• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.97-106
• /
• 2000

In these respects the purpose of this research is manufacturing Co-W-P alloy thin film on the corning glass 2948 by electroless plating method using $NaH_2PO_2H_2O$ (sodium hypophosphite) as a reductant, and analyzing deposition rate, alloy composition, microstructure, and magnetic characteristics at various pH's and temperatures. For Co-P alloy thin film, the reductive deposition reaction occurred only in basic condition, not in acidic condition. The deposition rate increased as the pH and temperature increased, and the optimum condition was found at the pH of 10 and the temperature of 8$0^{\circ}C$. Also magnetic characteristics was found to be most excellent at the pH of 9 and the temperature of 7$0^{\circ}C$, resulting in the coercive force of 870Oe and the squareness of 0.78. At this condition, the contents of P was 2.54% and the thickness of the film was 0.216$\mu\textrm{m}$. For crystal orientation, we could not observe fcc for $\beta$-Co. On the other hand, (1010), (0002), (1011) orientation of hcp for $\alpha$-Co was observed. We could confirm the formation of longitudinal magnetization from dominant (1010) and (1011) orientation of Co-P alloy. For Co-W-P alloy thin film, coercive force was 500Oe and squareness was 0.6. For crystal orientation, (0002) orientation of $\alpha$-Co was dominatly found. Then we could confirm the formation of perpendicular magnetization. The content of P was constant at 0.8$\pm$0.2% and the content of W increased as the concentration of Na$_2$WO$_4$increased. When the concentration of Na$_2$WO$_4$was 0.1mol/L, the composition of W was 20%. We observed the changes of magnetic characteristics and microstructure of thin film depositions of Co-W-P by the heat treatment. For heat treatment, the temperature was increased step by step to 10$0^{\circ}C$, 20$0^{\circ}C$, 30$0^{\circ}C$, and 40$0^{\circ}C$ and it took 1 hour at each step in the reductive condition of hydrogen gas. By the heat treatment, flatness of surface was improved, but there were no changes on the magnetic characteristics and the microstructures.