• Korean Journal of Materials Research
• /
• v.30 no.3
• /
• pp.105-110
• /
• 2020

Cu/PET composite films are widely used in a variety of wearable electronics. Lifetime of the electronics is determined by adhesion between the Cu film and the PET substrate. The formation of an anisotropic nanostructure on the PET surface by surface modification can enhance Cu/PET interfacial adhesion. The shape and size of the anisotropic nanostructures of the PET surface can be controlled by varying the surface modification conditions. In this work, the effect of Cu/PET interface nanostructures on the failure mechanism of a Cu/PET flexible composite film is studied. From observation of the morphologies of the anisotropic nanostructures on plasma-treated PET surfaces, and cross-sections and surfaces of the fractured specimens, the Cu/PET interface area and nanostructure width are analyzed and the failure mechanism of the Cu/PET film is investigated. It is found that the failure mechanism of the Cu/PET flexible composite film depends on the shape and size of the plasmatreated PET surface nanostructures. Cu/PET interface nanostructures with maximal peel strength exhibit multiple craze-crack propagation behavior, while smaller or larger interface nanostructures exhibit single-path craze-crack propagation behavior.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.239-244
• /
• 2011

In this paper, we analyzed the electrical characteristics with crack pattern in crystalline solar cell. crystalline solar cells with a thin substrate, even small shocks can be easily damaged. Before the module goes through many processes, because the solar cells are at risk of a crack. That occurred early in the PV module micro-crack is not easily detection by eye test or output test. Because the EL (Electroluminescence) device has been detected using. PV module is made by laminated of a variety of materials. By different properties of each material will affect the crack. For this reason, the crack will grow and affect the output. And We analyzed the three crack patterns in crystalline solar cell. A growth of cracks on crystalline solar cell was interpreted by analysing generated cracks on the PV modules. Based on this interpretation, an electrical output value was calculated by mathematical modeling on electrical output characteristic with each crack patterns.

• Fisheries and Aquatic Sciences
• /
• v.13 no.1
• /
• pp.49-55
• /
• 2010

A bacterial strain with phytase and glucose-1-phosphatase activity was isolated from seawater. The colony was identified as an Enterobacter cloacae strain and named E. cloacae B11. A gene, agpEnB11, coding for an intracellular acid glucose phosphatase was cloned from the strain and sequenced. It comprised 1,242 nucleotides and encoded a polypeptide of 413 amino acids. Recombinant glucose-1-phosphatase (AgpEn) was overexpressed in Escherichia coli and purified using Ni-NTA column under native conditions. Purified protein displayed a single band of 47 kDa on SDS-PAGE. AgpEn hydrolyzed a wide variety of phosphorylated compounds, with high activity for glucose-1-phosphate and glucose-6-phosphate. Optimum pH and temperature for enzyme activity were pH 5.0 and $50^{\circ}C$, respectively. Enzyme activity was stimulated by $Ca^{2+}$ and $Co^{2+}$, and inhibited by $Cu^{2+}$.

• Journal of Dairy Science and Biotechnology
• /
• v.21 no.2
• /
• pp.88-96
• /
• 2003

Cheese flavor is derived from three main pathways, that are proteolysis, lipolysis and glycolysis, the extent of which varies according to the cheese variety. Proteolysis is the most complex of the three primary events during cheese ripening. The basis of EMC technology is the use of specific enzymes acting at optimum conditions to produce required cheese flavors from suitable substrates. These enzymes consist of proteinases, peptidases, lipases, esterases. The key factors in EMC production are the type of cheese flavor required, the type and specificity of enzyme or cultures used, their concentration and some processing parameters, such as pH, temperature, agitation, aeration, and incubation time. The emulsifiers, bacteriocins, flavor compounds, and precursors also effect to it importantly. The dosage of enzyme or starter culture used is dependent on the intensity of flavor required, processing time and temperature and the quality of the initial substrate. To produce a consistent EMC product it is necessary to have a highly controlled process, and a detailed knowledge of the enzymatic reactions under the conditions used must be fully understood.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.30 no.1
• /
• pp.1-7
• /
• 2016

With a collimated $CO_2$ laser beam, the bidirectional current switching was realized in a two-terminal electronic device based on a highly resistive vanadium dioxide($VO_2$) thin film. A $VO_2$ thin film was grown on a $Al_2O_3$ substrate by a pulsed laser deposition method. For the fabrication of a two-terminal electronic device, the $VO_2$ thin film was etched by an ion beam-assisted milling method, and the $VO_2$ device, of which $VO_2$ patch width and electrode separation were 50 and $100{\mu}m$, respectively, was fabricated through a photolithographic method. A bias voltage range for stable bidirectional current switching was found by using the current-voltage property of the device measured in a current-controlled mode. The transient responses of bidirectionally switched currents were analyzed when the laser was modulated at a variety of pulse widths and repetition rates. A switching contrast was measured as ~3333, and rising and falling times were measured as ~39 and ~21ms, respectively.

• Korean Journal of Metals and Materials
• /
• v.48 no.12
• /
• pp.1064-1069
• /
• 2010

Thin films have been used in a large variety of technological applications such as solar cells, optical memories, photolithographic masks, protective coatings, and electronic contacts. If thin films experience frequent temperature changes, thermal stresses are generated due to the difference in the coefficient of thermal expansion between the film and substrate. Thermal stresses may lead to damage or deformation in thin film used in electronic devices and micro-machined structures. Thus, knowledge of the thermomechanical properties of thin films, such as the coefficient of thermal expansion, is an important issue in determining the stability and reliability of the thin film devices. In this study, thermal cycling of Cu and Ag thin films with various microstructures was employed to assess the coefficient of thermal expansion of the films. The result revealed that the coefficient of thermal expansion (CTE) of the Cu and Ag thin films increased with an increasing grain size. However, the effect of film thickness on the CTE did not show a remarkable difference.

• Mycobiology
• /
• v.51 no.3
• /
• pp.157-163
• /
• 2023

Cordyceps fumosorosea is an important species in the genus of Cordyceps, containing a variety of bioactive compounds, including fumosorinone (FU). This study was a ground-breaking assessment of FU levels in liquid and solid cultures. The present study focused on the impacts of solid-state fermentation (SSF) using solid substrates (wheat, oat, and rice), as well as the effects of fermentation parameters (pH, temperature, and incubation period), on the generation of FU. All the fermentation parameters had significant effects on the synthesis of FU. In a study of 25 ℃, 5.5 pH, and 21 days of incubation period combinations calculated -to give maximal FU production, it was found that the optimal values were 25 ℃, 5.5 pH, and 21 days, respectively. In a solid substrate medium culture, FU could be produced from SSF. At 30 days, a medium composed of rice yielded the most FU (798.50 mg/L), followed by a medium composed of wheat and oats (640.50 and 450.50 mg/L), respectively. An efficient method for increasing FU production on a large scale could be found in this approach. The results of this study might have multiple applications in different industrial fermentation processes.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.351-355
• /
• 1999

BN films with a high content of cubic phase has been deposited by a variety of techniques. It is well known that c-BN films grow with a unique microstructure consisting of $sp^2$ and $sp^{3-}$ bonded layers. Because of existence of the initially grown $sp^{2-}$ /bonded layer, BN films are not adhesive to the substrates. In this study, post-N$^{+ }$ / implantation was applied to improve the adhesion of the films. A Monte Carlo program TAMIX was used to simulate this modification process. The simulation showed nitrogen concentration profile at $1200\AA$ in depth in case of 50keV -implantation energy. FTIR spectra of the $N^{+}$ implanted specimens demonstrated a strong change of absorption band at 1380 cm$^{ -1 }$The films were also investigated by HRTEM. From these results, it is concluded that the post ion implantation could be an effective technique which improves the adhesion between BN film and substrate.

• Korean Journal of Materials Research
• /
• v.34 no.2
• /
• pp.105-110
• /
• 2024

Scanning probe microscopy (SPM) has become an indispensable tool in efforts to develop the next generation of nanoelectronic devices, given its achievable nanometer spatial resolution and highly versatile ability to measure a variety of properties. Recently a new scanning probe microscope was developed to overcome the tip degradation problem of the classic SPM. The main advantage of this new method, called Reverse tip sample (RTS) SPM, is that a single tip can be replaced by a chip containing hundreds to thousands of tips. Generally for use in RTS SPM, pyramid-shaped diamond tips are made by molding on a silicon substrate. Combining RTS SPM with Scanning spreading resistance microscopy (SSRM) using the diamond tip offers the potential to perform 3D profiling of semiconductor materials. However, damage frequently occurs to the completed tips because of the complex manufacturing process. In this work, we design, fabricate, and evaluate an RTS tip chip prototype to simplify the complex manufacturing process, prevent tip damage, and shorten manufacturing time.

• Korean Journal of Environment and Ecology
• /
• v.28 no.3
• /
• pp.302-313
• /
• 2014

This study was conducted to compare the characteristics of fish distribution according to sand type stream and cobble type stream the 4 stream selected every season. The collected Korea endemic species during the survey period were 24, including Acheilognathus gracilis. Dominant species of Hongcheon stream and Muju Namdae stream was Zacco koreanus, each accounting for 39.9% and 28.4% in order, and dominant species in Yanghwa stream was Rhodeus notatus, 13.6%, and those in Gap stream was Z. platypus, by 26.0%. As a result of community analysis, dominant index was 0.27~0.63, diversity index was 1.92~2.67, evenness index was 0.6~0.79, richness index was 3.09~3.53, and dominant index was the highest in Hongcheon stream, and the indices of diversity, evenness and richness were the highest in Yanghwa stream. As a result of tolerance guild analysis, Hongcheon stream and Muju Namdae stream with a variety of substrates accounted for relatively higher rate by 50.1% and 46.4% in sensitive species respectively, and Yanghwa stream and Gap stream with greater sand substrates had 0.5% and 5.3% scarce rate of sensitive species. As a result of similarity analysis using the species, population and substrate structures of the fisheries appeared in each stream, cobble type streams such as Hongcheon stream and Muju Namdae stream were the most similar by 50.4% in species and population, 95.2% in bed structure. As a result of IBI analysis, Hongcheon stream and Muju Namdae stream appeared as 'Class A,' Yanhwa stream and Gap stream as 'Class B' and the two groups of cobble type stream and sand type stream were divided as a result of principal components analysis.