• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.171-177
• /
• 1999

Many lubricated systems experience boundary lubrication condition during operation. However, the friction and wear characteristics of boundary lubrication are not clearly understood. In this work the factors which affect the friction and wear between boundary lubricated metallic surfaces are investigated. Experiments were performed using a pin-on-disk type tester with pure aluminum, pure copper, and SM45C steel as the disk material and steel, stainless steel and bearing ball as the ball. The experimental conditions were determined according to the Taguchi experimental method. From the experimental results, the major factors that influence the friction and wear characteristics of boundary lubrication could be identified.

• Journal of Korean Society of Steel Construction
• /
• v.18 no.4
• /
• pp.469-480
• /
• 2006

The goal of this study is to ases the static and dynamic behavior of disk bearings under railway vehicle loadings. Several static tests were conducted in a laboratory t bearings, all having the same kind of polyurethane disk as used in the static tests, were installed under a full-sized railway bridge and tested with a running locomotive, the tests results, the static and dynamic stiffness of the disk bearings were estimated and compared. the deformation of the disk bearings under the bridge was measured at varying disk bearing was almost half of that under dynamic loading. In addition, the dynamic stiffness of the fixed disk bearing was 80% higher than that of an expansion disk bearing, since the PTFE in the expansion bearing is displaced. The deformation of the disk bearing did not vary significantly with changes in locomotive's speed. The results of this study can contribute to fast-tracking the formulation of a design technique for disk bearings for railway bridges.

• Tribology and Lubricants
• /
• v.18 no.2
• /
• pp.167-172
• /
• 2002

The wear behaviors of ultrahigh molecular weight polyethylene pins against titanium alloy and stainless steel disks moving in two different kinematic motion were investigated by conducting repeat pass rotational sliding and linear reciprocal sliding wear tests. Linear reciprocal motion wore more the polyethylene pin than did repeat pass rotational motion for both disk materials. It means that the repeated directional change of contact stresses generates more wear debris in polyethylene. For the linear reciprocal sliding tests, titanium alloy disks were damaged with some scratches after one million cycles but no surface damage was observed on the polyethylene pins. On the other hand, fur the repeat pass rotational sliding tests, all titanium alloy disks were severely abraded on the entire region of sliding track. This phenomenon can be interpreted by that stress fatigue under repeated sliding contact initiated titanium oxide layer wear particles from disk surface, and these hard particles were embedded into polyethylene pin and then they severely abraded the disk surface. From these results it can be concluded that the kinematic motion in pin-on-disk wear tests play a crucial role on the wear behaviors of UHMWPE pins against titanium alloy and stainless steef discs.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.89-90
• /
• 2006

Austenitic stainless steel has been used as a corrosion resistance material. However, austenitic stainless steel has poor wear resistance property due to its low hardness. In this investigation, we apply powder composite process to obtain hard layer of Stainless steel. The composite material was fabricated from planetary ball milled SUS316L stainless steel powder and WC powder and then sintered by Pulsed Current Sintering (PCS) method. We also added TiC powder as a hard particle in WC layer. Evaluations of wear properties were performed by pin-on-disk wear testing machine, and a remarkable improvement in wear resistance property was obtained.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.11a
• /
• pp.109-116
• /
• 2001

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk in sliding are investigated. Also wear mechanism to form the oxide layer and the characteristics of the oxide layer formation are investigated. AIS152100 steel ball is used for the substrate of coated ball specimens. Two types of coated ball specimens were prepared by depositing TiN coating with 1 and 4um in coating thickness. AISI1045 steel is used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of the two materials, the tests were performed both in ambient for forming oxide layer on the contact parts and in nitride environment to avoid oxidation. And to study the effects of surface roughness of counter-body, TiN coating thickness and contact load of sliding test on the characteristics of oxide layer formation on counter-body, various tests were carried out. From the results, the friction characteristics between the two materials was predominated by iron oxide layer that formed on wear track on counter-body and this layer caused the high friction. And the formation rate of the oxide layer on wear track increased as the real contact area between the two materials increased as the contact load increased, the TiN coating thickness decreased and the surface of counter-body smoothened.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.10
• /
• pp.2597-2605
• /
• 1994

The wear behavior of two types of $Si_3N_4$ exposed to high and low humidity was examined at various sliding speeds, using bearing steel as disk material under pin-on-disk type sliding conditions. Higher wear rates were obtained at a high humidity than at a low humidity. As the sliding speed was increased, the wear rates were decreased and the effect of humidity on the wear rates of $Si_3N_4$ was reduced. The result that the $Si_3N_4$ pin showed higher wear rate under the high humidity condition was explained by the decrease in microhardness of $Si_3N_4$ due to the chemisorbed moisture on the pin and plowing action by the hard particles of $Fe_2O_3$ from the disk. An increase in the sliding speed is supposed to reduce the effect of humidity on the wear rate of $Si_3N_4$ by raising the average temperature of the disk surface and the local temperature at pin-disk contact point.

• Tribology and Lubricants
• /
• v.25 no.4
• /
• pp.217-224
• /
• 2009

In this study, friction tests were carried out in order to investigate the friction behavior of textured surface in unlubricated state using ball-on-disk type apparatus. Test specimens were SUJ2 bearing steel ball and SM45C steel disk. Square arrays of circular micro-dimples were created on the surface of disk specimen by Nd:YAG Laser. Friction tests were performed for the disk specimen with various micro-dimple parameters and was also conducted for the variation of normal loads and relative velocities. The results showed that fiction coefficient of textured surface was lower than that of non-textured surface and the deeper depth of micro-dimple was, the lower friction coefficient obtained at the same diameter of micro-dimple in unlubricated state. Area density of micro-dimple had an effect on the friction coefficient. It was also found that friction coefficient generally decreased with the increase of normal load and relative velocity.

• Proceedings of the KSR Conference
• /
• 2008.06a
• /
• pp.2080-2093
• /
• 2008

Disk brake system take charge of maximum braking energy among the mechanical brake systems for high speed train. For this reason, Metallic friction materials and heat resistant steel disk is adopted at disk brake system for high speed train. It was investigated tribological characteristics(friction coefficient, friction stability, wear rate and braking temperature) between some kinds of metallic friction materials and heat resistant steel disk. Cu-based friction material for high speed train have suitable tribological characteristics.

• Transactions of Materials Processing
• /
• v.20 no.7
• /
• pp.479-484
• /
• 2011

Dry sliding wear behavior of AISI 52100 steel that has a pearlite or bainite microstructure was characterized to explore the effect of microstructure on the wear of the steel. Isothermal heat treatments were employed to obtain the different microstructures. Pin-on-disk type wear tests of the steel disk were performed at loads of 25~125N in air against an alumina ball. Sliding speed and wear distance used were 0.1m/sec and 300m, respectively. Worn surfaces, wear debris and cross-sections of the worn surfaces were examined with SEM to investigate the wear mechanism of the steel. Hardness of the steel was also evaluated. Wear rate of the steel was correlated with the hardness and the microstructure. On the whole, wear resistance increased with an increase in hardness. However, the pearlite microstructure showed superior wear resistance as compared to the bainite microstructure with a similar hardness. The effect of the microstructure on the wear rate was attributed to the morphological differences of the carbide in the microstructure, which was found to have a significant effect on strain hardening during the wear.

• Transactions of Materials Processing
• /
• v.25 no.2
• /
• pp.96-101
• /
• 2016

The current study was conducted to elucidate the effect of cementite morphology and matrix-ferrite microstructure on sliding wear behavior in spheroidized high carbon (1wt. % C) steel. The high carbon steel was initially heat treated to obtain a full pearlite or a martensite microstructure before the spheroidization. The spheroidizing heat treatment was performed on the full pearlitic steel for 100 hours at 700℃ and tempering was performed on the martensitic steel for 3 hours at 650℃. A spheroidized cementite phase in a ferrite matrix was obtained for both the full pearlite and the martensite microstructures. Sliding wear tests were conducted using a pin-on-disk wear tester with the heat treated steel as the disk specimen. An alumina(Al₂O₃) ball was used as the pin counterpart during the test. After the spheroidizing heat treatment and the tempering, both pearlite and martensite exhibited similar microstructures of spheroidized cementite in a ferrite matrix. The spheroidized pearlite specimens had lower hardness than the tempered martensite; however, the wear resistance of the spheroidized pearlite was superior to that of the tempered martensite.