• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.34-39
• /
• 2002

The surfaces of machine components in sliding contact such as bearing, gears and pistons etc. frequently operate under the condition of mixed lubrication due to high load, high speed and slip. These machine components often undergo the inception of scuffing in practical application. The scuffing failure is a critical problem in modern machine components, especially for the requirement of high efficiency and small size. However, it is difficult to find a universal mechanism to explain all scuffing phenomena because there are so many factors affecting the onset of scuffing. In this study, scuffing experiments are conducted using Acoustic Emission(AE) measurement by an indirect sensing approach to detect scuffing failure. Acoustic Emission(AE) signal has been widely utilized to monitor the interaction at the friction interface. Using AE signals we can get an indication about the state of the friction processes, about the quality of solid and liquid layers eon the contacting surfaces in real time. The FFT(Fast Fourier Transform)analyses of the AE signal are used to understand the interfacial interaction and the relationship between the AE signal and the state of contact is presented

• Tribology and Lubricants
• /
• 제18권5호
• /
• pp.351-356
• /
• 2002

The surfaces of machine components in sliding contact such as bearing, gears and pistons etc. frequently operate under the condition of mixed lubrication due to high load, high speed and slip. These machine components often undergo the inception of scuffing in practical application. The scuffing failure is a critical problem in modern machine components, especially for the requirement of high efficiency and small size. However, it is difficult to find a universal mechanism to explain all scuffing phenomena because there are so many factors affecting the onset of scuffing. In this study, scuffing experiments are conducted using Acoustic Emission(AE) measurement by an indirect sensing approach to detect scuffing failure. Acoustic Emission(AE) signal has been widely utilized to monitor the interaction at the friction interface. Using AE signals we can get an indication about the state of the friction processes, about the quality of solid and liquid layers on the contacting surfaces in real time. The FFT(Fast Fourier Transform) analyses of the AE signal are sued to understand the interfacial interaction and the relationship between the AE signal and the state of contact is presented.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제33회 춘계학술대회 개최
• /
• pp.64-71
• /
• 2001

In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The size of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.191-192
• /
• 2002

The scuffing failure is a critical problem in modern machine components, especially for the requirement of high efficiency and small size. In this study. scuffing experiments are conducted using Acoustic Emission(AE) measurement by an indirect sensing approach to detect scuffing failure. Using AE signals we con get and indication about the state of the friction processes, about the quality of solid and liquid layers on the contacting surface in real time. The FFT(Fast Fourier Transform)analyses of the AE signal are used to understand the interfacial interaction and the relationship between the AE signal and the state of contact is presented.

• Journal of Mechanical Science and Technology
• /
• 제16권11호
• /
• pp.1428-1434
• /
• 2002

The ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the effect of initial spacing in surface profiles on wear and scuffing. Three kinds of surface spacing, which are closely related with initial surface micro-cracks on sliding surfaces, were produced on AISI 1045 steel surfaces using different grinding and polishing processes. Frictional forces and time to scuffing were measured, and the shape and amount of wear particles were analyzed to compare the with original surface profiles. From the tests, it was confirmed that the size of wear particles are related closely to the original spacing of the surface profile. The time to failure and amount of wear were sensitive to the surface spacing. The wider surface spacing shows much longer sliding life and smaller amount of wear than the others. Time to scuffing was increased with increasing surface pro(lie spacing. The size of wear particles increased while the wear and wear rate K were decreased with an increase in surface spacing. After the sliding tests, surface cracks of inner parts of the wear track formed due to scuffing were observed and compared among the specimens having the different surface spacing.

• Tribology and Lubricants
• /
• 제17권5호
• /
• pp.399-405
• /
• 2001

In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The sire of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.

• Tribology and Lubricants
• /
• 제21권6호
• /
• pp.263-267
• /
• 2005

The tribological performance of multi-walled carbon nanotubes (MWNT) in mineral oils is investigated at ambient temperature. The frictional forces, wear amounts and cycles to scuffing of the oils with nanotubes and without those were measured using the ball-on-disk tester. It was found that there were little differences in the frictional forces and wear amounts of two oils. However, the scuffing times of oils with nanotubes were much longer than those of oils without nanotubes in sliding tests. The nanotubes were very effective on maintaining the oil gap and protecting the surfaces in boundary lubricated sliding.

• Tribology and Lubricants
• /
• 제8권2호
• /
• pp.14-19
• /
• 1992

rate of growth of "protective" films of oxides and compounds derived from the lubricant. The protection afforded by the films is strongly dependent on lubricant and steel composition, initial composite surface roughness and the load/speed sequence or history in the early stages of sliding. The protective films, formed by chemical and mechanical action between lubricant and mating surfaces, delayed the surface roughening and offered higher load capacity. Given the great number of variables involved it is not possible to follow more than a few of the chemical changes on surfaces at the end of experiments. Ellipsometry was therefore used to monitor the formation and loss of dual protective films in real time, and also to find the effect of protective films on scuffing and break-in depending on lubricant conditions.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.227-228
• /
• 2002

One of the serious challenges in developing rotary compressor with HFC refrigerant is the prediction of scuffing times and wear amounts between vane and roller surface. In this study, the tribological characteristics of sliding surfaces using roller-vane geometry of rotary compressor were investigated. The sliding tests were carried out under various sliding speeds, normal loads and surface roughness. During the tests, friction force, wear scar width, time to failure, surface temperature, and surface roughness were monitored. Because severe wear was occurred on vane surface, TiN coating was applied on sliding surfaces to prolong the wear-life of vane-roller interfaces. From the sliding tests, it was found that there was the optimum initial surface roughness to break in and to prolong the wear life of sliding surfaces. Depending on load and speed, the protective layers, which were composed of metallic oxide and organic compound, were formed on sliding surfaces. Those would play an important role in the amount of friction and wear between roller and vane surfaces.

• 유체기계공업학회:학술대회논문집
• /
• 유체기계공업학회 2002년도 유체기계 연구개발 발표회 논문집
• /
• pp.221-226
• /
• 2002

One of the serious challenges in developing rotary compressor with HFC refrigerant is the prediction of scuffing times and wear amounts between vane and roller surfaces. In this study, the tribological characteristics of sliding surfaces using vane-roller geometry of rotary compressor were investigated. The sliding tests were carried out under various sliding speeds, normal loads and surface roughness. During the test friction force, wear depth, time to failure and surface temperature were monitored. Because severe wear was occurred on vane surface, TiN coating was applied on sliding surfaces to prolong the wear-life of vane-roller interfaces. From the sliding test it was found that there was the optimum initial surface roughness to break in and to prolong the wear life of sliding surfaces. Depending on the load and speed, the protective layers, which were composed of metallic oxide and organic compound, were formed on sliding surfaces. Those would play an important role in role amounts of friction and wear between miler and vane surfaces.