• 자원리싸이클링
• /
• 제18권3호
• /
• pp.3-10
• /
• 2009

무기성 산업폐기물을 이용한 $CO_2$ 고형화 연구는 폐콘크리트 시멘트 미분말 등 무기성 산업폐부산물의 성분 중의 CaO 또는 MgO 성분과 지구온난화의 주범인 $CO_2$와 반응시켜 탄소를 안정적으로 고형화시켜 대기 중의 $CO_2$의 발생을 저감시키는 연구이다. 본 고에서는 산업 현장 및 도시에서 발생되는 $CO_2$의 대기 방출을 저감시킴과 동시에 산업폐부산물의 유효 자원화를 위한 $CO_2$ 고형화 연구의 국내외 기술 동향을 파악하고, 이를 통해 한국형 $CO_2$ 저감 및 활용 기술을 제시하고자 한다.

• Geomechanics and Engineering
• /
• 제32권3호
• /
• pp.347-359
• /
• 2023

With the development of infrastructure, there is a critical shortage of filling materials all over the word. However, a large amount of silt accumulated in the lower reaches of the Yellow River is treated as waste every year, which will cause environmental pollution and waste of resources. Microbial induced calcium carbonate precipitation (MICP) technology, with the advantage of efficient, economical and environmentally friendly protection, is selected to solidify the abandoned Yellow River silt with poor mechanical properties into high-quality filling material in this paper. Based on unconfined compressive strength (UCS) test, determination of calcium carbonate (CaCO₃) content and scanning electron microscope (SEM) test, the effects of cementation solution concentration, treatment times and relative density on the solidification effect were studied. The results show that the loose silt particles can be effectively solidified together into filling material with excellent mechanical properties through MICP technology. The concentration of cementation solution have a significant impact on the solidification effect, and the reasonable concentration of cementation solution is 1.5 mol/L. With the increase of treatment times, the pores in the soil are filled with CaCO₃, and the UCS of the specimens after 10 times of treatment can reach 2.5 MPa with a relatively high CaCO₃ content of 26%. With the improvement of treatment degree, the influence of relative density on the UCS increases gradually. Microscopic analysis revealed that after MICP reinforcement, CaCO₃ adhered to the surface of soil particles and cemented with each other to form a dense structure.

• 한국주조공학회지
• /
• 제9권3호
• /
• pp.221-227
• /
• 1989

The effect of sulfur content and inoculant on solidification microstructure and mechanical properties of gray cast iron have been investigated. The main results obtained are as follows, 1. In the FeSi3Ca1Ba inoculated irons, with the variation of sulfur content, low sulfur levels (${\sim}0.03%$) yield low chill depth, high tensile strength, good wear resistance and type A graphite with a pearlite matrix. High sulfur levels( >0.08%) provide high chill depth, low mechanical proper ties and type D graphite with small amount ferrite. 2. In case of inoculant variation with normal FeSi, FeSi3Ca1Ba, 30CaSi and uninoculation at 0.03%S level, lower chill depth and higher tensile strength was obtained in the order ; 30CaSi, FeSi3Ca1Ba normal FeSi, uninoculation.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2001년도 The 6th International Symposium of East Asian Resources Recycling Technology
• /
• pp.586-591
• /
• 2001

This research investigated the feasibility of the accelerated carbonation of cement waste forms with carbon dioxide in a supercritical state. Hydraulic cement has been used as a main solidification matrix for the immobilization of radioactive and/or hazardous wastes. As a result of the hydration reaction for major compounds of portland cement, portlandite (Ca(OH)$_2$) is present in the hydrated cement waste form. The chemical durability of a cement form is expected to increase by converting portlandite to the less soluble calcite (CaCO$_3$). For a faster reaction of portlandite with carbon dioxide, SCCD (supercritical carbon dioxide) rather than gaseous $CO_2$, in ambient pressure is used. The cement forms fabricated with an addition of slated lime or Na-bentonite were cured under ambient conditions for 28days and then treated with SCCD in an autoclave maintained at 34$^{\circ}C$ and 80atm. After SCCD treatment, the physicochemical properties of cement matrices were analyzed to evaluate the effectiveness of accelerated carbonation reaction. Conversion of parts of portlandite to calcite by the carbonation reaction with SCCD was verified by XRD (X-ray diffraction) analysis and the composition of portlandite and calcite was estimated using thermogravimetric (TG) data. After SCCD treatment, tile cement density slightly increased by about 1.5% regardless of the SCCD treatment time. The leaching behavior of cement, tested in accordance with an ISO leach test method at 7$0^{\circ}C$ for over 300 days, showed a proportional relationship to the square root of the leaching time, so the major leaching mechanism of cement matrix was diffusion controlled. The cumulative fraction leached (CFL) of calcium decreased by more than 50% after SCCD treatment. It might be concluded that the enhancement of the characteristics of a cement matrix by an accelerated carbonation reaction with SCCD is possible to some extent.

• Environmental Engineering Research
• /
• 제11권1호
• /
• pp.54-61
• /
• 2006

An electron probe microanalysis (EPMA) investigation can provide quantitative and qualitative insight into the nature of the surface and bulk chemistry on solidified waste forms(SWF). The proportion of Pb in grain areas is below 0.3 wt. %, and the proportion near the border of the grain slightly increases to 0.98 wt. % but in the inter-particle areas farther from the grain, the concentration of Pb markedly increases. It is apparent that very little Pb diffuses into the tricalcium silicate($C_3S$) particles and most of the Pb exists as precipitates of sulfate, hydroxide, and carbonate in the cavity areas between $C_3S$ grains. Calcite additions on Pb-doped SWF are also observed to induce deeper incorporation of lead into the cement grains with EPMA line-analysis of cross-sections of cement grains. The line-analysis reveals the presence of $0.2{\sim}5$ weight % Pb over $5\;{\mu}m$ from cement grain boundaries. In the inter-particle areas, the ratio of Ca, Si, Al and S to Pb is relatively similar even at some distance from the grain border and the Pb (wt. %) ratio is reasonably constant throughout the whole inter-particles area. It is apparent that the enhanced development of C-S-H on addition of calcite can increasingly absorbs lead species within the silica matrix.

• 한국농공학회논문집
• /
• 제56권6호
• /
• pp.169-176
• /
• 2014

To evaluate bio-cementation of microbial on sands, laboratory test was conducted using acrylic cubic molding boxes ($5cm{\times}5cm{\times}5cm$). It was incubated the microbial, called Bacillus Pasteurii, according to Park et al (2011, 2012). and applied 50ml each specimen. Two type of sand samples used were Jumoonjin sand and common sand (well graded). These sands were molded in acrylic boxes with the relative density of 30 % and 60 % respectively. Microbial were poured onto the samples molded in acrylic boxes and cured at the room temperature and humidity. After 7, 14 and 21days, it was measured the compressive strength, pH, EC, and density and it were observed SEM and XRD to verify the effect of bio-cementation. It was found that bio-cementation was increased a strength of sands and it was appeared that strengths were related to the type of sand and relative density. Therefore it was confirmed the solidification of sands using the bio-cementation by microbial activation and the usefullness of acrylic molding boxes when tests were conducted on the soil of sands.