• 제목/요약/키워드: rapid sintering

검색결과 213건 처리시간 0.022초

Bloating Mechanism of Lightweight Aggregate with the Size

  • Lee, Ki Gang
    • 한국세라믹학회지
    • /
    • 제53권2호
    • /
    • pp.241-245
    • /
    • 2016
  • The purpose of this study was to investigate the bloating mechanism of artificial lightweight aggregates with different sizes (ESA, effective surface area). Aggregates were produced using hard clay, stone sludge, and a bloating agent in order to observe the effect of the gradation of the artificial lightweight aggregates. Kerosene and amorphous carbon were used as bloating agent. The particle size of the produced aggregate ranged from 3 mm to 9 mm. With regard to the amount of bloating agent to be used, 2 ~ 6 parts by weight were used. The specific gravity, absorption rate, and the type of aggregates produced by rapid sintering at $1075{\sim}1200^{\circ}C$ were determined. Microstructures were observed. When ESA had a value of 1 or below, kerosene, which has a high burning rate, was found to be advantageous for use as a bloating agent. When ESA had a value of 1 or above, carbon, which has a relatively low burning rate was found to be an advantageous bloating agent. It is thought that kerosene is more advantageous, as ESA decreases, for the production of aggregates having low water absorption rate.

SLS의 공정 파라미터 최적화에 관한 연구 (Optimization of Build Parameters in SLS Process)

  • 허성민;오도근;최경현;이석희
    • 대한기계학회논문집A
    • /
    • 제24권3호
    • /
    • pp.769-776
    • /
    • 2000
  • RP(Rapid Prototyping) technology is gaining its popularity in building a prototype in all industries. SLS(Slective Laser Sintering) is one of RP technologies, which is focused on tooling processes as well as three dimension solid model. There are several factors, the length and the cross-sectional area of a part, that have an effect on build setup in SLS process. In this paper, the computation on geometrical relationship is used to slice STL file and to estimate these factors. Based on these values, the build setup parameters such as the heating temperature, the laser power, and the powder cartridge feed rate are determined by neural network approaches. The test results show that the computation time is saved and the neural network approach is able to apply to get the optimal parameters of build process within an acceptable error rate.

혁신적인 3D 프린팅 방법을 사용하여 나노-에칭된 표면을 갖은 나선형 세포담체 제작 (Fabrication of spiral scaffolds with nano-etched surface by using an innovative 3D printing method)

  • 양지훈;이재윤;김근형
    • 한국표면공학회:학술대회논문집
    • /
    • 한국표면공학회 2018년도 춘계학술대회 논문집
    • /
    • pp.73-73
    • /
    • 2018
  • 조직재생공학은 조직이나 장기를 재생하고 유지하는 데 초점을 맞춘 종합 분야이다. 세포담체는 세포가 조직이나 장기로 발달 할 수 있도록 결정적인 역할을 한다. 따라서 공극률, 기공 크기, 기공 상호 연결성, 표면 거칠기, 기계적 강도 및 기하학과 같은 기본 요구 사항들은 중요한 특성으로 간주된다. Particle leaching, phase separation, solvent casting, gas foaming, selective laser sintering, fused deposition 및 3D dispensing (printing)과 같은 다양한 Rapid Prototyping 방법이 세포담체 제조에 사용되었다. 또한, 다양한 천연 및 합성 고분자가 세포담체를 제조하는데 사용되어왔다. 본 연구에서는 기존의 3D 프린팅 방법과 플라즈마 에칭 공정을 이용하여 나노 에칭 된 나선형 가닥으로 구성된 3 차원 세포담체를 제작 하였다. 제작 된 세포담체의 물리적 및 생물학적 성질을 비교 연구하기 위해, 본 연구에서는 매끄러운 가닥을 대조물로 사용하였다. 나노 에칭된 표면은 초기 세포 부착, 증식 및 골 형성 분화와 같은 세포 활동에 영향을 미쳤다.

  • PDF

급속가열 이력 제어에 의한 $Si_3-N_4-SiC$계 미분말 시편의 치밀화 (Densification of Ultrafine $Si_3-N_4-SiC$ Powder Compacts by Rapid Heating under Controlled Thermograms)

  • 이형직
    • 한국세라믹학회지
    • /
    • 제32권7호
    • /
    • pp.832-838
    • /
    • 1995
  • The densifying behavior of ultrafine amorphous Si3N4 (about 20 nm)-$\beta$-SiC (about 40~80 nm) powders (O2 : 1.3~15wt%, 0$700^{\circ}C$ within 15 sec and then immediately cooled and held at 135$0^{\circ}C$ for 10 min in N2 atmosphere without resorting to additives using a Xe image heating apparatus. Using an ultrafine pure Si3N4 powder with particle size less than 30nm, further more, mixed with an appropriate amount of $\beta$-SiC, was found to be advantageous to obtain uniform and homogeneous microstructure. In addition, ultrafine Si3N4 powders were also proved to be effective as sintering additive on densifying large sized Si3N4 powder compacts.

  • PDF

Soft-magnetic Characteristics of Co-based Amorphous Powder Produced by Spinning Water Atomization Process (SWAP)

  • Otsuka, I.;Wada, K.;Watanabe, A.;Kadomura, T.;Yagi, M.
    • 한국분말야금학회:학술대회논문집
    • /
    • 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
    • /
    • pp.784-785
    • /
    • 2006
  • Co-based amorphous powder was produced by a new atomization process "Spinning Water Atomization Process (SWAP)", having rapid super-cooling rate. The composition of the alloys was ($(Co_{0.95}Fe_{0.05})_{1-x}Cr_x$)$_{75}Si_{15}B_{10}$ (x=0, 0.025, 0.05, 0.075). The powders became the amorphous state even if particle size was up to about $500{\mu}m$. The coercive force of powders was about 0.35 - 0.7 Oe. Furthermore, Co-based amorphous powder cores with glass binders were made by cold-pressing and sintering methods. The initial permeability of the core in the frequency range up to 100 kHz was about 110, and the core loss at 100 kHz for Bm = 0.1 T was $350kW/m^3$.

  • PDF

Agile Fabrication of a Sample by a Solid Freeform Fabrication System

  • Taijoon Um;Youngcheol Joo;Park, Sehyung;Sanghyun Min
    • 대한전자공학회:학술대회논문집
    • /
    • 대한전자공학회 2002년도 ITC-CSCC -3
    • /
    • pp.1740-1743
    • /
    • 2002
  • This paper presents the basic concept of a Solid Freeform Fabrication System using a rapid prototyping procedure. The system can fabricate a ceramic model by laser cutting, accumulating, laminating and sintering of each slice. The system is mainly equipped with a laser apparatus, an x-y table, a material transfer system, and an electric oven. The system could fabricate a small object with smooth surface within comparatively short period of time. The system has also shown its effectiveness in terms of the direct application of the object without the secondary mechanical process. The fabricated sample could directly be applied and used to fairly wide practical areas.

  • PDF

급속응고 Al-20 wt% Si 합금 분말의 ECAP를 통한 고형화 (Consolidation of Rapidly Solidified Al-20 wt% Si Alloy Powders Using Equal Channel Angular Pressing)

  • 윤승채;홍순직;서민홍;정영기;김형섭
    • 한국분말재료학회지
    • /
    • 제11권3호
    • /
    • pp.233-241
    • /
    • 2004
  • In this study, bottom-up type powder processing and top-down type SPD (severe plastic deformation) approaches were combined in order to achieve both full density and grain refinement of Al-20 wt% Si powders without grain growth, which was considered as a bottle neck of the bottom-up method using the conventional powder metallurgy of compaction and sintering. ECAP (Equal channel angular pressing), one of the most promising method in SPD, was used for the powder consolidation. The powder ECAP processing with 1, 2, 4 and 8 passes was conducted for 10$0^{\circ}C$ and 20$0^{\circ}C$ It was found by microhardness, compression tests and micro-structure characterization that high mechanical strength could be achieved effectively as a result of the well bonded powder contact surface during ECAP process. The SPD processing of powders is a viable method to achieve both fully density and nanostructured materials.

Sintered Duplex Stainless Steels Corrosion Properties

  • Dobrzanski, L.A.;Brytan, Z.;Grande, M. Actis;Rossob, M.;Park, Woo-Young;Kim, Cheol-Su
    • 한국분말야금학회:학술대회논문집
    • /
    • 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
    • /
    • pp.583-584
    • /
    • 2006
  • This work presents mechanical properties and corrosion resistance of duplex stainless steels obtained through powder metallurgy starting from austenitic, martensitic powders by controlled addition of alloying elements in the right quantity to obtain the chemical composition of the structure similar to biphasic one. In the mixes preparations the Schaffler's diagram was taken into consideration. Prepared mixes of powders have been sintered in a vacuum furnace with argon backfilling. After sintering rapid cooling was applied using nitrogen. Corrosion properties have been studied through electrochemical methods in 1M NaCl.

  • PDF

MEMS 공정을 이용하지 않는 미세구조물 제작에 관한 연구 (A Study on fabrication of micro structure not using MEMS processing)

  • 유홍진;김동학;장석원;김태완
    • 한국산학기술학회:학술대회논문집
    • /
    • 한국산학기술학회 2004년도 춘계학술대회
    • /
    • pp.267-269
    • /
    • 2004
  • 본 연구에서는 일반적인 미세구조물 제작공정인 lithography 공정을 이용하지 않고 SLS(Selective Laser sintering)형 RP(Rapid Prototyping system)을 이용하여 패턴의 깊이가 400$\mu$m인 미세구조물을 제작하였다. 제작 공정변수 중 재료의 상태가 new powder 이고 배치각이 $0^{\circ}$ 일 때 패턴의 깊이, 선폭과 표면조도가 가장 잘 구현되었다.

  • PDF