Various compositions of CoFeNi alloys have been electrodeposited in chloride bath and in sulfate bath, and evaluated for electrodeposition characteristics and magnetic properties. For electrodeposited CoFeNi thin film alloys, the increase of Fe content in the deposits from sulfate bath was considerably faster than those from chloride bath. The current efficiencies in sulfate bath showed observable decrease from $75\%\;to\;50\%$ while those in chloride bath showed no significant decrease. From the low coercivity of 3 Oe in the minimum and the higher squarenesses of the alloys from sulfate bath than those from chloride bath, the alloy at Co, Fe, and Ni contents of $80wt.\%,\;10wt.\%,\;and\;10wt.\%$ can be considered to be the best CoFeNi alloy in this research for the soft magnetic material.

• Journal of Industrial Technology
• /
• v.21 no.A
• /
• pp.221-229
• /
• 2001

The effect of Mo underlayer on the magnetic properties of CoCrTa/Cr films deposited on glass substrates were investigated. The coercivity increased and the coercivity squareness decreased by introducing Mo underlayer. The coercivity increase was attributed to the increase of in-plane c-axis orientation and magnetic isolation of Co grains deposited on Cr/Mo underlayer. The decrease of coercivity squarenesses seemed to be caused by the increase of magnetic isolation. The increase of magnetic isolation of Co grains was attributed to the diffusion of Mo atoms into grain boundaries of Co films and the physical isolation of Co grains. The coercivity of CoCrTa/Cr/Mo showed maximum values at Mo thickness of $400{\AA}$. The appearance of the maximum coercivity at that thickness was attributed to the development of strong $Co(10{\bar{1}}0)$ and $Co(10{\bar{1}}1)$ preferred orientation.

• Journal of the Korean Magnetics Society
• /
• v.4 no.3
• /
• pp.263-271
• /
• 1994

We have produced $Co_{1-x}Pt_{x}(X\;=\;0.53\;and\;0.75)$ alloy films by DC magnetron sputtering at various substrate temperatures and sputtering pressures. Sputter-deposited Co-Pt alloy films showed a strong (111) texture, and the degree of (111) texture of the as-deposited film was found to depend on the substrate temperature and Ar pressure. However, we observed that the degree of (111) texture did not affect the magnetic properties. In addition, we have investigated the effect of heat-treatment on magnetic properties of these films. While the magnetic properties of the $Co_{0.25}Pt_{0.75}$ alloy films showed no noticeable changes, the coercivities and the squarenesses of the $Co_{0.47}Pt_{0.53}$ alloy films were drastically increased by annealing. Structural analysis using transmission electron microscopy(TEM) and x-ray diffractornetry(XRD) revealed that $CoPt(L1_{0})$ and $CoPt_3(L1_{2})$ ordered phases, respectively, were formed, each with a strong (111) texture. By comparing the magnetic properties between $CoPt(L1_{0})$ and $CoPt_3(L1_{2})$ ordered phases in relation to the atomic arrangements in a unit cell, we conclude that the magnetic anisotropy in the Co-Pt alloy system depends mainly on the atomic arrangements of Co and Pt.