• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1074-1082
• /
• 2002

Nanocomposite PMN-PT-BT/Ag/MgO was prepared by sintering at $950{\circ}C$ with addition of $AgNO_3$ and MgO sol to the PMN-PT-BT powder sinterable at $1200{\circ}C$. The low-temperature-sinterable PMN-PT-BT/Ag powder prepared by the modified mixed oxide method was calcined at $600{\circ}C$ for 1h and surface modified with the MgO sol of 0-10 wt% and then subjected to consolidation at $850-950{\circ}C$ for 4h under a flowing oxygen. The nanocomposite PMN-PT-BT/Ag/MgO(0.5wt%) sintered at $950{\circ}C$ showed the microstructure with grains of $1-3{\mu}m$, the second phase of MgO of $0.1-0.3{\mu}m$ by SEM and Ag of << $1{\mu}m$ qualitatively by SIMS. It showed the sintered relative density of 99%, the room temperature dielectric constant of 17200, the dielectric loss of 2.1% and the specific resistivity of $5.46{\times}10^{12}{\Omega}{\cdot}cm$. But the PMN-PT-BT/Ag/MgO(0 wt%) nanocomposite sintered at $950{\circ}C$ showed a little better properties : the sintered relative density of 99.5%, the room temperature dielectric constant of 19500, the dielectric loss of 2.1% and the specific resistivity of $7.30{\times}10^{12}{\Omega}{\cdot}cm$.

• Proceedings of the KIEE Conference
• /
• 1995.07c
• /
• pp.1102-1104
• /
• 1995

This study presents the results of an investigation on the electrical characteristics of $PVF_2$ film, to be regarded as the excellent piezo and pyroelectricity, using dielectric relaxation technique by the variation of temperature and frequency. As one of the results, we confirmed that crystal form with Infrared absorption and XRD was ${\alpha}$ type and its crystalline was 59[%]. Also, the results of observation conformed to Debye theory for frequency variation of relative permitivity and dielectric relaxation. Especially, we confirmed each constant values in comparision with equation related to diffusion behavior of ion, so we obtained that activation energy was computed 17.25[kcal/mole] from the relation curve with frequency and temperature.

• Tribology and Lubricants
• /
• v.27 no.4
• /
• pp.209-212
• /
• 2011

The capacitive application(prove) can be used to measure the complex permittivity of dielectric material of various thickness and cross section. This paper presents that we designed the analysis system of engine oil permittivity to know the relation between the engine oil deterioration and the prove dimension. Each of the dimension of capacitive prove is changed and then electric capacity is measured by LCR {Inductance(L), Capacitance (C), and Resistance (R)} meter. The engine oil permittivity has extracted in the prove measurement. As the additional research, this paper suggest the best of the prove dimension for the permittivity measurement.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.51-56
• /
• 1999

The $BaTiO_3$ powders were synthesized by GNP (Glycine-Nitrate process). The powders were prepared using carbonate and alkoxide as starting materials and nitric acid was used as a solvent for starting materials as well as an oxidant for combustion. the effects of aggregates in $BaTiO_3$ powders on green densities, sintering and dielectric characteristics were investigated. When the glycine/cation molar ratio was 1.2, reactivity of self-combustion was most intensive and the degree of aggregates after calcination was low. On sintering at $1400^{\circ}C$, maximum theoretical relative density(94.99%%0 was obtained in case of 1.2 molar ratio of glycine/cation. The dielectric constant of this sintered $BaTiO_3$ was 1919.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2209-2210
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coaled on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field wore 16.48 ${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.577-578
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at 650f showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were 16.48${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.3
• /
• pp.237-241
• /
• 1998

In this study, PLZT stock solutions around x/65/35 (x=6~11) ferroelectric region were prepared by Sol-Gel method and deposited on ITO-glass by spin-coating method. The thin films were annealed by RTA(rapid thermal annealing). The variations of crystallographic structure of the thin films were observed using XRD and hysteresis curves, dielectric characteristics, and optical transmittances were measured in order to investigate the characteristics of the thin films. The thin films were crystallized at $750^{\circ}C$ for 5 min by RTA. Relative dielectric constant and optical transmittance increased with increasing La content, Ec and Pr were higher for thin films than for bulk materials.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.685-688
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with an organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The grain size decreased with increasing amounts of $MnO_2$, and the BSCT(50/40/10) thick film doped with 1wt% $MnO_2$ showed a value of 6.5mm. The thickness of thick films by four-cycle on printing/drying was approximately 100mm. The relative dielectric constant, dielectric loss and tunability of the BSCT(S0/40/10) thick films doped with 1.0wt% $MnO_2$ were 1296, 0.61% and 11.18%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.193-196
• /
• 2001

XLPE is occasionally happened to deteriorate cable insulation characteristics. It is happened to do a breakdown state by the degradation of electrical characteristic and electrical breakdown strength. I prepared TR-XLPE (Tree-Retardant XLPE) as adding various additives to prevent its states. Various additives are treeing retardants, anti-oxidants. Treeing retardants three kinds of aromatic compounds as adding each additive. Anti-oxidants use quinone compound and cresol compound as adding each additive. In order to observe each electrical characteristics, I measured breakdown strength, relative dielectric constant$({\varepsilon}_r)$, dielectric loss tangent$(tan{\delta})$. TR-XLPE specimens as adding treeing retardants and anti-oxidants enhance breakdown strength, ${\varepsilon}_r$, $tan{\delta}$ than pure XLPE.

• Proceedings of the KIEE Conference
• /
• 2006.07b
• /
• pp.1243-1244
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were $16.48{\mu}C/cm^2$ and 35.48kV/cm, respectively.