• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.6
• /
• pp.179-187
• /
• 2010

Corrosion of rebar embedded reinforced concrete is the main cause of collapse and degradation of reinforced concrete structure. Degradation occurs in reinforced concrete structures from corrosion caused by the Chloride that the damage other than the severe degradation of the structure in terms of maintenance and construction when the huge expense required and deciding terms is hard. Therefore, early detection of rebar corrosion is important for efficient maintenance and repairing and planning. Meanwhile, how to evaluate the corrosion of the non-destructive measurements have been used a lot. In particular CM-II (corrosion meter) is used to measurement the natural potential, polarization resistance and the resistivity of the concrete, but has some disadvantages. Embedded mini-sensor has been developed in order to overcome these disadvantages. So Measurement corrosion for using the mini-sensor compares with the measured results CM-II (corrosion meter), the developed mini-sensor verify the validity.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10c
• /
• pp.207-210
• /
• 1998

Recently it has become general to use the inhibitor with a view to protecting corrosion of rebars in concrete. So, it needs to study effect of protection and reasonable dosage of inhibitor to reduce corrosion of rebar in concrete containing chlorides. In this study, we estimate the corrosion rate of rebar in mortar by Tafel extrapolation method, one of electrochemical techniques, and the reasonable dosage of inhibitor for different chlorides environments.

• Structural Engineering and Mechanics
• /
• v.53 no.6
• /
• pp.1183-1200
• /
• 2015

Reinforcement corrosion can cause serious safety deterioration to aging concrete structures exposed in aggressive environments. This paper presents an approach for reliability analyses of deteriorating reinforced concrete structures affected by reinforcement corrosion on the basis of the representative symptoms identified during the deterioration process. The concrete cracking growth and rebar bond strength evolution due to reinforcement corrosion are chosen as key symptoms for the performance deterioration of concrete structures. The crack width at concrete cover surface largely depends on the corrosion penetration of rebar due to the expansive rust layer at the bond interface generated by reinforcement corrosion. The bond strength of rebar in the concrete correlates well with concrete crack width and decays steadily with crack width growth. The estimates of cracking development and bond strength deterioration are examined by experimental data available from various sources, and then matched with symptom-based lifetime Weibull model. The symptom reliability and remaining useful life are predicted from the predictive lifetime Weibull model for deteriorating concrete structures. Finally, a numerical example is provided to demonstrate the applicability of the proposed approach for forecasting the performance of concrete structures subject to reinforcement corrosion. The results show that the corrosion rate has significant impact on the reliability associated with serviceability and load bearing capacity of reinforced concrete structures during their service life.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.37-38
• /
• 2022

During the past decades, the corrosion of the steel rebar embedded in concrete structure surrounding marine environment is actually problematic and required the suitable preventive method. An eco-friendly corrosion inhibitor mix is investigated to stifle the active corrosion in comparison with other commercial corrosion inhibitors. The hybrid inhibitor enhances the corrosion resistance and the workability of concrete. However, it reduces the compressive strength slightly after 28-day-age. The electrochemical studies and mechanical studies are pointed out the corrosion resistance property, corrosion kinetics, and the mechanical properties of all concrete samples. H-3 is the optimum dose of hybrid inhbitor that meets the demand of both electrochemical property and mechanical property. It performs the noble features due to the formation of optimum amount of P-Zwitterions-(Cl)-Fe complex onto the steel rebar surface.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.1E
• /
• pp.17-22
• /
• 2006

Artificial cracks were made in the cover concrete of specimens embedding ten types of steel rebars of different Cr contents. The research aims for developing Cr-bearing steel rebars resistant to macrocell corrosion environments induced by cracking in cover concrete. The cracks were subjected to intensive penetration of carbon dioxide (carbonation specimens) to form macrocells. The carbonation specimens were then treated with accelerated corrosion curing, during which current macrocell corrosion density was measured. The corrosion area and loss from corrosion were also measured at the end of 105 cycles of this accelerated curing. The results of the study showed that Cr-bearing steel with Cr content of 5% or more suppressed corrosion in a macrocell corrosion environment induced by the differences in the pH values due to carbonation of cracked parts. Cr-bearing steels with Cr content of 7% or more are proven to possess excellent corrosion resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.3
• /
• pp.47-57
• /
• 2023

In this study, pull-out tests were performed to investigate the effects of stirrup spacing, rebar diameter, and corrosion rate on bond strength of deformed bars in reinforced concrete. Twelve pull-out specimens with different stirrup spacing, rebar diameter, and corrosion rate were prepared following the RILEM RC6 guidelines. The test results showed that the bond strength of specimens with stirrups increased when the corrosion rate was less than 3%, whereas it decreased when the corrosion rate was more than 3%. On the other hand, the bond strength of specimens without stirrups decreased as the corrosion rate increased. The effect of rebar diameter was less significant compared to those of stirrup spacing and corrosion rate. A bond strength model for pull-out specimens was proposed considering stirrup ratio and corrosion rate, and the model showed the lowest error among the previous models.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.479-482
• /
• 2005

The galvanic currents between carbon steel and Cr-bearing rebars have been studied in concrete subjected to carbonation and chloride attack. The results revealed that in case of SD345 contacted with Cr-bearing rebar in concrete under chloride attack environment and carbonation environment, the corrosion acceleration by galvanic corrosion is not generated. Therefore, Cr-bearing rebar can be used together with the carbon steel in the new establishment structure.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.65-66
• /
• 2021

In this study, the optimum amount of hybrid inhibitors i.e. L-Arginine (LA) and sodium phosphate tribasic dodecahydrate (SP), applied for carbon steel rebar in simulated pore concrete (SCP) solution contaminated with 3.5 wt.% NaCl, was discovered. The corrosion inhibition performance of hybrid inhibitors was investigated by open circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization. The highest corrosion inhibition efficiency was found as 99.52% corresponding to 2% LA and 0.25% SP after 210 h exposure. Anodic type inhibition action was confirmed by potentiodynamic polarization study. Surface studies including scanning electron microscopy (SEM), and atomic force microscopy (AFM) were used to figure out the surface morphology of the steel rebar treated with hybrid inhibitors in order to collaborate with electrochemical studies.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.846-848
• /
• 1999

The corrosion problem of rebar is a world wide concern of every engineer engaged in reinforced concrete business, clients, engineers construction contractor and maintenance organizations, all alike. Research and development of new systems, materials, and design concept of rebar corrosion is actively progressing world wide. We have to open our mind and change the paradigm so that creative and active approach will make all of us beneficial.

• Journal of the Korea Concrete Institute
• /
• v.18 no.2 s.92
• /
• pp.233-238
• /
• 2006

In lifetime estimation, the FEM analysis method is proposed for predicting corrosion failure time of concrete structures exposed to sea-water. This study shows that the corrosion rate of rebar in artificial pore solution can be transferred to the corrosion rate of rebar in concrete using the relationship between pore volume and concrete volume by Jennings' model. And this study considered the pitting corrosion effects of reinforcement bar on corrosion failure analysis, rebar size to cover depth and nonlinear crack analysis. These analysis results have good accordance with the experimental results of Williamson's work. This methodology can be applied to lifetime prediction procedure of reinforced concrete structures and also gives more reasonable results of concrete cover failure time estimation of reinforced concrete structures exposed to sea-water.