• 한국태양에너지학회:학술대회논문집
• /
• 한국태양에너지학회 2011년도 추계학술발표대회 논문집
• /
• pp.177-186
• /
• 2011

We can expect reduction of the sunlight absorption quantity to a structure and an earth surface, a decline of the surface temperature and a decline of the heat transport volume in what there is a method I give the sunlight reflectance in the aspect to the surface of the building by painting sunlight high reflectance paint, and to reduce the sunlight absorption quantity to a structure and an earth surface and does so, and, in addition, a method high water retentivity of tree planting and the road surface of the city space uses evaporation latent heat of the water by making it, and to restrain a rise in temperature is thought about. and It is thought that I reduce the sunlight absorption quantity to not only the structure but also other structures and attention gathers to the reflexive reflector reflecting in the direction again and it is wide as a marker of a board and the clothing of the traffic sign and is used the incidence energy from a source of light for this reflexive reflector now by there is it and devises surface structure again, and controlling reflection directivity for the sunlight for the purpose of raising night visibility.

• 한국재료학회지
• /
• 제22권10호
• /
• pp.531-538
• /
• 2012

Hollow silica spheres were prepared by spray drying of precursor solution of colloidal silica. The precursor solution is composed of 10-20 nm colloidal silica dispersed in a water or ethanol-water mixture solvent with additives of tris hydroxymethyl aminomethane. The effect of pH and concentrations of the precursor and additives on the formation of hollow sphere particles was studied. The spray drying process parameters of the precursor feeding rate, inlet temperature, and gas flow rate are controlled to produce the hollow spherical silica. The mixed solvent of ethanol and water was preferred because it improved the hollowness of the spheres better than plain water did. It was possible to obtain hollow silica from high concentration of 14.3 wt% silica precursor with pH 3. The thermal conductivity and total solar reflectivity of the hollow silica sample was measured and compared with those values of other commercial insulating fillers of glass beads and $TiO_2$ for applications of insulating paint, in which the glass beads are representative of the low thermal conductive fillers and the $TiO_2$ is representative of infrared reflective fillers. The thermal conductivity of hollow silica was comparable to that of the glass beads and the total solar reflectivity was higher than that of $TiO_2$.

• 공업화학
• /
• 제31권1호
• /
• pp.43-48
• /
• 2020

본 연구에서는 침전과 수열처리에 의해 나노입방체와 나노막대구조를 갖는 Fe₂O₃ 나노입자를 합성하였다. Fe₂O₃ 나노 입자 표면에 TiO₂가 20 nm 두께로 코팅된 Fe₂O₃/TiO₂ core-shell (CS) 복합재료를 합성하였다. Fe₂O₃/TiO₂ CS를 화학적 에칭과 열처리에 의해 Fe₂O₃/TiO₂ CS에서 Fe₂O₃/TiO₂ yolk-shell (YS) 형태의 복합재료를 제조하였다. FE-SEM, HR-TEM, XRD 분석을 통하여 Fe₂O₃와 Fe₂O₃/TiO₂ CS 및 Fe₂O₃/TiO₂ YS 안료의 물리적 특성을 측정하였다. 안료를 poly acrylate (PA) 수지에 혼합한 도료들의 일사반사율과 색상변화는 UV-Vis-NIR 분석으로 차열 온도는 실험실에서 제작한 차열 온도 측정기를 통해 측정하였다. Fe₂O₃/TiO₂ YS 적색 안료를 사용한 PA 도료는 우수한 근적외선 반사율을 보였으며, Fe₂O₃ 안료를 사용한 도료에 비해 차열 온도가 13 ℃ 감소하였다.

• 공업화학
• /
• 제27권1호
• /
• pp.16-20
• /
• 2016

본 연구에서는 $TiO_2$/마이카 혼성 복합 재료의 합성과 적외선 반사 특성에 관한 연구를 수행하였다. 마이카 입자의 존재 하에 아세트산 수용액에서 titanium isopropoxide의 가수 분해 반응과 축합 반응에 의해 $TiO_2$/마이카 복합 재료를 합성하였다. $TiO_2$/마이카 복합 재료의 열처리($600{\sim}1000^{\circ}C$, 1~3 h)에 의해 마이카 표면에 형성된 비결정성 상의 $TiO_2$은 anatase 상을 거쳐 결정성 rutile 상으로 전환되었으며 열처리 조건에 의해 결정의 크기가 제어되었다. FE-SEM 분석, ED-XRF 분석, XRPD 분석을 통하여 마이카와 $TiO_2$/마이카 복합 재료의 물리화학적 특성을 규명하였다. 확산 반사-근적외선 분광 분석을 통하여 측정한 $TiO_2$/마이카 혼성 복합 재료의 근적외선 범위(780~2,500 nm)에서의 일사 반사율은 88.6%로, 순수한 소성 마이카의 86.6%보다 다소 높았다. 따라서 $TiO_2$/마이카 혼성 복합 재료는 높은 광반사율을 나타내는 차열 도료의 안료로 사용할 수 있을 것이다.