• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1989년도 춘계학술대회 논문집
• /
• pp.74-76
• /
• 1989

x Pb($Sb_{1/2}Sn_{1/2}O_3-PbTiO_3-PbZrO_30.05{\leq}x{\leq}0.25$) ternary compound ceramics were fabricated by the mixed oxide method. The sintering temperature and time were 1200-1270[$^{\circ}C$], 2 hour, respectively. Increasing the PSS contents, the transition temperatures were decreased. The relative dielectric constant and Curie temperature of the 0.25 PSS-0.25 PT-0.5 PZ specimens were 450, 220[$^{\circ}C$]. The Pyroelectric coefficient of the 0.25PSS-0.25PT-0.50 PZ specimen was $5.20{\times}10^4$[C$\textrm{cm}^2$K].

• 대한전자공학회논문지SD
• /
• 제41권6호
• /
• pp.9-15
• /
• 2004

1,3 propanediol 을 이용한 sol-gel 방법으로 PZT(30/70) 후막을 제작하였다. 제작된 film 의 초전특성은 dynamic 방법을 이용하여 변조 주파수 의존성을 조사하였다. 초전계수 (pyroelectric coefficient) 는 약 $5.0{\times}10^{-8}\;C/cm^2{\cdot}K$를 나타내었다. 전압감도와 비검출능에 대한 재료평가지수는 비교적 높은 유전률과 높은 초전계수로 인해 각각 $3.4{\times}10^{-11}\;C{\cdot}cm/J$과 $5.9{\times}10^{-9}\;C{\cdot}cm/J$을 나타내었다. 전압감도는 저주파 영역에서 증가하다가 고주파 영역에서는 주파수에 반비례하는 경향을 보이며, 10Hz에서 최대값 1.84 V/W를 나타내었다. 잡음전압은 Johnson 잡음의 영향으로 거의 $f^{-1/2}$ 에 비례하여 증가하였다 잡음등가전력과 비검출능은 같은 주파수 80Hz 에서 각자 $2.83{\times}10^{-7}\;W/Hz^{1/2}$ 과 3.13{\times}10^5\;cm{\cdot}Hz^{1/2}/W$를 나타내었다.

• 센서학회지
• /
• 제6권6호
• /
• pp.491-499
• /
• 1997

초전재료의 개발 및 박막화를 위하여 5, 10 및 15 mol%의 La 조성을 가지는 세라믹 PLT 시편 및 박막 PLT를 제조하여 그 특성을 분석하였다. PLT의 완전 소결과 Pb 성분의 휘발을 막기 위하여 TG/DTA를 사용하여 하소 및 소결온도를 결정하였다. PLT 세라믹 시편을 제조하기 위한 하소 및 소결온도는 각각 $850^{\circ}C$, $1150^{\circ}C$ 이고 더 높은 소결온도에서는 많은 질량 손실이 발생하였다. 세라믹 시편을 사용한 온도-유전율 특성의 측정으로 La 조성에 따른 PLT의 온도에 대한 유전특성을 조사하였다. 5, 10 및 15 mol%의 La 농도에 따라 PLT의 상전이점은 각각 $330^{\circ}C$, $269^{\circ}C$ 및 $210^{\circ}C$를 나타내었다. 제조된 PLT 시편을 사용하여 적외선 감지 특성을 확인하였고, 고주파 마그네트론 스퍼터링을 이용하여 PLT 박막을 증착하였다. 다음으로 격자상수 및 광투과 특성을 통하여 완전 소결된 PLT 타겟으로 제작한 PLT 박막은 타겟과 동일한 구조를 가지고 있음을 확인하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.543-546
• /
• 2000

Ferroeleclric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the mixed-oxide method and cold-pressing method using sol-gel derived PZT(90/10) and PZT(10/90) powders. All specimens show a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increase in sintering temperature, the value for the x=0.65 specimen sintered at 125$0^{\circ}C$ was 14.4$\mu$m. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247, 2.06%, respectively. All specimens showed fairly good temperature and frequency stability of dielectric constant with the range from -2$0^{\circ}C$ to 6$0^{\circ}C$ and 100Hz to 10MHz. The coercive field and the remanent polarization of x = 0.65 specimen sintered at 125$0^{\circ}C$ were 8.5 kV/cm and 13 $\mu$C/cm$^2$, respectively. The pyroelectric coefficient of the x=0.65 specimen sintered at 125$0^{\circ}C$ was 5.64$\times$10$^{-8}$ C/cm$^2$K, respectively.

• 센서학회지
• /
• 제6권1호
• /
• pp.1-5
• /
• 1997

La가 첨가된 $PbTiO_{3}(PLT)$ 박편을 이용하여 압전효과에 대한 보상이 이루어진 고감도 초전형 적외선 센서를 제작하였다. 센서는 두 개의 $1{\times}2\;mm^{2}$의 cell을 인접하게 나란히 설치하고 적절히 전극을 배열한 이중소자 형태로 제작하였으며, 제작된 센서는 단일 소자형 센서에 비하여 잡음 특성이 향상되어 신호대 잡음비가 350에 이르렀다. 나아가 2400 V/W 이상의 전압감도, $4.6{\times}10^{-8}\;C/cm^{2}K$의 초전계수 및 $4.2{\times}10^{-11}\;Ccm/J$의 전압 성능지수와 8.7 msec의 작은 열시상수 특성들을 보였다. 제작된 초전형 적외선 센서는 적절한 매치를 통하여 인체의 이차원적 이동방향의 감지에 응용할 수 있음을 실험을 통하여 확인하였다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1991년도 하계학술대회 논문집
• /
• pp.194-197
• /
• 1991

In this study, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, added $MnO_2$ (0-0.30[mol%]) ceramics were fabricated by the mixed oxide method. The sintering temperature and time were $1250[^{\circ}C]$, 2[hr], respectively. In the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens, relative dielectric constant and dielectric loss were minimum values 3.52, 0.003, respectively, and Curie temperature were highest values $256[^{\circ}C]$. Pyroelectric coefficient and voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, and added $MnO_2$ (0.24[mol%]) specimen were good values, $6.73{\times}10^{-8}[C/cm^2K],\;125[v/W]$, respectively. Figure of merit of pyroelectric current, voltage and detectivity of the specimen, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) were good values $2.714{\times}10^{-8}[Ccm/J],\;7.706{\times}10^{-11}[Ccm/J],\;2.640{\times}10^{-8}[Ccm/J]$, respectively. Voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens were decreased with increasing the chopper frequency.

• 한국세라믹학회지
• /
• 제56권4호
• /
• pp.412-420
• /
• 2019

In this study, the dielectric and polarization properties of manganese (Mn% = 0.0, 0.1, 0.2, 0.5) doped (Pb_0.93La_0.07)(Zr_0.82Ti_0.18)O₃ (PLZT 7/82/18) anti-ferroelectric ceramics were studied for energy storage capacitor and pyroelectric applications. A systematic investigation demonstrated that the electric properties of PLZT 7/82/18 ceramics are affected significantly by the Mn-doping content. A maximum dielectric constant of ~ 2,128 at 1 kHz was found for 0.1% Mn-doped PLZT ceramics with a low dielectric loss of 0.018. The bipolar polarization versus electric field (P-E) hysteresis loops were traced for all compositions showing a typical anti-ferroelectric nature. The breakdown field was found to decrease with Mn-doping. The energy storage density and efficiency were found to be 460 J/㎤ and ~ 63%, respectively, for 0.2% Mn-doped PLZT ceramics. The pyroelectric coefficient of PLZT ceramics shows an increase based on the amount of Mn-doping.

• 한국진공학회지
• /
• 제17권5호
• /
• pp.442-447
• /
• 2008

강유전체 0.65Pb$(Mg_{1/3}Ta_{2/3})O_3-0.35PbTiO_3$ 고용체에 $Ag_2O$를 첨가하여 $1200^{\circ}C$에서 소결하여 시료를 제작하였다. 완성된 시료의 미세구조는 주사 전자현미경(SEM)을 이용하여 관찰하였고, 전기적 특성의 관찰을 위하여 유전상수와 유전손실, 초전계수를 측정하였다. 제작된 시료 중에서 0.2 mol%의 $Ag_2O$를 과잉 첨가한 시료에서 유전상수와 초전계수가 가장 크게 나타났다. 각 시료에서 유전상수와 초전계수의 최대값의 온도는 $Ag_2O$ 첨가량이 증가할수록 저온으로 이동하였다.

• 폴리머
• /
• 제35권5호
• /
• pp.375-377
• /
• 2011

두 단계 스핀 코팅 방법을 사용하여 세라믹 체적 분율 0.10과 0.13의 $PbTiO_3$/P(VDF/TrFE) 0~3형 복합재료를 제작하고 분석하였다. 0~3형 $PbTiO_3$/P(VDF/TrFE) 복합재료를 SEM 전자현미경 사진으로 성공적으로 확인할 수 있었다. 이러한 전자현미경 사진을 통하여 복합재료의 0~3형 구조를 재확인하였다. 0~3형 $PbTiO_3$/P(VDF/TrFE) 복합재료는 P(VDF/TrFE) 공중합체보다 센서용 전기적 특성이 우수함을 나타내었다. 그러므로 이러한 낮은 유전상수와 높은 초전계수를 나타내는 0~3형 $PbTiO_3$/P(VDF/TrFE) 복합재료는 더 높은 성능을 나타낼 수 있는 새로운 초전형 센서 재료로 사용될 수 있다.

• 한국세라믹학회지
• /
• 제33권5호
• /
• pp.556-562
• /
• 1996

In order to understand the electrostrictive behavior of Pb(Mg1/3Nb2/3)O3-PbTiO3 (PMN-PT) solid solutions the dielectric constants the electric-field-induced strains and the pyroelectric coefficients of (1-x)PMN-xPT (x=0.1-0.4) were investigated in the temperature range -50~20$0^{\circ}C$. For x=0.1~0.35 where the phase transi-tion is diffusive the strain has a maxima at the temperature of maximum pyroelectric coefficient (depolrizing temperature) rather than the temperature of maximum dielectric constant. For x=0.4 where the phase transition is relatively sharp the strain decreases monotonically as the temperature increases. Relationships among the above experimental results are discussed.