• 한국응용과학기술학회지
• /
• 제34권3호
• /
• pp.650-656
• /
• 2017

The water-swollen hydrogels containing silicone or fluorine were prepared by copolymerization of 2-hydroxy ethyl methacylate (HEMA) with 3-(trimethoxysilyl)propyl methacrylate(SM) or 2,2,2-trifluoroethyl acrylate(FA). When the content of SM or FA increased in copolymers, there was tendency of water absorbance to decrease, whereas contact angles to increase. The hydrogels containing FA showed 2 ~ 4% higher water content and 4 ~ 5% lower contact angles compared to that of SM. Tensile strengths decreased as the content of SM increased. However, FA exhibited strength of $2.2Mpa/cm^2$ which is similar to $2.3Mpa/cm^2$ of B. FA, which implies comparatively low adherence, hence, showed better protein resistance properties than SM-based hydrogel. The photo-polymerization was also applied instead of thermal polymerization to enhance the energy efficiency. As a result, the reaction yield reached over 95% within 1 minute.

• 대한화장품학회지
• /
• 제32권1호
• /
• pp.45-51
• /
• 2006

화장품에서 색조 화장품 분야에서 분체의 함유율이 높은 투웨이케익, 팩트, 페이스파우더와 같은 파우더류 제품은 함유되는 분체의 물성이 품질에 큰 영향 인자로 작용하기 때문에 분체의 복합화, 금속비누 처리, 아미노산처리, 실리콘처리, 불소 처리등을 통한 품질 향상을 목적으로 표면처리가 시도되어 왔다. 위와 같은 파우더류 제품중에 투웨이케익은 커버력이 가장 요구되는 제품으로서 부착성이나 퍼짐성과 같은 부가품질의 동시 구현이 다른 파우더류 제품보다 어려우며, 화장을 두껍게 느끼거나 답답하다는 사용자들의 잠재불만도 존재하는 제품군이다. 본 연구는 투웨이케익 제품의 중요품질인 부착성과 퍼짐성을 향상시키고, 친화성을 충분히 고려한 새로운 표면처리 방법으로서 피부성분과 구조를 모사하여, 스킨케어에 주로 사용하는 성분들로 나노베시클을 제조하여 그 구조를 파괴하지 않은 상태로 표면 처리하는 방법에 대한 것이다. 분체를 제조하기 위해 먼저, 레시친, 세라마이드, 초산토코페롤, 부틸렌글리롤을 사용하여 고압.유화로 나노유화물을 제조하였고, 이것을 수상에 분산된 체질안료 분산액에 투입, 2가 금속염 용액을 투입한 후, 여과, 건조과정을 통해 나노베시클이 피복된 새로운 기능의 분체를 얻었다. 피복되는 공정에서는 금속염의 농도에 따라 피복량이 결정됨을 확인하였고, 피복된 파우더의 물성에서는 현재 주로 사용하는 실리콘 처리체질안료에 비해 본 연구를 통해 제조된 파우더의 마찰계수가 낮았으며, 외력에 의한 부착성 평가에서도 파우더의 이탈량이 적은 결과를 나타내었다. 또한 이를 함유한 투웨이케익과 함유하지 않은 투웨이케익의 평가에서도 같은 경향의 결과를 나타내었다.