• Journal of the Korean Wood Science and Technology
• /
• v.19 no.1
• /
• pp.31-63
• /
• 1991

It was proved that in conventional kiln drying of disks piling position in the kiln exerted a great influence on drying rates, and the larger the variation of disk diameter, the more undulating drying rates of disks. While in vacuum drying disks there was no influence on drying rates. By the end-wrapping treatments and the radial direction of disks tangential surface stresses in the core of disks were slightly compressive in three species. In control disks the drying stresses distributed into one step-style that compressive stresses in the pith side of 6cm from pith were larger than those in the bark side, while in the disks end-wrapped with Korean paper the drying stresses distributed uniformly, because flow rates of free water in disks had no difference between heart-and sap-wood by obstruction of evaporating water from surface of disks by end-wrapping with Korean paper. And end-wrapping with Korean paper considerably restrained those. Tangential differential shrinkage stresses developed the maximum tensile stress near the bark and with approaching the pith the stresses gradually reduced and changed into compressive stresses in near the pith. At the end of vacuum drying the maximum tangential tensile stresses of disks end-wrapped with Korean paper were smaller than those of control disks, and critical moisture contents causing the V-shaped crack of disks end-wrapped with Korean paper were lower than those of control disks because of the set by obstruction of evaporating water of end-wrapping with Korean paper. In the experiment of vacuum drying stress distribution the disks end-wrapped with Korean paper or aluminum foil in three species were free from V-shaped cracks and control disks were defected very slightly by V-shaped cracks. And also disks end-wrapped with Korean paper were free from heart checks in Alnus japonica and Juglans sinensis, and heart checks were occurred very slightly in others. Especially, not to speak of disks end-wrapped with Korean paper, vacuum drying of disks end-wrapped with aluminum foil prevented effectively drying defects, moreover drying times could be shortened, that is. Ginkgo biloba, Alnus japonica, and Juglans sinensis disks could be dried from green to in-use moisture content in 110 hours, 272 hours, and 407 hours, respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.17 no.1
• /
• pp.3-11
• /
• 1989

This study was carried out to investigate the physical and mechanical properties. durability of adhesive bond and paint film for the basic data which were required to determine the suitability as a raw material for furniture the laminated veneer lumber (LVL) with pitch pine (Pinus rigida Mill). The results obtained were as follows; 1) The proper pressing time for making the LVL was over 45 second per milimeter of LVL thickness. 2) The bending strength of the LVL was lower than that of the solid wood but the compressive strength of the LVL was similar to that of the solid wood. The strength increased with the decrease of veneer thickness. 3) The impact bending absorbed energy of the LVL was 0 to 0.3 kg.m/$cm^2$ in the direction of parallel to the grain. The energy of the LVL was lower than that of the solid wood (0.68 kg.m/$cm^2$). 4) In warm water soaking and cold-dry tests, delamination of adhered layers surface crack, swelling, and color change were not found when the hot pressing time was over 45 second per milimeter of LVL thickness. As a result of soak under vacuum test shrinkage in the direction of parallel to the grain was about -1.0 percent and. was about 3.0 percent in the direction of the perpendicular to the grain. 6) The film cacks on the LVL's surface after the wet and cold-dry test were not found at all. 7) In the use of the LVL for interior decoration it was considered that the surface of the LVL be overlaid crossly with fancy veneers of birch and paulownia, etc. This cross overlayirg methods have resulted in few cracks on the fancy veneer.