• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.119-124
• /
• 1999

Silicon nitride ceramics with highly oriented microstructure were prepared by tape casting a slurry containing 5 wt% of the silicon nitride whiskers. The whiskers were aligned in the casting direction and worked as seeds for the grain growth. The anisotropy was observed from the sintering shrinkage, Vickers indentation crack lengths, and XRD patterns. The cracks were much longer on the surface normal to the aligned grains than on the tape casting surface where the lateral cracks were also observed. The effect of sintering additives and the annealing treatment on the indentation crack length was examined. The sample with higher silica content had longer cracks than the one with lower silica content. The crack length anisotropy increased after annealing at 2123K.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.4
• /
• pp.141-148
• /
• 2005

The nonlinear humidity distribution occurs due to the moisture diffusion when a concrete is exposed to an ambient air. This nonlinear humidity distribution induces shrinkage cracks on surfaces of the concrete. Because shrinkage cracks largely affect the durability and serviceability of concrete structures, the moisture diffusion in concrete must be investigated. The purpose of this paper is to propose a model of the moisture diffusion coefficient that governs moisture diffusion within concrete structures. To propose the model, numerical analysis was performed with several experiments. Because the moisture diffusion coefficient is changed with aging, especially at early ages, the proposed model includes aging effect by terms of the porosity as well as the humidity of concrete.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.7
• /
• pp.3-10
• /
• 2018

Steel fiber reinforced concrete can improve the resistance to cracking by adding steel fibers when mixing concrete. It can reduce the temperature and shrinkage cracks, and its flexural performance can be improved by increasing the effective moment of inertia. In this study, the deck-plate was used to replace the concrete form and reinforcing bars, and the steel fiber reinforced concrete was used to control the shrinkage and temperature cracks, and improve the flexural performance of the slab. Total 9 slab specimens were tested for analyzing the structural performance and serviceability. As a results, flexural capacity of the slab with deck-plate was evaluated to be superior to that of the normal reinforced concrete slab specimens with the same tensile reinforcement. The steel fiber reinforced concrete was found to have about 8% flexural capacity increase depending on the steel fiber content $15.7kg/m^3$. Also, in terms of flexural stiffness, the specimens using steel fiber reinforced concrete for the same parameters were evaluated to have a stiffness increase of about 30% compared with the case of using ordinary concrete. Especially, it was found that the stiffness of the test results was significantly higher than the analytical result because the increase of the tensile strength of the steel fiber reinforced concrete is not reflected in the current structural code.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.10
• /
• pp.163-170
• /
• 2019

In spite of various advantages, steel fiber reinforced concrete is still limited in its use due to the insufficient research results on the structural performance and design criteria. This study evaluated the long-term behavior of the steel fiber reinforced concrete slabs by long-term loading experiments based on the short-term load bearing capacity of steel fiber reinforced concrete slabs obtained from previous studies. In this study, long-term loading experiments were carried out on Total four 2-span continuous slab specimens were tested for examining the long-term behavior of steel fiber reinforced concrete members. Long-term behavior characteristics of members were evaluated by measuring the long-term deflection, drying shrinkage, the number and width of cracks. Experimental results showed that the instant deflection of the steel fiber reinforced concrete slab is about 50% of the normal reinforced concrete slab. And, it was analyzed that the long-term deflection of the specimen using steel fiber reinforced concrete was about 10~20% lower than that of normal concrete by the long-term deflection over 100 days. In addition, the slab specimen using steel fiber reinforced concrete was evaluated to have just 70% of the number and width of cracks compared with normal concrete specimens.

• Journal of the Korean Ceramic Society
• /
• v.45 no.8
• /
• pp.443-452
• /
• 2008

Shrinkage crack is a major concern for cement materials, especially for flat structures such as Korean On-Dol floor system, flooring for garages, and wall. One of the methods to reduce the adverse effects of shrinkage cracking is to reinforce cement materials with shot randomly distributed fibers. The efficiency of inorganic fibrous material to arresting cracks in cementitious composites was studied. Cement materials reinforced with five different qualities of inorganic fibrous material were tested. Contents of inorganic fibrous material were 1.0 kg, 1.5 kg, 2.0 kg, 2.5 kg, 3.0 kg by weight of cement mortar and C : S types of cement mortar were 1:3 and 1:4. W/C were 60% and 80%. Cement mortar of inorganic fibrous material reinforcement showed an ability to reduce the crack width and crack length significantly as compared to unreinforced cement mortar. $40%{\sim}60%$ drop in shrinkage crack of 1:4 cement mortar with 1.5 kg over was observed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.677-680
• /
• 2008

The autogenous shrinkage of HPC is important in that it can lead the early cracks in concrete structures. The purpose of the present study is to explore the autogenous shrinkage of HPC with cellulose fiber and expansive additive and to derive a realistic equation to estimate the autogenous shrinkage model of that. For this purpose, comprehensive experimental program has been set up to observe the autogenous shrinkage for various test series. Major test variables were the quantity of expansive additive and cellulose fiber. Water-cement ratio is fixed with 13%. The autogenous shrinkage of HPC is found to decrease with increasing expansive additive and cellulose fiber. A prediction equation to estimate the autogenous shrinkage of HPC was derived and proposed in this study. The proposed equation shows reasonably good correlation with test data on autogenous shrinkage of HPC.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.1
• /
• pp.31-37
• /
• 2017

The use of half PC slab has been increasing to shorten construction period. Because the drying shrinkage of topping concrete is restrained by PC slab, the tensile stress is generated at the topping concrete and the cracks can be occurred at the topping concrete due to drying shrinkage. Therefore, it is important to predict the tensile strain of half PC slab due to drying shrinkage to improve the quality of half PC slab. However, there is no studies on prediction of shrinkage behavior of half PC slab yet. Therefore, in this study, half PC slab was made, and the predictability of tensile strain generated at half PC slab due to drying shrinkage was investigated. The step by step method considering creep was used to estimate the tensile strain of half PC slab. In result, good agreement was obtained between the analytical and experimental values.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.125-126
• /
• 2021

In order to improve the housing culture, construction changes for the utilization of diverse and multifunctional spaces are appearing in response to the increasing diverse needs of consumers. Cellular Light-weight Concrete (CLC) is being developed for use in fire-resistant heat-insulating walls and non-bearing walls. However, manufacturing non-uniformity has become a problem as a drawback due to the use of foamed bubbles and normal temperature curing, and additional research is required. Therefore, in order to suppress cracks due to drying shrinkage, silica sand is mixed with CLC to try to understand its characteristics. In the experiment, the compressive strength from 7 to 28 days of age was measured via a constant temperature and humidity chamber, and the drying shrinkage was analyzed according to each condition using a strain gauge. The compressive strength of matrix tends to decrease as the substitution rate of silica sand increases. This is judged by the result derived from the fact that the specific surface area of silica sand is smaller than that of slag. Based on KS F 2701 (ALC block), the compressive strength of 0.6 products is 4.9 MPa or more as a guide, so the maximum replacement rate of silica sand that satisfies this can be seen at 60%. Looking at the change in drying shrinkage for just 7 days, the shrinkage due to temperature change and drying is 0.7 mm, and the possibility of cracking due to shrinkage can be seen, and it seems that continuous improvement and supplementation are needed in the future.

• Journal of the Korea Concrete Institute
• /
• v.13 no.5
• /
• pp.457-465
• /
• 2001

Shrinkage strains of concrete slab in multi-story building are restrained by structural members such as columns or walls, then can induce cracks due to excessive shrinkage stress over tensile strength of member. In this study, a shrinkage stress analysis method of concrete slab in multi-story building considering not only material properties such as shrinkage, creep and reinforcement effect but also construction sequence is proposed. Tensile stresses of slab due to shrinkage are calculated by converting shrinkage strains into equivalent temperature gradients, creep that can release shrinkage stress can be considered by replacing the modulus of elasticity of concrete, Ec , to the effective secant modulus of elasticity of concrete, E$\_$eff/ Reinforcements are also considered by modeling them as equivalent beam elements in FEM program. Results of step by step analysis reflecting construction sequence summed up to calculate stresses of the whole building considering that shrinkage stresses of the building come from the difference of shrinkage between i-th floor and (i-1)-th floor, named as effecitive shrinkage, and it can be varied by construction sequence. The results of 10-story example building show that shrinkage stresses of lower floors are greater than those of upper floors, that is, stresses of lower floors(1∼2FI.) exceed modulus of rupture of concrete, but stress ratios of higher floors are in the range of 27.9∼92.8%.

• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.295-301
• /
• 2011

Recently, the use of UHPC made of superplasticizers, silica fume, and steel fibers has been increasing worldwide. Although UHPC has a very high strength as well as an excellent durability performance due to its dense microstructures, earlyage cracks may occur due to the high heat of hydration and autogenous shrinkage caused by low W/B and high unit cement content. The early-age shrinkage cracking of UHPC can be controlled by using the shrinkage reducers and expansive admixtures having autogenous shrinkage compensation effect. In this paper, ultrasonic pulse velocity of UHPC containing shrinkage reducers and expansive agents was measured to predict its stiffness change. Also, the effect of shrinkage reducers and expansive agents on the autogenous shinkage of UHPC was investigated through the shrinkage test of UHPC specimens. Furthermore, the material coefficients of autogenous shrinkage prediction model were determined using the autogenous shrinkage values of UHPC with age. Consequently, the test results showed that, by adding shrinkage reducers and expansive agents, the stiffness of UHPC was rapidly developed at early-ages and the autogenous shrinkage was considerably reduced.