• Steel and Composite Structures
• /
• v.45 no.6
• /
• pp.819-830
• /
• 2022

This paper presented an experimental study of the bond-slip behavior of reactive powder concrete (RPC)-filled square steel tube. A total of 18 short composite specimens were designed forstatic push-out test, and information on their failure patterns, load-slip behavior and bond strength was presented. The effects of width-to-thickness ratio, height-to-width ratio and the compressive strength of RPC on the bond behavior were discussed. The experimental results show that:(1) the push-out specimens remain intact and no visible local buckling appears on the steel tube, and the interfacial scratches are even more pronounced at the internal steel tube of loading end; (2) the bond load-slip curves with different width-to-thickness ratios can be divided into two types, and the main difference is whether the curves have a drop in load with increasing slip; (3) the bond strength decreases with the increase of the width-to-thickness ratio and height-width ratio, while the influence of RPC strength is not consistent; (4) the slippage has no definite correlation with bond strength and the influence of designed parameters on slippage is not evident. On the basis of the above analysis, the expressions of interface friction stress and mechanical interaction stress are determined by neglecting chemical adhesive force, and the calculation model of bond strength for RPC filled in square steel tube specimens is proposed. The theoretical results agree well with the experimental data.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.190-191
• /
• 2020

The bonding of steel bar to concrete is closely related to the roughness and corrosion degree of steel bar surface. The accelerated corrosion of concrete specimens with different reinforcement diameters was carried out in this test. Through the pullout test of the corroded concrete specimens, the relationship between the bond stress and the displacement of the corroded concrete specimens under the corresponding corrosion degree was obtained. The bond stress of reinforced concrete with different size and corrosion degree are compared and analyzed to find out the influence of corrosion on the bonding property of reinforced concrete.

• Steel and Composite Structures
• /
• v.10 no.4
• /
• pp.317-329
• /
• 2010

According to the results of 9 circular concrete filled steel tube (CFT) push-out tests, a new theoretical model for average bond stress versus free end slip curve is proposed. The relationship between verage bond stress and free end slip is obtained considering some varying influential parameters such as slenderness ratio and diameter-to-thickness ratio. Based on measured steel tube strain and relative slip at different longitudinal positions, the distribution of bond stress and relative slip along the length of steel tube is obtained. An equation for predicting the varying bond-slip relationship along longitudinal length and a position function reflecting the variation are proposed. The presented method can be used in the application of finite element method to analyze the behavior of CFT structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.6 no.1
• /
• pp.103-109
• /
• 2002

Reinforced concrete structure resist to external load caused by integration of steel bar and concrete and this integration is obtained from bond stress between steel bar and concrete. Researches of bond stress between steel bar and concrete have been performed by many researcher, but existent researches of bond stress are concerned with compression strength of well cured concrete and insufficient study of bond stress according to early material. The secure regular strength of concrete in early age is caused by rapid velocity of early hardening process, but questionable bond stress in early age is proportion to strength of that. So this study performed experiments to compare bond stress according to material age and compression strength. The result is showed that bonding strength in early material age compare the ratio of concrete compression strength with the ratio of maximum bond stress the later inferior on the former.

• Journal of the Korea Concrete Institute
• /
• v.11 no.4
• /
• pp.129-136
• /
• 1999

For the prediction of concrete-steel bond ability in reinforced concrete, many countries establish specifications for the pullout test. But these methods hardly to consider many parameters such as strength, shape, diameter and location of steel, concrete restrict condition by loading plate, strength of concrete and cover depth etc, and it is difficult to solve concentration and disturbance of stress. The purpose of this study is to propose a New Ring Test method which can be rational quantity evaluations of bond splitting mechanism. For this purpose, pullout test was carried out to assess the effect of several variables on bond splitting properties between reinforcing bar and concrete. Key variables are concrete compressive strength, concrete cover, bar diameter and rib spacing. Failure mode was examined and maximum bond stress-slip relationships were presented to show the effect of above variables. As the result, it appropriately expressed general characteristics of bond splitting mechanism, and it proved capability for standard test method.

• Computers and Concrete
• /
• v.23 no.4
• /
• pp.273-279
• /
• 2019

Corrosion of the rebar embedded in concrete has a fundamental role in the determination of life and durability of the concrete structures. Researches have demonstrated that artificial neural networks (ANNs) can effectively predict issues such as expected damage in concrete structures in marine environment caused by chloride penetration, the potential of steel embedded in concrete under the influence of chloride, the corrosion of the steel embedded in concrete and corrosion current density in steel reinforced concrete. In this study, data from different kind of concrete under the influence of chloride ion, are analyzed using the neural network and it is concluded that this method is able to predict the bond strength between the concrete and the steel reinforcement in mentioned condition with high reliability.

• Steel and Composite Structures
• /
• v.1 no.2
• /
• pp.231-244
• /
• 2001

The strengthening of reinforced concrete structures using externally bonded steel or advanced fibre reinforced plastic (FRP) composites is becoming increasingly common. A key factor affecting the behaviour and reliability of such strengthened structures is the bond strength between the steel or FRP plate and the concrete substrate. Several different experimental set-ups have previously been used to determine bond strength. This paper presents a careful finite element analysis of the stress distributions in these test set-ups. Results show that stress distributions can be significantly different for different set-ups, for similar materials and geometry.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.561-566
• /
• 2001

Load at steel beam column joints transfered by beam depend on bond strength between concrete and steel tube. But it is different to transmit a load efficiently in the established concrete filled steel tubular column. Therefore, shear-connector is demanded for transfering loads efficiently. An ascent of bond stress and a transmission of load after debonding are expected by a reinforcement of shear-connector

• Advances in concrete construction
• /
• v.10 no.2
• /
• pp.113-125
• /
• 2020

This paper presents experimental results on bond-slip behavior of steel reinforced high-strength concrete (SRHC) after exposure to elevated temperatures. Three parameters were considered in this test: (a) high temperatures (i.e., 20℃, 200℃, 400℃, 600℃, 800℃); (b) concrete strength (i.e., C60, C70, C80); (c) anchorage length (i.e., 250 mm, 400 mm). A total of 17 SRHC specimens subjected to high temperatures were designed for push out test. The load-slip curves at the loading end and free end were obtained, the influence of various variation parameters on the ultimate bond strength and residual bond strength was analyzed, in addition, the influence of elevated temperatures on the invalidation mechanism was researched in details. Test results show that the shapes of load-slip curves at loading ends and free ends are similar. The ultimate bond strength and residual bond strength of SRHC decrease first and then recover partly with the temperature increasing. The bond strength is proportional to the concrete strength, and the bond strength is proportional to the anchoring length when the temperature is low, while the opposite situation occurs when the temperature is high. What's more, the bond damage of specimens with lower temperature develops earlier and faster than the specimens with higher temperature. From these experimental findings, the bond-slip constitutive formula of SRHC subjected to elevated temperatures is proposed, which fills well with test data.

• Structural Engineering and Mechanics
• /
• v.60 no.2
• /
• pp.301-312
• /
• 2016

In a concrete member under pure tension, the stress in concrete is uniformly distributed over the whole concrete section. It is supposed that a local bond failure occurs at each crack, and there is a relative slip between steel and surrounding concrete. The compatibility of deformation between the concrete and reinforcement is thus not maintained. The bond transfer length is a length of reinforcement adjacent to the crack where the compatibility of strain between the steel and concrete is not maintained because of partially bond breakdown and slip. It is an empirical measure of the bond characteristics of the reinforcement, incorporating bar diameter and surface characteristics such as texture. Based on results from a series of previously conducted long-term tests on eight restrained reinforced concrete slab specimens and material properties including creep and shrinkage of two concrete batches, the ratio of final bond transfer length after all shrinkage cracking, to THE initial bond transfer length is presented.