• Economic and Environmental Geology
• /
• v.56 no.1
• /
• pp.103-114
• /
• 2023

The Christian Museum of Gongju Jeil Church was first built in 1931 and was largely damaged during the Korean War, but the walls and chimneys have been preserved. This building has a high architectural values in that the chapel was reconstructed in 1956, and maintains its original form through repair of damaged parts rather than new construction. The stained glass windows were as installed in 1979 and has a great significance in the Dalle de Verre method using lump glass. However, some of the stained glass damaged partially, such as various cracks and splits, and vertical and horizontal cracks in the joint fillers of supporting the colored glass. As the structural materials of the stained glass window, an iron frame and cement mortar filled with it were used, and corrosion of iron, cracking of mortar and granular decomposition appear partially due to weathering. In the joint fillers, the content of Ca and S is very high, indicating that gypsum were used as admixtures, and the gypsums grow in a rhombohedral and forms a bundle, which is investigated to have undergone recrystallization. As a result of modeling the ultrasonic velocity at the joint fillers, the left and right windows at the entrance show relatively weak in the range of 800 to 1,600m/s, and the lower right corner of the altar window and the upper left corner of the center window were also 1,000 to 1,800m/s, showing relatively low physical properties. And gypsums produced during the neutralization of lime mortar were detected in the joint fillers and contaminants on the surface. Such salts may cause damage to the joint material due to freezing and thawing, so appropriate preventive conservation is required. Also, since various damage types are complexly appearing in stained glass window and joint filler, customized conservation treatment should be reviewed through clinical tests.

• Journal of Conservation Science
• /
• v.32 no.3
• /
• pp.425-436
• /
• 2016

The Yakhyeon catholic church (Historic Site No. 252 in Korea) that was constructed in 1892 has been the first western brick structure to ever have existed and one of the most important historical materials in the Korean modern architecture. After a fire had broken out at the catholic church in 1998, the stained glass on the back wall, the slab glass (dalle de verre) introduced by Lee Nam Guy in 1974, was repaired in 1999 because of singe scorch and water leakage. An analysis of the coloration elements showed that yellow, red and green included Zn, K and Cd, respectively. The glass of red contained Se, dark green contained Mn and Cr, and blue contained Pb and S. According to material analysis, the masonry joint was identified dolomite ($CaMg(CO_3)_2$) and calcite ($CaCO_3$), which was observed plate, columnar, rhombic and square of crystalline particles. Meanwhile, ultrasonic velocity in the stained glass recorded low speed in the middle and lower right of the window (an average of 4,130 m/s). And the joint was measured the lowest physical properties of the top left and middle of the window (an average of 2,053 m/s). This study have showed that extensive physical damage was founded to the left and middle rather than the right side. In this respect, more research in needed to conserve the correlation between color and physical properties.