• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.679-682
• /
• 2004

Air void systems in hardened concrete has an important influence on concrete durability such as freeze-thaw resistance, water permeability, surface scaling resistance. Linear traverse method and point count method described at ASTM is the routine analysis of the air void system that have been widely used to estimate the spacing factor in hardened concrete. Recently, many concretes often have a spacing factor higher than the generally accepted $200-250{\mu}m$ limit for the usual range of air contents. This study is proposed to estimate the matrix spacing factor by calculation of simplicity. The matrix spacing factor needs two parameters that are air content and numbers of air voids in the hardened concrete. Those are obtained from the standard air-void system analysis of the ASTM C 457. The equation is valid for all values of paste-to-air ratio because the estimation of paste content is unnecessary at the using ASTM C 457. The matrix spacing factor yields a similar estimate of the standard spacing factor.

• 한국구조물진단유지관리공학회 논문집
• /
• 제19권3호
• /
• pp.30-38
• /
• 2015

적설한랭지의 경우, 동절기의 동해 및 적설에 의한 교통통행의 원활을 기하기 위하여 제설제를 사용한다. 이와 같은 제설염의 사용은 동결융해 및 염화물에 의해 콘크리트의 급속한 스케일링 피해를 야기시킨다. 이에 대한 피해로 인하여 콘크리트 포장은 콘크리트의 피복두께 감소에 따른 조기 열화 및 사용자의 안정성 등 여러 가지 문제를 발생시킨다. 이에 따라 국외적으로 이와 같은 현상에 대하여 평가를 하기 위해 다양한 시험 및 평가 방법이 제시되고 있다. 하지만 국내에서는 아직 평가방법에 대한 규정은 없으며, 관련 연구 또한 미미한 수준이다. 따라서 본 논문에서는 각 기관 및 나라에서 제시되고 있는 평가방법을 조사하고, 각각의 규정에 따라 실험을 수행하여 결과를 도출하여 비교 분석하였다. 나아가 이와 같은 실험방법과 실험결과의 고찰을 통하여 국내현장에 맞는 실험법을 제안하고자 한다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1991년도 가을 학술발표회 논문집
• /
• pp.158-161
• /
• 1991

By applying the newly developed techniques of polymer impregnated concrete (PIC) severely deteriorated and low quality concrete can be restored to an adequate structural material. Early deterioration of concrete causes severe problems for bridge deck concrete, pavement concrete for highways and airports, hydraulic structures and buiilding structures. Deterioration has its orgin in cracks on concrete surface, scaling of spalling due to freezing and thawing, neutralization of concrete, penetrations of water, salt, and calcium chloride. The objective of this study is to develope the new surface impregnants and strengthening techniques for them. It is found that the new impregnants and strengthening techniques developed in this study can retian the charecteristics of the existing concrete and decrease deterioration, and also increase durability, chemical resistance, strength, stiffness and ductility of the existing concrete.

• 한국방재학회 논문집
• /
• 제9권3호
• /
• pp.41-47
• /
• 2009

포스트텐션 콘크리트 포장(post-tensioned concrete pavement ; PTCP)은 초장스팬 콘크리트 포장(l=120 m)을 구현하고 장기공용성(40년 이상)을 확보하기 위해 개발되었다. 본 논문에서는 PTCP공법의 장점을 효율적으로 활용하기 위하여 고내구성 콘크리트 재료개발에 대한 연구를 수행하였다. 첫째로, 알칼리 골재반응을 억제할 수 있도록 플라이 애시를 20% 치환(단위바인더량대비)하고, 둘째로, 조기강도확보 및 투수저항성을 개선하기 위하여 실리카흄을 적용하였다. 삼성분계 콘크리트의 역학적 특성, 투수저항성 및 표면박리저항성을 평가한 결과, 실리카흄 첨가에 따라 조기강도가 현저히 개선되고, 투수저항성이 "Low"에서 "Very Low" 등급으로 개선되는(ASTM C 1202 기준) 것으로 나타났다. 그러나 실리카흄 첨가량이 증가함에 따라 표면박리저항성이 저하되므로, 내구성을 고려한 현장 적용성을 확보하기 위해서는 단위바인더량 대비 5%이하로 첨가되는 것이 바람직한것으로 나타났다. 공극구조 분석결과, 개선배합에서 간격계수(spacing factor)가 $250\pm15\mu m$로 평가되어 내구성 지수가 향상된 것으로 나타났다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제14권2호
• /
• pp.171-175
• /
• 2010

본 연구는 동결융해, 염해 및 중성화가 복합적으로 작용하는 콘크리트 구조물의 내구성능을 평가하기 위하여 일반강도 콘크리트를 대상으로 동결수를 달리하여 동결융해 시험을 실시함으로서 염해와 동결융해 복합작용에 의한 콘크리트의 열화를 평가하였고, 염해, 동결융해 및 중성화의 세가지 열화가 복합적으로 발생되는 복합열화에 대해서는 적절한 평가방법이 부재하여 동결수에 따른 동결융해 시험 후의 시험체에 대하여 중성화 촉진시험을 실시함으로서 복합열화에 의한 콘크리트 내구성능 저하 특성을 평가하고자 하였다. 본 연구를 통하여 동결수의 종류나 물-결합재비 수준과 무관하게 고로슬래그미분말을 사용한 배합의 경우 염해와 동결융해가 동시에 복합적으로 발생되는 환경에서도 우수한 저항성능을 보이는 결과를 나타내므로 동결융해를 포함한 복합열화 환경에서 충분한 내구성 확보를 위해서는 최소한의 설계기준강도의 확보와 고로슬래그미분말 등 적절한 시멘트 결합재의 선정이 무엇보다 중요하다는 결론을 얻었다.

• 한국방재학회 논문집
• /
• 제8권6호
• /
• pp.47-52
• /
• 2008

겨울철 도로의 결빙을 방지하기 위하여 염화물계 제설제가 많이 사용되고 있으며, 매년 사용량이 증가하고 있다. 이러한 제설제의 사용은 구조물의 부착강도 저하, 표면스케일링, 환경오염을 발생시킨다. 본 연구에서는 17년간 사용해 온 콘크리트 도로 시설물의 피해상황에 대하여 현장조사를 실시하였으며, 기존 제설제와 개발된 친환경 제설제의 부식 저항성에 대한 비교 실내실험을 수행하였다. 현장피해 조사결과에 따르면, 제한 염화물량의 침투 깊이는 평균 40 mm정도로 나타났고, 조사구간의 표면 염화물 농도는 $3.45kg/m^3$으로 조사되었으며, 이에 비해 탄산화 깊이는 매우 적었다. 한편, 친환경 제설제의 경우, 기존 염화물계 제설제에 비해 염화물 침투 깊이가 적었으며, 부식저항성도 높은 것으로 나타났다.

• 산업기술연구
• /
• 제25권A호
• /
• pp.39-47
• /
• 2005

Air void systems in hardened concrete has an important influence on concrete durability such as freeze-thaw resistance, water permeability, surface scaling resistance. Linear traverse method and point count method described at ASTM are the routine analysis of the air void system that have been widely used to estimate the spacing factor in hardened concrete. Recently, many concretes often have a spacing factor higher than the generally accepted $200-250{\mu}m$ limit for the usual range of air contents. This study is proposed to estimate the plane spacing factor by calculation of simplicity. The plane spacing factor need two parameters that are air content and numbers of air voids in the hardened concrete. Those obtained from the standard air-void system analysis of the ASTM C 457. The equation is valid for all values of paste-to-air ratio because the estimation of paste content is unnecessary at the using ASTM C 457. The plane spacing factor yields a similar estimate of the standard spacing factor.

• 한국도로학회논문집
• /
• 제15권5호
• /
• pp.101-110
• /
• 2013

PURPOSES : The purpose of this study is to evaluate the durability of ternary blended concrete mixtures adding ultra fine admixture. METHODS : From the literature review, crack was considered as the main distress failure criterion on concrete bridge deck pavement. To reduce the initial crack development due to drying shrinkage, CSA expansion agent and shrink reduction agent were used to ternary blended concrete mixtures as a admixture. Laboratory tests including chloride ion penetration test, surface scaling test, rapid freeze & thaw resistance test, non restrained drying shrinkage and restrained drying shrinkage test were conducted to verify the durability of ternary blended concrete mixtures. RESULTS : Based on the test results, proposed mixtures were verified as high qualified durable materials. Expecially initial drying shrinkage crack was not occurred in ternary blended concrete mixtures with CSA expansion agent. CONCLUSIONS : It is concluded that the durability of proposed ternary blend concrete mixture was acceptable to apply for the concrete bridge deck pavement.

• Journal of Periodontal and Implant Science
• /
• 제27권4호
• /
• pp.819-828
• /
• 1997

The purpose of this study was to evaluate the abrasion-resistance of root surface after NaF iontophoresis, Nd:YAG laser irradiation and combined treatment 50 anterior teeth with flat interproximal root surface that had been extracted due to periodontal destruction were selected. All teeth were treated by the same procedure as conventional periodontal root treatment, such as scaling and root planing, root conditioning with tetracycline HCI(lOOmg/ml, 5min). The pre-treatment weight of each tooth was measured by a dial scale(SHIMADEU Co, LIBROR EB-220HU, capacity 220.000 g, Japan). All teeth were divided into 5 groups as follows: Nd:YAG laser irradiation(group 1, 1 W, 100 mJ, 10Hz, fiberoptic-root surface distance=5mm, $10\;sec.{\times}6times$, EL.EN.EN060, Italy): NaF iontophoresis(group 2, $150{\mu}A$, 4 min}: Nd:YAG laser irradiation following NaF iontophoresis(group 3): NaF iontophoresis following Nd:YAG laser irradiation(group 4): No treatment(control group). Electric toothbrushing (Oral-B, Brown Co, Germany) was conducted during 1 hour($lO\;min.{\times}6\;times$). Subsequently post-treatment weight was remeasured by the same method as pre-treatment weight measurement. The difference of abrasion rate among all groups was statistically analyzed by ANOVA(SAS program). Following results were obtained: 1. The abrasion rate was significantly lower in Nd:YAG laser irradiation group than NaF iontophoresis group(p < 0.001). 2. The abrasion rate was significantly lower in combined groups of Nd:YAG laser irradiation and NaF iontophoresis than either Nd:YAG laser irradiation group or NaF iontophoresis group(p < 0.001). 3. There was no significant difference in abrasion rate according to application order in the combined groups(p > 0.05). 4. The abrasion rate was significantly lower in all experimental groups than control group(p < 0.001). The results suggest that combined treatment of Nd:YAG laser irradiation and NaF iontophoresis on exposed root surface after periodontal therapy can enhance the abrasion-resistance of root surface and may inhibit the root caries development.

• 한국도로학회논문집
• /
• 제11권3호
• /
• pp.51-60
• /
• 2009

본 연구에서는 고강도 고내구성 시멘트콘크리트 포장을 위하여 도출된 배합 콘크리트의 굳지않은 콘크리트 특성, 강도발현 특성, 염소이온의 투수특성 및 동결-융해에 대한 저항성 등의 역학적 내구적 특성을 분석하였다. 제시된 배합의 목표스럼프와 공기량은 적절한 혼화제의 사용으로 확보가 가능하나, 혼화제의 적정사용량은 충분한 현장배합실험을 통하여 구하여야 할 것이다. 단위시멘트량을 증가한 경우 일반적으로 강도가 증가하였으며 특히 재령 28일 이후의 강도가 지속적으로 증가하는 양상을 나타내었다. 휨강도는 그 특성상 단위시멘트량을 증가하더라도 뚜렷한 효과는 나타나지 않았다. 염소이온 침투저항성도 단위시멘트량보다는 재령에 따른 영향을 더 크게 받는 것으로 나타났다. 공기량에 가장 많은 영향을 받는 동결-융해 저항성은 각 실험변수에 대한 시험체를 공기량이 3% 이하 및 이상인 경우에 대하여 그리고 동결시 수돗물을 사용한 경우와 현장의 열악한 환경을 모사하기 위하여 4%의 NaCl 용액을 사용한 경우로 구분하여 실시하였다. 공기량에 상관없이 수돗물을 사용한 경우에는 동결-융해반복회수가 300회까지 상대동탄성계수나 표면의 손상이 거의 발생하지 않았다. 4% NaCl 용액을 사용한 경우에는 단위시멘트량이 현재의 한국도로공사의 표준배합인 경우 손상이 발생하였으며, 단위시멘트량이 동결-융해 저항성에 미치는 영향이 큰 것으로 나타났다. 따라서, 동결-융해에 대한 저항성을 충분히 확보하는 고내구성의 시멘트콘크리트 포장을 위해서는 단위시멘트량을 현재의 수준보다 증가시키는 것이 유리한 것으로 판단되며, 실험결과로부터 이러한 요구성능을 발휘하기 위해서는 단위시멘트량을 400kg/$m^3$ 이상으로 할 것을 권장한다.