• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 봄 학술논문 발표대회
• /
• pp.137-138
• /
• 2023

This study proposed the optimal mixing time for pre-mixed cement and post mixed cement using the statistical analysis method of box plots. Pre-mixed cement can prevent material seegregation, strength loss, and quality variation if mixed for at least 60 seconds, and the data median is shown to be within the box range. Post-mixed cement should be mixed for at least 180 seconds to prevent material segregation, strength loss, and quality variation, and compressive strength tends to increase with longer vibrating times. Therefore, it is suggested that using pre-mixed cement can shorten the vibrating time and increase the productivity of the concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1997년도 가을 학술발표회 논문집
• /
• pp.641-646
• /
• 1997

Polymer cement mortar which is used as material for aging concrete structures is generally mixed manually and applied on the job site. but, to secure the required quality of the mortar, pre-mixed polymer cement mortar is favored. This study was initiated to four different pre-mixed polymer cement mortars which are produced in Korea. The for pre-mixed mortars were selected and tested with respect to physical and mechanical properties an proved that their qualities were better than those of common cement concrete mortars.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.25-28
• /
• 2006

This study investigated pre-mixed cement combined with ordinary portland cement, BF and SF, in order to manufacture cement binder, which is possible to produce 150MPa ultra high strength concrete. The BF used in this study reduces and control hydration heat. It can also improve concrete fluidity, while AP increases hydration product and accelerates reaction of BF. SF has micro filler effect and makes pozzolanic reaction. It also fabricates high density internal organization. This developed pre-mixed cement can reduce hydration heat and increase hydration product. It is possible to fabricate high density organization and to secure homogeneity. The mock-up test of ultra high strength concrete showed excellent dispersibility and workability and indicated compressive strength more than 150MPa at 28 days.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.192-193
• /
• 2022

In this study, concrete durability was reviewed before CGS, a by-product generated from IGCC, was used as a fine aggregate for concrete. The characteristics of concrete and effect on carbonization according to the type of pre-mixed cement and the CGS substitution rate were analyzed. As a result of the analysis, the depth of carbonation according to the pre-mixed cement types increased by up to 52%, and the carbonation resistance tended to be similar overall when CGS was used as a fine aggregate.

• 시멘트 심포지엄
• /
• 통권34호
• /
• pp.144-149
• /
• 2007

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.381-384
• /
• 2008

본 연구에서는 폭렬방지용 합성섬유의 효과적인 투입방안 마련을 목적으로, 섬유혼입 프리믹스시멘트 결합재를 사용한 고강도 콘크리트의 폭렬방지 및 내화특성을 검토하였다. 내화시험 결과, 원주형 공시체의 폭렬은 W/C 15%의 수동투입에서 일부 박리 또는 파괴폭렬이 발생한 것을 제외하고 대부분 방지되었고, 전체적으로 섬유혼입 프리믹스시멘트는 폭렬방지 성능이 섬유 수동투입과 비교하여 동등 이상으로 우수하였으며, 결합재량이 많아 점성이 큰 고강도 콘크리트일수록 양호한 섬유의 분산성으로 폭렬방지에 더욱 효과적인 것으로 나타났다. 또한, 섬유혼입 프리믹스시멘트 결합재를 사용한 기둥부재의 온도이력은 폭렬이 방지되어 철근이 노출되지 않으면 최외곽 철근의 온도가 내화성능기준의 평균온도 538$^{\circ}C$를 넘지 않는 것으로 나타나, 고강도 콘크리트의 내화기준을 만족하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.154-155
• /
• 2022

In this study, propose a plan to efficiently utilize CGS, a by-product generated from IGCC, as a mixed fine aggregate for concrete. The effect of the premixed cement types and CGS replacement rate on the overall characteristics and length change rate of concrete was analyzed. As a result of the analysis, the effect of CGS was found to be insignificant, and the effect of cement was found to be dominant.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2008년도 춘계 학술논문 발표대회
• /
• pp.93-97
• /
• 2008

The study analyzed on each kind of basic characteristics in mortar to prove an effect of pre-mix cement, ultra high strength binder. The results were as follows. in characteristics of not set mortar, fluidity time was the quickest at the time of using POBSA and was more delayed at the time of using Fly Ash than at the time of using Blast Furnace Slag as a binder. Mortar ring flow and flow con flow got smaller as fluidity time got longer, on the contrary to fluidity time. Unit capacity mass was smaller at the time of using Fly Ash than at the time of using Blast Furnace Slag. According to pre-mix, it was difficult to discover a regular tendency. In characteristics of hardening mortar, the 28th day compressive strength was better than thing mixed after measuring separately in pre-mix. According to a binder's kind, Silica Fume B, C was better than Silica Fume A.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 2002년도 가을 학술발표회 논문집
• /
• pp.665-672
• /
• 2002

In order to expand agricultural lands in the western and southern coasts of Korean Peninsula, coarse soils excavated from hillsides have been used as fill materials for reclamation. In order to tackle with the problems and to confirm availability, research on soil improvement involve mixing cement to the fine wet soils. Required undrained shear strength(c$\sub$u/) for fill material was analyzed to be 0.34∼1.2kg/$\textrm{cm}^2$. It has been known that when cement is added to high water content marine clay, its unconfined compression strength increased to 2kg/$\textrm{cm}^2$. Consolidation results show that pre-consolidation pressure increased to 1.8kg/$\textrm{cm}^2$ and 3.4kg/$\textrm{cm}^2$ with the addition of 3% and 5% of cement respectively. This result shows that low-height embankments could be constructed without significant compression. Since the effectiveness of improvement may be different site by site, the mix design for each site is necessary in order to optimize it. The process is first to determine aimed shear strength and then optimum mix ratio of cement after carrying out a series of tests.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 추계 학술논문 발표대회
• /
• pp.37-40
• /
• 2007

This study investigates the effect of the pre-mix cement to the physical properties of the concrete according to the various combinations of the binders and the silica fume types. The results are summarized as following. For the properties of the fresh, the fluidity in the case that OPC+cilica fume-blast-furnace slag is appropriate compared to OPC+cilica fume+fly ash. Expecially, it is favorable when pre-mix is used. The fluidity time of the A, B depending on silica fume types is favorable, but it is decreased on C. The air content depending on silica fume types is low when the fly ash is used. Specially, the air content in the case that pre-mix is used is low caused by the dispersion of the silica fume. For the properties of the hardened concrete, the compressive and flexible strength when the blast-furnace slag is pre-mixed are high, and they exceed OPC. The strength depending on the silica fume types is high on B, and the strength of the others is similar.