientation gives rise to a localized mechanical instability, thus lowering the nucleation barrier so that the t→m phase transformation (degradation) proceeds. The amount of transformed m-ZrO2 during aging becomes greater as the chemical free energy change related to the transformation, ΔGo, increases with increasing the Ta2O5 alloying content.

• The Journal of Engineering Research
• /
• v.6 no.2
• /
• pp.33-38
• /
• 2004

To investigate the reliability of the MTJs on the roughness of insulating tunnel barrier, we prepared two MTJs with the different uniformity of barrier thickness. Namely, the one has uniform insulating barrier thickness; the other has non-uniform insulating barrier thickness as compared to different thing. As to depositing amorphous layer CoZrNb under the pinning layer IrMn, we achieved MTJ with uniform barrier thickness. Toinvestigate the reliability of the MTJs dependent on the bottom electrode, time-dependent dielectric breakdown (TDDB) measurements were carried out under constant voltage stress. The Weibull fit of out data shows clearly that $t_{BD}$ scales with the thickness uniformity of MTJs tunnel barrier. Assuming a linear dependence of log($t_{BD}$) on stress voltages, we obtained the lifetime of $10^4$years at a operating voltage of 0.4 V at MTJs comprising CoNbZr layers. This study shows that the reliabilityof new MTJs structure was improved due to the ultra smooth barrier, because the surface roughness of the bottom electrode influenced the uniformity of tunnel barrier.

• International Journal of Railway
• /
• v.3 no.1
• /
• pp.19-27
• /
• 2010

In the present study, the electrical sliding wear and corrosion resistance of pure copper (Cu) and six age-hardened copper alloys (CuCr, CuZr, CuCrZr, CuNiSiCr, CuBe and CuBeNi) were investigated by a pin-on-disc tribometer and electrochemical measurement. Various copper-based alloys in the form of cylindrical pin were forced to slide against a counterface stainless steel disc in air under unlubricated condition at a sliding velocity of 31 km/h under normal load up to 20 N with and without electric current. The worn surface of and wear debris from the specimens were studied by scanning electron microscopy. Both mechanical wear and electrical arc erosion were the wear mechanisms for the alloys worn at 50 A. Owing to its good electrical conductivity, high wear and corrosion resistance, CuCrZr is a promising candidate as the overhead catenary material for electric traction systems.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1177-1185
• /
• 1996

Y-TZP/Ce-TZP ceramics having relative sintered densities of>95% average grain sizes of 0.36$\mu\textrm{m}$ microhar-dness of 1150 kg/mm2 fracture strength of 390-830 MPa and toughness of 6.4-10.2 MPa$.$mm1/2 were prepared by conventional sintering of 3 mol% Y2O3-ZrO2 and 12 mol% CeO2-ZrO2 powders at 1400 and 1500$^{\circ}C$ The average grain sizes of Y-TZP/Ce-TZP ceramics were mainly governed by those of Ce-TZP. White increasing Ce-TZP content toughness increased while microhardness and fracture strength decreased. With comparing microhardness and toughness fracture strength was more sensitive on not only grain size but also other factors such as microstructural and compositional variations. The densification of Y-TZP/Ce-TZP cermaics was not greatly affected by composition and soaking time at temperature over 1400$^{\circ}C$ With increasing CE-TZP content the stability of t-ZrO2 decreased under thermal aging in air whereas increased in hydrothermal atmosphere and aqueous solution.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.3
• /
• pp.233-238
• /
• 2000

t-$ZrO_2/Al_2O_3$composites having a superior biocompatability and phase stability were prepared by adding 0~4 mol% of $Eu_2O_3$and sintered for 1 h at $1600^{\circ}C$ to evaluate phase stability, chromaticity and mechanical properties of the composites. No tetragonal to monoclinic phase transformation was observed for the composites containing $Eu_2O_3$after heat treatment for 20 h at $180^{\circ}C$ under 3.5 MPa water vapor pressure condition. As $Eu_2O_3$content increased, the color of the composites was changed from a slight white ivory to a light pink. The strength and the fracture toughness of the composites containing $Eu_2O_3$were above 620 MPa and 7.6 MPa.$m^{1/2}$, respectively, when $Eu_2O_3$was added up to 3 mol%.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.