• Design & Manufacturing
• /
• v.7 no.1
• /
• pp.45-49
• /
• 2013

Since the shell-molds are used to make casting the metal parts for the automobile industry, the quality may well be inconsistent with the lower productivity, increasing the cost of the end products. The primary elbow design shell molded steel castings being produced through extrusion process has $180^{\varnothing}$ O.D., $150^{\varnothing}$ I.D., 14mm thickness and 400mm length, while being processed onto the left side of the tubing. The primary cause for the poor processing is the uneven manual shell molding. If the manual shell molds should be produced to have even quality, they would not be processed for tube linking. The purpose of this study was to develop the flask-molds for manufacturing of the shell molds to ensure mass-production, consistent quality, ommission of processing and comfortable working environment. For this purpose, four flask-molds were produced and thereby, four shell molds were assembled. In particular, the shell molds for processing were formed of the fine coated sand to be blown. As a result, productivity increased about three times, while a consistent quality was ensured. Furthermore, the tubes could be linked with each other without being processed, while pallets could be stacked, stored, transported and managed more easily. In a nut-shell, the molding theory could be applied more effectively. However, it is conceived that this study should be followed up by future studies which will research into reliability and endurability of the end products.

• Journal of Conservation Science
• /
• v.30 no.3
• /
• pp.263-275
• /
• 2014

It's shown how to proceed the study on Manufacturing techniques & Conservation to the Iron Pot from Cheonmachong Ancient Tomb(the 155th Tomb in Hwangnam-dong). In order to investigate manufacturing techniques of the Iron Pot, some parts of the relic were gathered. After mounting, polishing and etching on the relic, analyzing the metal microstructure was conducted. Also it's conducted a SEM-EDS analysis on the nonmetallic inclusion. White iron structure was observed in the metallurgical structure inspection, SEM-EDS analysis. It seems to be dried slowly at room temperature after casting, doesn't look as particular heat treatment to improve brittleness. It is estimated that it's as the handle seam side were verified about 3cm inch wide, 1.5 thick in center of body, so 2 separate half-completed products was cast with width-type mould. The manufacturing techniques Using white cast iron structure, width-type mould are observable to the Iron Pot excavated from Sikrichong Ancient Tomb & Hwangnamdaechong grand Ancient Tomb around those were constructed the same time. It's able to recognize that it's almost identical manufacturing techniques at that time. Conservation is generically following those are survey of pretreatment, foreign material removal, stabilization, restoration and color matching in the order. cleaning & drying were added to the process as occasion demands. The strengthening treatment were difficult with artifact's volume, low concentration Paraloid NAD-10 solution was spread two or three times with a brush, surface hardening also came up with 15wt% Paraloid NAD-10 solution after the conservation was complete. There were connection & restoration for the restoration to the damage after modeling forms that it's similar to damaged parts by using the Fiber Reinforced Plastic resins(POLYCOAT FH-245, mold laminated type). Throughout this research, capitalizing on accumulations of measurements about the production technique of Iron Pot in the time of the fifth and 6th centuries is no less important than the Iron artifact's conservation for a better study in the future.