• Elastomers and Composites
• /
• v.35 no.3
• /
• pp.215-226
• /
• 2000

Cure characteristics of carbon black-filled rubber compounds with different rubber composition were studied using a rheometer. The carbon black-filled rubber compounds with single, binary, and ternary rubber compositions of natural rubber (NR), styrene-butadiene rubber (SBR), and butadiene rubber (BR) were used. Delta-torques of the NR/BR- and SBR/BR-based compounds with a high BR content were higher than those of the single rubber-based compounds. For ternary rubber-based compounds, the delta-torques of the compounds were lower when the difference in the rubber content ratios was small than when it was big. Scorch and optimum cure times of the rubber compounds became shorter by increasing the content of NR in the compounds while those became longer by increasing the SBR content. Cure rates of the rubber compounds increased with a decrease of the SBR content in the rubber compounds. Reversion ratios decreased with an increase of the SBR content in the rubber compounds.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2010.09c
• /
• pp.129-134
• /
• 2010

This paper investigates effects of rubber inclusion on the strength and physical characteristics of rubber.added composite geomaterial (CGM) in which dredged soils, crumb rubber, and bottom ash are reused for recycling. Several series of test specimens were prepared at 5 different percentages of rubber content (i.e. 0%, 25%, 50%, 75%, and 100% by weight of the dry dredged soil) and three different percentages of bottom ash content (i.e. 0%, 50% and 100% by weight of the dry dredged soil). The mixed soil specimens were subjected to unconfined compression test and elastic wave test to investigate their unconfined compressive strengths and small strain properties. The values of bulk unit weight of the CGM with bottom ash content of 0% and 100% decrease from 14kN/$m^3$ to 11kN/$m^3$ and 15kN/$m^3$ to 12kN/$m^3$, respectively, as rubber content increases, because the rubber had a specific gravity of 1.13. The test results indicated that the rubber content and bottom ash content were found to influence the strength and stress-strain behavior of CGM. Overall, the unconfined compressive strength, and shear modulus were found to decrease with increasing rubber content. Among the samples tested in this study, those with a lower rubber content exhibited sand-like behavior and a higher shear modulus. Samples with a higher rubber content exhibited rubber-like behavior and a lower shear modulus. The CGM with 100% bottom ash could be used as alternative backfill material better than CGM with 0% bottom ash. The results of elastic wave tests indicate that the higher rubber content, the lower shear modulus (G).

• Elastomers and Composites
• /
• v.36 no.1
• /
• pp.37-43
• /
• 2001

Influence of the filler composition ratio on cure characteristics and bound rubber content of the compounds and on physical properties of the vulcanizates were studied using both silica and carbon black-filled styrene-butadiene rubber (SBR) compounds with the total filler content of 80.0 phr. The bound rubber content increased slightly with increase of the silica content ratio. The viscosity also increased with increasing the silica content ratio, especially increased steeply after the silica content of 60.0 phr. The cure times obtained with a rheometer, t2, t40, and t90, are increased by increasing the silica content ratio and the cure rate decreased. The delta torque increased with the increased silica content ratio. Variation or the modulus with the silica content ratio showed a decreased trend though the delta torque increased. The tan ${\delta}$ at $60^{\circ}C$ decreased with increased of the silica content ratio.

• Applied Chemistry for Engineering
• /
• v.5 no.5
• /
• pp.878-888
• /
• 1994

In order to investigate the fracture behavior of ABS terpolymer under the tension and impact load, varing the content of rubber, molecular weight of SAN, content and kinds of lubricant, tension speed, the mechanical properties were measured and SEM pictures of fracture area were taken. Under the tension, the tensile strength increased as rubber content and lubricant content decreased, while molecular weight and tension speed increased. The deformation of area near fracture site did not occur as rubber content, tension speed and molecular weight decreased and liquid lubricant was used. And in the shape of fracture seemed phase seperation. Under the impact load, the notched izod impact strength increased as rubber content, molecular weight, ambient temperature and lubricant content increased. In the SEM picture, the strength was high white the fracture surface was small.

• Elastomers and Composites
• /
• v.53 no.2
• /
• pp.80-85
• /
• 2018

Chloro isobutylene isoprene rubber (CIIR) and ethylene propylene diene monomer (EPDM) compounded with other formulation chemicals, depending on the polymer blend, were prepared by mechanical mixing. After manufacturing the rubber vulcanizate by compression molding with a hot press, the mechanical and thermal properties including thermal conductivity, rebound resilience of the CIIR/EPDM blends were measured. As the EPDM rubber content increased, hardness and tension set showed a tendency to increase. Pure CIIR exhibited the lowest tensile strength; however, tensile strength increased with loading of EPDM rubber. On the other hand, in CIIR rubber, which is usually a low-rebound elastomer owing to a high damping effect, rebound resilience exhibited an increasing trend as the content of EPDM rubber increased. As the EPDM rubber content increased, thermal stability was improved due to reduction of decomposition rate in the rubber region of the blend vulcanizate.

• Elastomers and Composites
• /
• v.53 no.3
• /
• pp.168-174
• /
• 2018

Natural rubber (NR) and bromo-isobutylene-isoprene rubber (BIIR) were compounded with other formulation chemicals through polymer blending via a mechanical mixing method. After rubber vulcanization by hot-press compression molding, the cure characteristics, mechanical properties, and ozone resistance of the NR/BIIR blends were measured. As the BIIR content increased, the maximum torque of the blends decreased, while the optimum cure time and scorch time tended to increase. Furthermore, the hardness of the blends increased with increasing BIIR content, reaching the maximum value at 75 wt% BIIR, and decreased with a further increase in the BIIR loading. The tensile strength and elongation at break decreased with an increase in the BIIR content, reaching the minimum value at 75 wt% BIIR, and increased with a further increase in the BIIR content. In the ozone resistance test, cracks were not generated when the BIIR content was more than 75 wt%.

• Elastomers and Composites
• /
• v.52 no.1
• /
• pp.17-21
• /
• 2017

The optimum mixing conditions of silica and silane containing rubber composites were evaluated by investigating the properties of rubber composites prepared with a silica composition of 10, 20, 40, 60, and 80 g, respectively. The crosslinking rate decreased with increasing silica content, with he promoters being adsorbed on the silica surface with in the rubber composite. As a result, the increase in crosslinking time resulted in the destruction of the silica structure. The increase of the bound rubber content due to the destruction of the silica structure inhibited the chain motion of the polymer molecules and reduced the cohesion of the silica itself. Finally, the increase of silica content showed the increase of hardness, tensile strength, and storage modulus of rubber composites.

• Elastomers and Composites
• /
• v.46 no.3
• /
• pp.186-194
• /
• 2011

Natural fiber/natural rubber composites were fabricated by uniformly compounding natural rubber and cellulose- based natural fiber kenaf and then by compression molding. The effect of kenaf fiber content on their vulcanization behavior, hardness, tensile properties, tear strength and static and dynamic properties was investigated. The contents of kenaf fiber in the composites were 0, 5, 10, 15, and 20 phr, compared to natural rubber and additives. The result indicated that various properties of natural rubber depended on the kenaf fiber content. With increasing kenaf fiber content, the torque for vulcanization of natural rubber was increased whereas the vulcanization time was reduced as well. The hardness, tensile modulus and tear strength of kenaf/natural rubber composites were gradually decreased with the fiber content whereas the tensile strength and elongation at break were decreased. Also, with increasing the kenaf fiber content the dynamic property of natural rubber was changed more greatly than the static property. The loss factor, which is closely related with the damping or absorption of the energy given to natural rubber, was proportionally increased with the fiber content.

• Elastomers and Composites
• /
• v.33 no.4
• /
• pp.231-237
• /
• 1998

In order to investigate the physical properties of rubber blend compound, this experiment was carried out on the cure rate, loss tangent, reinforcement and abrasion properties of S-SBR (solution styrene-butadiene rubber) blends containing silane coupled silica and E-SBR (emulsion styrene-butadiene rubber) blends containing carbon black as a model compound. E-SBR blend showed the highest total bound rubber(TBR), while S-SBR blends showed constant TBR level regardless of rubber type. Rapid cure rate was achieved when the styrene and vinyl content of rubber microstructure decreased and TBR content of rubber compounds increased. The modulus as the index of rubber reinforcement showed the linear relation with TBR content. The large amount of PICO loss was observed when the styrene and vinyl content of rubber microstructure increased, while the small amount of PICO loss was observed when the ratio of bu-tadiene increased in the S-SBR blends with silane copuled silica. The high loss tangent at $0^{\circ}C$, the low loss tangent at $60^{\circ}C$, and the large difference of loss tangent were shown in the S-SBR blends with high styrene content compared to E-SBR blend.

• Composites Research
• /
• v.13 no.5
• /
• pp.10-17
• /
• 2000

The fatigue properties of short nylon66 fiber reinforced Chloroprene rubber have been investigated as functions of interphase conditions and fiber content. The spring constant of rubber decreased about 21% after the fatigue test. On the contrary, that of reinforced rubber increased in all cases. The changing rate of spring constant for reinforced rubber decreased with increasing fiber content. This means that the better interphase condition, the smaller changing rate of spring constant. Temperature of matrix increased about 2.5 times and one of reinforced rubber showed 1.7∼2 times up after the test. The changing rate of temperature for reinforced rubber during fatigue test decreased with increasing fiber content. It is found that the better interphase condition, the smaller changing rate of specimen temperature at the same fiber content. Double coatings of bonding agent 402 and rubber solution became the best interphase model in this study. And, we have investigated the possibility of applying short-fiber reinforced rubber to automotive engine mount rubber, bush and stopper.