• Journal of the Korea Furniture Society
• /
• v.11 no.2
• /
• pp.45-53
• /
• 2000

This study was carried out to determine the suitability of 3 months old bamboo species of Phyllostachys bambusoides S. et Z., Phyllostachys Pubescens Mazel and Phyllostachys nigra var henonis Stapf as raw materials for the manufacture of strandboard. Total of 108 strandboards were made using urea-formaldehyde resin content level of 12% and one percent of liquid wax emulsion. The strandboard consisted of three layers the top and the bottom layer of which were oriented to the same direction and weighted 25% of the strandboard each. The middle core layer weighed 50% of the board and was perpendicular to the outer top and bottom layers. Analysis was performed to determine the effect of strand lengths and Uowing years of 3 months, 2 years and 3 years on strandboard properties. The physical and mechanical properties of bamboo species and boards were measured and compared to the standard requirements of strandboards. The results are as follows; 1. The more the growing years the higher the density of bamboo. Top part of bamboo indicated higher density value than that of bottom part. 2. Bamboo showed higher static bending strength compared to the main wood species. Longer growing years of bamboo generally inclosed the static tending strength out there were no statistical significancies for Phyllostachys bmbusoides S. et Z. and Phyllostachys pubescens Mazel. 3. Strand length indicated no difference on density and moisture content of strandboard. 5 cm of strand length gave the best static bending strength and internal bonding strength. Bamboo strandboard exhibited lesser extents of thickness swelling than that of CSA standard. 4. 3 months old bamboo gave higher static bending strength of strandboard than those of 2 years and 3 years old bamboo. In case of Phyllostachys nigra var henonis Stapf, 3 months old bamboo indicated higher internal bonding strength than those of 2 years and 3years old bamboo. but in Phyllostachys bambusoides S. et Z., Phyllostachys pubescens Mazel, there were no difference among growing years. Growing years showed no different physical properties of bamboo strandboard.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.6
• /
• pp.13-22
• /
• 2008

Internal voids affecting the mechanical properties of wood composite were classified into two catagories and characteristics of voids were examined according to density variation of strandboard. The void distribution and content of strandboard according to board density were measured by X-ray computed tomography system and analized using image processing software. Prior to investigation, the densities of strandboard were measured by densitometer and the results were showed high correlation with conventional oven drying method. Based on the image analysis conducted on captured images by X-ray tomography, low resolution can be used to capture the macro-voids (between strand) but not the micro-voids (within strands). Intermediate resolution can be used to capture both the macro and the micro-voids and high resolution can be successfully used to capture the majority of the micro-voids. The content of macro-void was measured and content of micro-void was computed by corresponding related equation. The macro-void distribution can be successfully understood and void content can be correctly estimated through the results.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.5
• /
• pp.1-10
• /
• 2008

Decay and mold resistance of zinc borate (ZB) and calcium borate (CB) modified oriented strandboard (OSB) from southern mixed hardwood and southern yellow pine was investigated in this study. Brown rot fungus Gloeophyllum trabeum and white-rot fungus Trametes versicolar were used to examine the decay resistance of the OSB. The OSB test specimens were colonized by brown and white rot fungal mycelium in both the brown and white-rot culture bottles after 8 and 12 weeks, respectively. The wood species and fungus type had the significant effects on the decay resistance. Brown rot decay was evident for all untreated southern pine and mixed hardwood controls. The white-rot decay, however, did not show significant weight loss at both species control samples. The incorporation of ZB and CB composites provides suitable protection against brown-and white-rot fungi. No significant weight loss was observed from the borate treated OSB.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.5
• /
• pp.46-57
• /
• 2007

The leachability of boron in zinc borate (ZB)-modified oriented strandboard (OSB) from southern wood species was investigated in this study. The leaching experiments were conducted by exposing edge-sealed OSB samples under running water at $31^{\circ}C$ for 8, 24, 72, and 216 h. The results from leached samples were compared with those from the unleached controls. Boron leaching of the modified OSB occurred upon the initial water exposure, and the leaching rate decreased as the leaching time increased. Initial boric acid equivalent (BAE) level, wood species, and sample thickness swelling significantly influenced the leachability. There was no consistent effect of polyethylene glycol (PEG) on zinc borate leaching. The glue-line washing within OSB due to thickness swelling of the test samples under water and decomposition of the borate to form water-soluble boric acid were thought to be two possible causes for the observed leaching. The relationship between assayed BAE and leaching time followed a decaying exponential function for zinc borate treated OSB. From the boron/zinc ratio after each leaching period, boron element in ZB was more or less leachable. The material constant of the regression models allowed comparing the leachability of the modified OSB for various wood species. An unified leaching method for treated wood composite materials is needed.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.5
• /
• pp.11-23
• /
• 2008

The mechanical and physical properties of zinc borate (ZB)-modified oriented strandboard (OSB) from southern wood species were investigated in this study. OSB panels treated with ZB were not significantly weaker than the untreated samples in terms of specific modulus of elasticity (SMOE) and specific modulus of rupture (SMOR). ZB showed the negative effect on specific internal bond (SIB) strength, since some of ZB would persist as a powder state on the flake surfaces, thereby reducing the bonding efficiency of the adhesive. The ZB level did not show significant effect on thickness swelling (TS). ZB-modified OSB showed the suitable mechanical and physical properties for the structural wood composites.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.67-72
• /
• 2018

This study was conducted to investigate a potential of Yellow poplar (Liriodendron tulipifera L.) as a raw material for the manufacturing of particleboard (PB) and oriented strandboard (OSB). PB panels were prepared at the parameters of $0.7g/cm^3$ density, 15 mm thickness, three-layer, $E_1$ grade urea-formaldehyde (UF) resin, emulsion wax, and hardener. OSB panels were manufactured with a density of $0.65g/cm^3$, thickness of 10 mm, and $E_1$ grade of UF resin. Particle size of the face layer of PB was 20~80 mesh with 7~9% moisture content (MC), while that of core-layer was 3~20 mesh with 3~5% MC, which was similar to the production condition of commercial PB. As a result, the manufactured PB panels with 15.8 mm thickness, $0.7g/cm^3$ density, and 5.8% MC satisfied the requirement of bending strength of 15 type PB of Korean Industrial Standard (KS F 3104). Both internal bonding (IB) strength and surface screw withdrawal resistance also satisfied the requirement of 18 type PB of the standard. But, the edge screw withdrawal resistance satisfied the requirement of 15 type PB of the standard. These differences in properties could be due to the slenderness ratio of raw particles. In case of OSB panels with 10.7 mm thickness, $0.68g/cm^3$ density, and 5.8% MC satisfied all the requirements of bending strength, screw withdrawal resistance, and IB strength of 18 type PB of the standard. These results suggest that Yellow poplar wood has a good potential as a raw material for the production of PB and OSB.