• Progress in Superconductivity and Cryogenics
• /
• v.18 no.2
• /
• pp.5-7
• /
• 2016

We present an experimental investigation of the superconducting transition temperatures, $T_c$, of superconductor/ferromagnet bilayers with varying the thickness of ferromagnetic layer. FeN was used for the ferromagnetic (F) layer, and NbN and Nb were used for the superconducting (S) layer. The results were obtained using three different-thickness series of the S layer of the S/F bilayers: NbN/FeN with NbN thickness, $d_{NbN}{\approx}9.3nm$ and $d_{NbN}{\approx}10nm$, and Nb/FeN with Nb thickness $d_{Nb}{\approx}15nm$. $T_c$ drops sharply with increasing thickness of the ferromagnetic layer, $d_{FeN}$, before maximal suppression of superconductivity at $d_{FeN}{\approx}6.3nm$ for $d_{NbN}{\approx}10nm$ and at $d_{FeN}{\approx}2.5nm$ for $d_{Nb}{\approx}15nm$, respectively. After shallow minimum of $T_c$, a weak $T_c$ oscillation was observed in NbN/FeN bilayers, but it was hardly observable in Nb/FeN bilayers.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.790-793
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$ single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1 ${\mu}{\textrm}{m}$. When BaTiO$_3$is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4 $\times$ 10$^4$ A/cm$^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.11
• /
• pp.959-962
• /
• 2000

We have fabricated good quality superconducting YBa$_2$Cu$_3$$O_{7-x}$(YBCO) thin films on Hastelloy(Ni-Cr-Mo alloys) metallic substrates with CeO$_2$and BaTiO$_3$buffer layers in-situ by pulsed laser deposition in a multi-target processing chamber. YBCO film with CeO$_2$single buffer layer shows T$_{c}$ of 71.64 K and the grain size less than 0.1${\mu}{\textrm}{m}$. When BaTiO$_3$ is used as a single buffer layer, the grain size of YBCO is observed to be larger than that of YBCO/CeO$_2$by 200 times and the transition temperature of the film is enhanced to be about 84 K. CeO$_2$/BaTiO$_3$double buffer layer has been adopted to enhance the superconducting properties, which results in the enhancement of the critical temperature and the critical current density to be about 85 K and 8.4$\times$10$^4$ A/$\textrm{cm}^2$ at 77 K, respectively mainly due to the enlargement of the grain size of YBCO film.ilm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.280-281
• /
• 2005

We have studied the superconducting properties and flux pinning enhancement of $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{1.8}Ba_{2.4}Cu_{3.4}O_y$ [(YNS)-1.8] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5$ [(YNS)211] nonsuperconducting particles were uniformly dispersed in large (YNS)123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-1.8 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd.

• Progress in Superconductivity and Cryogenics
• /
• v.24 no.1
• /
• pp.18-22
• /
• 2022

The effect of electron beam (EB) irradiation on superconducting properties and microstructures of MgB₂ bulk superconductors were investigated. At E-beam doses of 1×10¹⁶ e/cm² and 1×10¹⁷ e/cm², the effect of irradiation on a superconducting transition temperature (T_c) of MgB₂ was weak. As a dose increases to 5×10¹⁷ e/cm², T_c decreases by 0.5 K. The critical current density (J_c) measured at 4.2 K and 20 K, and 0 T - 5 T increases slightly as exposure time increases. X-ray diffraction for the irradiation surface of MgB₂ shows that the diffraction intensity of (hkl) peaks decreases proportionally as the exposure time increases. This indicates that the crystallinity of MgB₂ was degraded by irradiation. TEM investigation for the irradiated sample showed distorted lattice structure, which is consistent with the XRD results. The J_c increase and T_c reduction of MgB₂ by irradiation are believed to be caused by the lattice distortion.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.3
• /
• pp.55-59
• /
• 2009

In attempts to closely study the effect of high efficiency, friendly environment HTS(High Temperature Superconducting) cable and SFCL(Superconducting Fault Current Limiters) on power system, several projects were carried out around the world. Promising results have been achieved in terms of cable capacity and reliability. commercial HTS cable and SFCL, however, must not only be only be feasible, but meet practical requirements as well. To facilitate the transition of HTS cable technology from the Lab. to the Real Grid, a New project for applying 22.9kV HTS cables and SFCL to the commercial Power Grid supported by Government has just started in KEPCO. Target of this project is to operate two 22.9kV, 50MVA, 150MVA HTS cables and two 22.9kV 630A, 3000A SFCL in a KEPCO Grid in order to demonstrate its reliability and stable operation. This paper will present the technology for selecting appropriate site and its plan for installation & operating of 22.9kV HTS cables & SFCL in KEPCO Grid.

• Progress in Superconductivity
• /
• v.13 no.2
• /
• pp.65-84
• /
• 2011

Study of superconductivity in layered iron-based materials was initiated in 2006 by Hosono's group, and boosted in 2008 by the superconducting transition temperature, $T_c$, of 26 K in $LaFeAsO_{1-X}F_X$. Since then, enormous researches have been done on the materials, with $T_c$ reaching as high as 55 K. Here, we review briefly experimental and theoretical results on atomic and electronic structures and magnetic and superconducting properties of FeAs-based superconductors and related compounds. We seek for clues for unconventional superconductivity in the materials.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.128-132
• /
• 2009

Polycrystalline samples of $(Ru_{0.8}Nb_{0.2})Sr_2(Gd_{1.5-x}Nd_xCe_{0.5})Cu_2O_z$($ 0{\leq}x{\leq}1.25$) have been synthesized by a solid-state reaction route. The X-ray diffraction data revealed that the Nd solubility limit can be placed between x=0.5 and x=0.75. The superconducting transition temperature decreased with increasing Nd content, confirming that Nd entered the lattice. Room-temperature thermoelectric power measurements showed that all the samples are in the underdoped state and the partial substitution of Nd for Gd resulted in a decrease in the carrier density on the superconducting layers.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05a
• /
• pp.17-17
• /
• 1992

The ceramic high transition temperature superconducting materials present many interesting characteristics that will be analysed from two points of view: physical behavior, and chemical aspects. From the first point of view, these materials display an enormous variety of different physical properties. At low doping levels the normal state shows antiferromagnetism and insulating behavior. At intermediate doping levels, an anomalous metallic state appears and, the optimum Tc in the superconducting state is generated. With increasing doping a normal metallic state develops and superconductivity starts to disappear. Many of the physical phenomena that describe the overall behavior when doping levels are changed will be discussed. From the poing of view of the chemical aspects. we well discuss some of the problems involved in the methods of preparation with particular emphasis on defects, crystal structures, critical currrents, and applications in technology.