• Journal of the korean academy of Pediatric Dentistry
• /
• v.46 no.3
• /
• pp.274-282
• /
• 2019

The purpose of this study was to evaluate effect of saliva decontamination procedures on microtensile bond strength (MTBS) of 1-step self-etching adhesives to dentin of primary posterior teeth. 63 sound primary-posterior teeth were randomly divided into 3 groups according to different kinds of 1-step self-etching adhesives: $Scotchbond^{TM}$ Universal Adhesive (SBU), All-Bond $Universal^{(R)}$ (ABU), and $Tetric^{(R)}$ N Bond Universal (TBU). Each group was randomly categorized into 7 subgroups: (I) application of adhesive without saliva contamination (control); (II - IV) contamination by saliva before photopolymerization; (V - VII) contamination by saliva after photopolymerization; (II, V) decontamination by drying; (III, VI) decontamination by washing and drying; (IV, VII) decontamination by washing, drying, and reapplication of adhesive. All samples were cut into the blocks. At least 15 blocks were tested for each subgroup. For SBU and ABU, the MTBS values of subgroups (I, IV, VII) were significantly higher than those of subgroups (II, III, V, VI). For TBU, the MTBS values of subgroups (I, IV) was significantly higher than those of subgroup (II, III, V, VI). The MTBS of 3 adhesives was reduced by saliva contamination. The adhesive strength on dentin of primary posterior teeth was restored by reapplication of the adhesives after washing and drying.

• Restorative Dentistry and Endodontics
• /
• v.42 no.1
• /
• pp.1-8
• /
• 2017

Objectives: The purpose of this study was to evaluate the effect of adhesive luting on the fracture resistance of zirconia compared to that of a composite resin and a lithium disilicate glass ceramic. Materials and Methods: The specimens (dimension: $2mm{\times}2mm{\times}25mm$) of the composite resin, lithium disilicate glass ceramic, and yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) were prepared. These were then divided into nine groups: three non-luting groups, three non-adhesive luting groups, and three adhesive luting groups, for each restorative material. In the non-luting groups, specimens were placed on the bovine tooth without any luting agents. In the non-adhesive luting groups, only zinc phosphate cement was used for luting the specimen to the bovine tooth. In the adhesive luting groups, specimens were pretreated, and the adhesive luting procedure was performed using a self-adhesive resin cement. For all the groups, a flexural test was performed using universal testing machine, in which the fracture resistance was measured by recording the force at which the specimen was fractured. Results: The fracture resistance after adhesive luting increased by approximately 29% in the case of the composite resin, 26% in the case of the lithium disilicate glass ceramic, and only 2% in the case of Y-TZP as compared to non-adhesive luting. Conclusions: The fracture resistance of Y-TZP did not increased significantly after adhesive luting as compared to that of the composite resin and the lithium disilicate glass ceramic.

• Composites Research
• /
• v.16 no.4
• /
• pp.51-58
• /
• 2003

Since the reliability of adhesively bonded joints is much dependent on the curing status of thermosetting adhesive, the on-line cure monitoring during the cure of adhesively joints could improve the quality of adhesively bonded joints. In this work, the dielectric method which measures the dissipation factor of the adhesive during the cure of joints and converts it into the degree of cure of the adhesive was devised. The relation between the dissipation factor and the degree of cure of adhesive was investigated, which could eliminate the temperature effect on the dissipation factor that is a strong function of the degree of cure and temperature of adhesive. From the investigation, it was found that the dissipation factor showed a trend similar to the cure rate of the adhesive.

• The korean journal of orthodontics
• /
• v.37 no.4
• /
• pp.283-292
• /
• 2007

The purpose of this study was to evaluate the clinical usefulness of 4 self etching primers by measuring the shear bond strength of orthodontic brackets and examining the failure pattern of bracket-tooth interfaces. Methods: Seventy-five, defect-free, premolars were randomly assigned into five groups: control group (37% phosphoric acid + Transbond XT primer) and self etching primer treated groups (Transbond Plus self etching primer, Unifil bond, Clearfil SE bond, and Adhese). The shear bond strength was measured with a universal testing machine and the amount of residual adhesive remaining on the brackets after debonding was assessed by the adhesive remnant index (ARI). Results: The results showed that the groups conditioned with self etching primer had significantly lower shear bond strength than the control group (p < 0.05), although clinically acceptable. However, there were no significant differences in shear bond strength among the self etching primer groups (p > 0.05). Evaluation of the ARI scores indicated there was less resin remnant on the teeth in the groups conditioned with self etching primers, although not statistically significant. Conclusion: The results of this study suggest that all four of the self etching primers have shown acceptable bond strength for clinical use.

• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.106-115
• /
• 2010

The purpose of this study was to evaluate the microtensile bond strength (${\mu}TBS$), failure modes and bonding interfaces of self-etching and three self-adhesive resin cements to dentin and indirect composite resin. Cylindrical composite blocks (Tescera, Bisco Inc.) were luted with resin cements (PA: Panavia F 2.0, Kuraray Medical Inc., RE: RelyX Unicem Clicker, 3M ESPE., MA: Maxem, Kerr Co., BI: BisCem, Bisco Inc.) on the prepared occlusal dentin surfaces of 20 extracted molars. After storage in distilled water for 24 h, $1.0\;mm\;{\times}\;1.0\;mm$ composite-dentin beams were prepared. ${\mu}TBS$ was tested at a cross-head speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and Tukey's HSD test. Dentin sides of all fractured specimens and interfaces of resin cements-dentin or resin cements-composite were examined at FESEM (Field Emission-Scanning Electron Microscope). In conclusion, PA and RE showed higher bond strength and closer adaptation than MA and BI when indirect composite blocks were luted to dentin using a self-etching and three self-adhesive resin cements.

• Restorative Dentistry and Endodontics
• /
• v.40 no.4
• /
• pp.299-305
• /
• 2015

Objectives: The purpose of this study was to investigate the effectiveness of multiple decontamination procedures for salivary contamination after curing of a universal adhesive on dentin bond strength according to its etch modes. Materials and Methods: Forty-two extracted bovine incisors were trimmed by exposing the labial dentin surfaces and embedded in cylindrical molds. A universal adhesive (All-Bond Universal, Bisco) was used. The teeth were randomly divided into groups according to etch mode and decontamination procedure. The adhesive was applied according to the manufacturer's instructions for a given etch mode. With the exception of the control groups, the cured adhesive was contaminated with saliva for 20 sec. In the self-etch group, the teeth were divided into three groups: control, decontamination with rinsing and drying, and decontamination with rinsing, drying, and adhesive. In the etch-and-rinse group, the teeth were divided into four groups: control, decontamination with rinsing and drying, decontamination with rinsing, drying, and adhesive, and decontamination with rinsing, drying, re-etching, and reapplication of adhesive. A composite resin (Filtek Z350XT, 3M ESPE) was used for filling and was cured on the treated surfaces. Shear bond strength was measured, and failure modes were evaluated. The data were subjected to one-way analysis of variation and Tukey's HSD test. Results: The etch-and-rinse subgroup that was decontaminated by rinse, drying, re-etching, and reapplication of adhesive showed a significantly higher bond strength. Conclusions: When salivary contamination occurs after curing of the universal adhesive, additional etching improves the bond strength to dentin.

• The korean journal of orthodontics
• /
• v.34 no.5 s.106
• /
• pp.439-447
• /
• 2004

The purpose of this study was to investigate the influence of water, saliva and blood contamination on the bonding strength of metal brackets with a self-etching primer/adhesive to enamel. Ninety-six extracted human teeth were divided into four groups. The brackets were bonded to enamel with a self- etching primer (3M/Unitek Dental Products. Monorovia California) according to one of four protocols. The teeth were bonded in a dry condition (group D) or in contamination with distilled water (group W), artificial saliva (group S). or fresh human blood (group B) Shear bond strengths were tested using an Instron Universal testing machine. After debonding. bracket and tooth surfaces were examined with a stereomicroscope. In each group, four samples were selected and examined with a Scanning electron microscope of the prepared enamel surface and resin-enamel interlace. The results obtained were summarized as follows: Shear bond Strength if group D $(15.22{\pm}2.86MPa)$ and W $(15.20{\pm}3.85 MPa)$ Were higher than in group B$(12.56{\pm}2.94MPa)$ (p<0.05). There were no statistical differences in the shear bond strengths between groups D. W and S (p>0.05). There was a tendency to have less residual adhesive remaining on the enamel surfaces of group B than group D. The SEW morphology of group D and W showed a more roughened etching pattern than group S and B. Water or saliva contamination on bending of orthodontic brackets with Transbond plus self etching primer had almost no influence on bond strength In this study, the blood contaminated group showed the lowest bond strength, but it was above the clinically acceptable bond strength (5.9-7.8 MPa, Reynold, 1975). The results of this study suggest that acceptable clinical bond strengths can be obtained in wet conditions when self-etching adhesives are used.

• Restorative Dentistry and Endodontics
• /
• v.40 no.1
• /
• pp.30-36
• /
• 2015

Objectives: This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. Materials and Methods: 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resins with extracted human molars stored in saline for 24 hr. Testing was performed using the wire-loop method and a universal testing machine. Bond strength data was statistically analyzed using two way analysis of variance (ANOVA) and Tukey's post hoc test. Results: Two way ANOVA revealed significant differences for the factors of dentin adhesives and composite resins, and significant interaction effect (p < 0.001). All combinations with Xeno V (Dentsply De Trey) and Clearfil $S^3$ Bond (Kuraray Dental) adhesives showed no significant differences in micro-shear bond strength, but other adhesives showed significant differences depending on the composite resin (p < 0.05). Contrary to the other adhesives, Xeno V and BondForce (Tokuyama Dental) had higher bond strengths with the same manufacturer's composite resin than other manufacturer's composite resin. Conclusions: Not all combinations of adhesive and composite resin by same manufacturers failed to show significantly higher bond strengths than mixed manufacturer combinations.

• Restorative Dentistry and Endodontics
• /
• v.28 no.1
• /
• pp.23-33
• /
• 2003

The purpose of this study was to compare in vitro interfacial relationship of restorations bonded with three self-etching primer adhesives and one self-etching adhesive. Class I cavity preparations were prepared on twenty extracted human molars. Prepared teeth were divided into four groups and restored with four adhesives and composites Clearfil SE $Bond/Clearfil^{TM}$ AP-X (SE), UniFil $Bond/UniFil^{\circledR}$ F (UF), FL $Bond/Filtek^{TM}$ Z 250 (FL) and Prompt $L-Pop/Filtek^{TM}$ Z 250 (LP) After storing in distilled water of room temperature for 24 hours, the specimens were vertically sectioned and decalcified. Morphological patterns between the enamel/dentin and adhesives were observed under SEM. The results of this study were as follows : 1. They showed close adaptation between enamel and SE, UF and FL except for LP. 2. The hybrid layer in dentin was $2{\;}\mu\textrm{m}$ thick in SE, $1.5{\;}\mu\textrm{m}$ thick in UF, and $0.4{\;}\mu\textrm{m}$ in both FL and LP. So, the hybrid layers of SE and UF were slightly thicker than that of FL and LP. 3. The lengths and diameters of resin tags in UF and FL were similar, but those of LP were slightly shorter and slenderer than those of SE. 4. The resin tags were long rod shape in SE, and funnel shape in other groups Within the limitations of this study, it was concluded that self-etching primer adhesives showed close adaptation on enamel. In addition, the thickness of hybrid layer ranged from $0.4-1.5{\;}\mu\textrm{m}$ between adhesives and dentin. The resin tags were long rod or funnel shape, and dimension of them was similar or different among adhesives.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.49 no.3
• /
• pp.264-273
• /
• 2022

Due to the development of properties of adhesive materials currently used in dentistry, the bonding ability between the brackets and the tooth enamel has been greatly improved. In general, in situations where cooperation can be obtained, adhesion of the orthodontic bracket through the conventional three-step process can show excellent bonding strength. However, if it is difficult to expect patient cooperation, as in the pediatric dentistry area, or if moisture isolation is not properly performed, the binding strength that does not reach the expected effect. As a result, various products that simplify the process for adhesion are being developed. The aim of this study was to evaluate and compare the shear bonding strength between the conventional 3-step adhesion system, self-etching primer system and one-step adhesion system that reduces the priming process. A total of 60 human maxillary, mandibular premolars were prepared. Group I (control group) were followed conventional 3-step bonding process. Group II were conditioned with self-etching primer. Group III were etched with 37% phosphoric acid and brackets were bonded with self-priming adhesive. The resultant shear bond strength of each group was measured and an adhesive remnant index (ARI) was recorded. The mean shear bond strength of group I, II, III were 14.69 MPa, 11.21 MPa and 12.21 MPa respectively. Significant differences could only be found between group I, II and group I, III (p < 0.05). The ARI indicated no significant difference among all groups.