• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.4
• /
• pp.401-408
• /
• 2009

This study is performed to check the three dimensional characteristics of residual stress in the dissimilar metal weld. Although two dimensional analysis has been widely used for the assessment of weld residual stress, it has limitations to understand the stress distribution of the third direction. 3-D analysis was done to understand residual stress distribution of the welded plate. A simple butt-welded plate was considered to show the stress variation on all direction. A mock-up plate weldment was fabricated with SA-508 and F316L, which are widely used in nuclear power plants. The analysis results were validated with the measured values in the mock-up.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.9
• /
• pp.770-781
• /
• 2008

In nuclear power plants, ferritic low alloy steel components were connected with austenitic stainless steel piping system through alloy 82/182 butt weld. There have been incidents recently where cracking has been observed in the dissimilar metal weld. Alloy 82/182 is susceptible to primary water stress corrosion cracking. Weld-induced residual stress is main factor for crack growth. Therefore exact estimation of residual stress is important for reliable operating. This paper presents residual stress computation performed by 6" safety & relief nozzle. Based on 2 dimensional and 3 dimensional finite element analyses, effect of welding variables on residual stress variation is estimated for sensitivity analysis.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.4 no.4
• /
• pp.25-32
• /
• 1995

This study is to inspect the influence of the initial residual stress on fatigue crack growth behavior after the distribution of the initial residual stress is measured when the crack is growing from the compressive residual stress field. Also, the tensile residual stress field. Also, the influence of the variation of residual stress distribution on fatigue crack growth behavior at the crack tip is studied when the initial crack occurs on weld metal, bead interface and HAZ (Heat Affected Zone), respectively. For this purpose, CT-type specimen that crack parallel to the welding bead were manufactured by butt welding on the Al. Alloy 1100-O plate.

• The Journal of the Acoustical Society of Korea
• /
• v.20 no.5
• /
• pp.48-53
• /
• 2001

In speaker verification based on LPC analysis the prediction residues are ignored and LPCC(LPC cepstrum) are only used to compose feature vectors. In this study, LPCC and RCEP (residual cepstrum) extracted from residues are used as feature parameters in the various environmental speaker verification. We propose the weighting function which can enlarge inter-speaker variation by weighting pitch, speaker inherent vector, included in residual cepstrum. Simulation results show that the average speaker verification rate is improved in the rate of 6％ with RCEP and LPCC at the same time and is improved in the rate of 2.45% with the proposed weighted RCEP and LPCC at the same time compared with no weighting.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.10
• /
• pp.1411-1417
• /
• 2010

CFRP (Carbon Fiber Reinforced Plastic) has received considerable attention in various fields as a structural material, because of its high specific strength, high specific stiffness, excellent design flexibility, favorable chemical properties, etc. Most products consisting of several parts are generally assembled by mechanical joining methods (using rivets, bolts, pins, etc.). Holes must be drilled in the parts to be joined, and the strength of the components subjected to static and fatigue loads caused by stress concentration must be decreased. In this study, we experimentally evaluated the variation in the residual strength of a holenotched CFRP plate subjected to fatigue load. We repeatedly subjected the hole-notched specimen to fatigue load for a certain number of cycles, and then we investigated the residual strength of the hole-notched specimen by performing the fracture test. From the results of the test, we can observe the initiation of a directional crack caused by the applied fatigue load. Further, we observed that the residual strength increases with a decrease in the notch effect due to this crack. It was evaluated that the residual strength increases to a certain level and subsequently decreases. This variation in the residual strength was represented by a simple equation by using a model of the decrease in residual strength for plain plate, which was developed by Reifsnider and a stress redistribution model for hole-notched plate, which was developed by Yip.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.6
• /
• pp.50-56
• /
• 2006

Residual gas fraction in a combustion process is very crucial to improve combustion and cyclic variations. Especially, the residual gas fraction is strongly affected by backflow of the residual gas during the valve overlap period in an idle operation. Therefore, it is one of the most interesting that valve timings can affect flow characteristics of gas exchange process, especially during idle operation. This analysis investigates residual gas fraction with respect to valve timing changes which is critical for combustion efficiency and engine performance. Flow characteristics of residual gas by changing intake and exhaust valve timing are calculated by CFD methodology during an idle operation in an SI engine. It is analyzed that retarded EVO and advanced IVO results in the increase of valve overlap period and consequently, residual gas fraction. Futhermore, changes in IVO have stronger effects on variation of residual gas fraction.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.245-248
• /
• 2005

During manufacturing thick composite cylinders, large thermal residual stresses are developed and induce catastrophic interlaminar failures. Since the residual stresses are dependent on many process parameters, such as temperature distribution during cure, cure shrinkage, winding tension, and migration of fibers, calculation of the residual stresses is very difficult. Therefore a radial-cut method have been used to measure the residual stresses in the composite cylinders. But the conventional radial-cut method needs to know numerous material properties which are not only troublesome to obtain but also vary with change of fiber arrangement during consolidation. In this paper, a new radial-cut method with cut-cylinder-bending test was proposed and the measured residual stresses were compared with calculated thermal residual stresses. It was found that the new radial-cut method which does not need to know any of material properties gave better estimation of residual stresses regardless of radial variation of material properties. Additionally, interlaminar tensile strength could be obtained by the cut-cylinder-bending test.

• Nuclear Engineering and Technology
• /
• v.47 no.1
• /
• pp.115-125
• /
• 2015

Background: Residual stress always exists on any kind of welded area. This residual stress can cause the welded material to crack or fracture. For many years, the hole-drilling method has been widely used for measuring residual stress. However, this method is destructive. Nowadays, electronic speckle pattern interferometry (ESPI) can be used to measure residual stress with or without the hole-drilling method. ESPI is an optical nondestructive testing methods that use the speckle effect. Mechanical properties can be measured by calculation of the phase difference by the variation of temperature, pressure, or loading force. Methods: In this paper, the residual stress on the butt-welded area is measured by using ESPI with a suggested numerical calculation. Two types of specimens are prepared. Type I is made of pure base metal part and type II has a welded part at the center. These specimens are tensile tested with a material test system. At the same time, the ESPI system was applied to this test. Results: From the results of ESPI, the elastic modulus and the residual stress around the welded area can be calculated and estimated. Conclusion: With this result, it is confirmed that the residual stress on the welded area can be measured with high precision by ESPI.

• Transactions of Materials Processing
• /
• v.31 no.3
• /
• pp.136-142
• /
• 2022

The purpose of this study was to investigate the effects of sample thickness and support structure on the residual stress of Hastelloy X superalloy samples fabricated by laser powder bed fusion (LPBF), which is an additive manufacturing process. The residual stresses of LPBF samples with different thicknesses and support structures were measured using X-ray diffraction. The results revealed that as the thickness of sample increased from 2.5 mm to 20 mm, its tensile residual stress gradually decreased from 443.5 MPa to 182.2 MPa. Additionally, the residual stress in the bottom region of sample was higher than that in the top region, and the residual stress difference in the bottom and top regions became more pronounced as the sample thickness decreased. The residual stress of LPBF sample also varied depending on the structure of support. The residual stress of sample decreased with increasing contract area between the sample and the support, because the larger contract area led to smaller temperature gradient throughout the sample.

• Nuclear Engineering and Technology
• /
• v.55 no.1
• /
• pp.80-99
• /
• 2023

This paper presents the results of investigating the change in welding residual stresses of the core shroud, which is one of subcomponents in reactor vessel internals, performing finite element analysis. First, the welding residual stresses of the core shroud were calculated by applying the heat conduction based lumped pass technique and finite element elastic-plastic stress analysis. Second, the temperature distribution of the core shroud during the normal operation was calculated by performing finite element temperature analysis considering gamma heating. Third, through the finite element viscoelastic-plastic stress analysis using the calculated temperature distribution and setting the calculated residual stresses as the initial stress state, the variation of the welding residual stresses was derived according to repeating the normal operation. In the viscoelastic-plastic stress analysis, the effects of neutron irradiation on mechanical properties during the cyclic normal operations were considered by using the previously developed user subroutines for the irradiation agings such as irradiation hardening/embrittlement, irradiation-induced creep, and void swelling. Finally, the effect of neutron irradiation on the welding residual stresses was analysed for each irradiation aging. As a result, it is found that as the normal operation is repeated, the welding residual stresses decrease and show insignificant magnitudes after the 10^th refueling cycle. In addition, the irradiation-induced creep/void swelling has significant mitigation effect on the residual stresses whereas the irradiation hardening/embrittlement has no effect on those.