• Journal of the Korean Wood Science and Technology
• /
• v.25 no.1
• /
• pp.15-22
• /
• 1997

The effectiveness of presteaming for improving CCA treatability on refractory Japanese larch heartwood was investigated in this study. Presteaming was effective on improving treatability, and the extent of improvement was dependent on moisture contents of wood specimen and steaming conditions. Green wood showed higher average value in both preservative retention and penetration than dry wood, and steaming under pressure conditions also had higher treatability than steaming at atmospheric conditions. The degree of improvement for treatability was increased with the extension of steaming period. Treatability of dry wood pres teamed under pressure conditions more than 6 hours and green wood for 3 hours was similar to that enhanced by conventional incising. Presteaming green wood under pressure conditions more than 6 hours was more effective than conventional incising in improvement of CCA treatability, and resultant treatability satisfied a minimum value required for CCA-treated wood for being used at the regions of hazard class H3 and H4. In addition, an improvement of treatability by presteaming was due to an increase in permeability resulted from the degradation of hemicelluloses within aspirated pit membrane and cell wall, not the removal of extractives from pit membrane. The reduction in strength, measured as longitudinal compressive strength, due to pres teaming was related with the degradation of hemicelluloses, and was increased as steaming conditions were severe. The degree of strength reduction associated with presteaming treatment to obtain required treatability could be quantified from the relatively good relation between the increase in treatability and the decrease in strength.

• Analytical Science and Technology
• /
• v.21 no.1
• /
• pp.1-8
• /
• 2008

This study was conducted to investigate the characteristics of the leaching of metal components from CCA-treated wood during outdoor exposure. CCA-treated wood specimens were placed horizontally or buried vertically into the soil, and then exposed to the natural environment for a year. Wood samples were collected from the side of the horizontal wood specimens using a drill and saw dust samples were collected at the end of the exposure. Soil samples were also obtained around the wood specimens and at different depths of the posts. Wood and soil samples were analyzed for metals using an atomic absorption spectrometer. Monthly metal concentrations varied greatly and more metals were released when wood specimens were exposed vertically than horizontally. Arsenic was released from the wood by 80 % of the intial content. In addition, more leaching was observed from the zone below the ground than above the ground, and soil around the posts was contaminated with metals released from CCA-treated wood.

• Journal of the Korean Wood Science and Technology
• /
• v.13 no.2
• /
• pp.35-44
• /
• 1985

The purposes of this study were, first, to investigate retention levels of toxic elements and oxide individual plies for each panel and, second, to examine disproportioning of individual toxic elements Thirty five water gum plywood panels were treated with a copper-chromium-arsenic preservative (CCA) by the soaking process as the treament time were applied. Such individual plies at a distance of 2.5cm, 7.5cm from the edge were assayed for CuO, $CrO_3$, and $As_2O_5$ on the basis of copper, chromium and arsenic content by Atomic Absorption Spectrophotometry. In these experiments, 12mm thickness plywood panels made of water gum, which were selling, were selected for the preservative treatment. Treating solutions were prepared for 10%, dilute solution of copper-chromium-arsenic preservative and then 1, 3, 6, 12 and 24 hours soaking trements in CCA preservative were applied. The results obtained are as follows: 1. The retention of total oxide in the face and back plies (1+7) retained more than the retention of total oxide in the other plies. The total oxide retention for the individual plies except the face and back plies (1+7) was showed in the following orders; cross plies (3+5), cross plies (2+6), core ply (4). 2. The retentions of total oxide increased as the increase of treatment time. The CCA treated plywood retained high levels of total oxide retention in the face and back plies (1+7). 3. All the retentions in the face and back plies (1+7) is over 5Kg/$m^3$, New Zealand Timber Preservation Standards Specification, and after 6 hours, the retentions in the cross plies (3+5) is over 4. The relative penetration of copper, chromium, and arsenic were not affected by the treatment time. The proportion of arsenic decreased in relation to both copper and chromium and the proportion of copper increased in relation to both chromium and arsenic. 5. A disproportioning of copper, chromium occurred with longer distance from edge, and with longer distance from edge the leachability resistance of CCA treated specimens decreased. After 6 hours (soaking time), the proportion of active elements at a distance of 2.5cm from the edge was consistent. And after 24 hours-soaking, the proportion of active elements at a distance of 7.5cm from the edge was consistent.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.4
• /
• pp.306-315
• /
• 2010

The stress laminated timber, which could be manufactured by small dimension lumber on construction site, has high possibilities for bridges in remote area, such as recreation forest or forest road, because those bridges may be short span and low frequency in use. The stress laminated timber has merits of easiness for preservative treatment and transportation because it is manufactured with small dimension lumber. This study was carried out to analyze performances of stress laminated timber manufactured with preservative treated domestic pitch pine for developing structural design data for stress laminated timber bridges for vehicular traffic. Perpendicular to grain compressive performance by preservative treatment and bending performance by bored holes of pitch pine lumber was analyzed. Then, the effects of bending performance by pre-stress pressure, distance of bolts, number of laminations and planning were analyzed. Conclusively, planning of lumber was not necessary for manufacturing stress laminated timber, and 80% of bending stiffness criteria was maintained as pre-stress pressure was higher than 3.0 kg/$cm^2$. However, further researches are needed to define the effects of bolt distances and number of laminations. The results of this research would be basic data for design stress laminated timber bridges for vehicular traffic in Korea.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.1
• /
• pp.42-47
• /
• 2000

This study was designed to investigate the effect of treatment variables on CCA treatment of Japanese red pine (Pinus densiflora), Japanese larch (Larix leptolepis), and ezo spruce (Picea jezoensis) round posts. Variables included were duration of initial vacuum (30, 45, or 60 minutes) and maximum pressure applied (8.5, 10.5, or 14.0 kg/$cm^2$), and maximum pressure was maintained until refusal point was reached. Regardless of wood species, extending the duration of initial vacuum more than 30 minutes did not affect treatability. Increasing pressure did not affect preservative penetration; however, preservative retention was affected by pressure levels, particularly at higher level (14.0 kg/$cm^2$). Preservative penetration depth of Japanese red pine met a minimum requirement specified by Notification of Korean Forestry Administration (No. 1999-8) for hazard class H5 of CCA-treated wood. Penetration of preservative in both Japanese larch and ezo spruce was not deep because of shallow sapwood thickness of these species, so pretreatment such as incising should be considered if these species are treated with preservatives. Although retention in Japanese red pine was not significantly increased even with 14.0 kg/$cm^2$, that of refractory Japanese larch and ezo spruce was significantly increased with the application of 14.0 kg/$cm^2$. Effect of treatment variables on refusal time was unclear; however, it is cleared that the refusal time was shortened with the increase in sapwood thickness.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.6
• /
• pp.55-59
• /
• 2003

The fixation and leaching characteristics of chromated copper arsenate (CCA Type C) and chromium- copper-fluoride-zinc (CCFZ) in domestic softwood (Japanese red pine, Korean pine, and Japanese larch) sapwood were investigated using the expressate method to follow chromium fixation and the American Wood-Preservers' Association (AWPA) leaching procedure to determine leaching properties after fixation. The rates of fixation were affected by preservative types; CCA was fixed much faster than CCFZ for all species evaluated. There were definite differences in the fixation rates of different species, with Korean pine requiring shorter to fix than the other species evaluated. Chromium fixation was greatly enhanced by elevated temperatures, and fixation time can be estimated according to fixation temperatures applied. The percentage of arsenic and zinc leached from domestic softwoods was relatively high compared to chromium and copper, indicating that there is still a relatively high unfixed arsenic and zinc components after complete chromium fixation in CCA-and CCFZ-treated samples, respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.29 no.2
• /
• pp.126-132
• /
• 2001

This research is carried out to investigate the formation and preservative effectiveness of inorganic substance, calcium carbonate($CaCO_3$), in wood. The specimens were prepared by the impregnation with saturated solutions of potassium carbonate($K_2CO_3$) into the wood followed by precipitation in saturated solutions of calcium chloride($CaCl_2$) for 24h, 72h and 120h, and then they were leached in instrument flowing with water for 24h. The weight percent gains of $K_2CO_3$ solution impregnated specimens reached approximately a maximum value (108.1%) by 72h precipitation in $CaCl_2$ solutions. Inorganic substances were observed to he produced in the lumina of tracheids of specimens. From these inorganic substances filling in the tracheids, characteristic X-rays of calcium(Ca-$K_{\alpha}$) were detected by energy dispersive X-ray analyzer. Moreover, it was shown from a leaching treatment that these substances could not he leached easily from the specimens. Therefore, they were could he considered to be insoluble calcium carbonates. The weight losses of the prepared specimens were hardly occurred by test fungi attacks. Thus inorganic substances in specimens can be said to have preservative effectiveness.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.3
• /
• pp.245-254
• /
• 2009

As a substitute for CCA, which is inhibited due to its environmental pollution and human harmfulness, and CuAz and ACQ with a high cost, okara-based wood preservatives were formulated with okara hydrolyzates using copper sulfate and/or borax as a metal salt. The efficacy of the preservatives and X-ray microanalysis of wood specimens treated with the preservatives were examined to confirm the potential of the okara-based wood preservatives. Most of the preservatives showed excellent decay resistance against brown-rot fungi, Postia placenta and Gloeophyllum trabeum. The efficacy was improved when the acid concentration and temperature used for the hydrolysis of okara increased. In addition, when borax was added into copper sulfate/okara hydrolyzates preservative formulations, any decay was not found in the specimens. From the microscopic observation of the specimens treated with okara-based wood preservatives, it seems that okara is contributed to the fixing of metal salts in wood blocks. Therefore, it is speculated that okara-based wood preservatives can effectively protect wood against fungal attack as CuAz, and that the preservatives are sufficient to use as an alternative wood preservative of CCA, ACQ and CuAz.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.743-749
• /
• 2016

The concentration control of wood preservatives is necessary to produce a preservative treated wood having a uniform quality. Concentration measurement method of wood preservatives to be easily used in the field has not been developed yet. This study examined the way to estimate the concentration from turbidity of ACQ wood preservative that can be relatively easily measured by using a portable turbidity meter. The addition of phosphoric acid solution in an alkaline ACQ solution having a very low turbidity is created a suspension of the white substance and the turbidity suddenly increased. The optimum amount of addition of the phosphoric acid solution is until the pH of ACQ solution reaches 7, the turbidity of the ACQ solution reaches maximum value. Excessive addition of the phosphoric acid solution results in a turbidity decrease with acidification of the ACQ solution. Also ACQ solution becomes transparent. The high significance was recognized with positive correlation between the concentration and the turbidity of the ACQ solution. From the t-test, The significant difference between the actually measured concentrations and the concentrations predicted by the regression equation for industrial ACQ solutions was not recognized. Thus, it was possible to know that concentration prediction and control of industrial ACQ solution using the turbidity and a regression equation. Therefore, using the regression equation and turbidity is expected to be able to management the concentration of ACQ solution in the industrial field.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.1
• /
• pp.41-48
• /
• 2014

To development of the low toxic preservatives, we prepared 29 kinds of chemicals using dinotefuran of low toxic insecticide, IPBC and propiconazol of fungicide, and clove oil has fungicidal activity, but is harmless to humans. It was conducted to investigate the inhibitory effectiveness of mycelial growth and anti-mold effectiveness to treated PDA medium and wood specimen with prepared chemicals. It was not showed anti-mold effectiveness that solvent and emulsifier form preservatives. Therefor, we thought that only four component, dinotefuran, IPBC, propiconazol and clove oil, has anti-mold effectiveness. In the PDA medium test, the preservative which has much IPBC showed high anti-mold effectiveness. By the wood specimen test, it was known that many prepared preservatives which showed good inhibitory effectiveness of mycelial growth in the PDA medium test, have not anti-mold effectiveness. Of all prepared preservatives in this study, only three preservatives containing dinotefuran and IPBC, or adding clove oil appeared the excellent anti-mold effectiveness.