• Journal of the Korean Applied Science and Technology
• /
• v.28 no.3
• /
• pp.351-358
• /
• 2011

It was researched to be alternative of TGIC type hardener with human hazard element as PT 910 mix powder paint with hardener. Generally PT 910 was compared with TGIC & Epoxy resin of hardener to be used at thermosetting powder paint. We inquired a property of matter for paint through Gel time, glass transition temperature, melting point and a property of matter for film through a property of adhesion, a property of tolerance, softness, gloss, acid-resistant, alkali-resistant, salt water spray-resistant, facilitation climatic. When PT 910 is used of hardener, it was shown the excellent results in gel time, softness, salt water spray-resistant, fracilitation climatic and the similar results in melting point, a property of tolerance, a property of adhesion, gloss, acid-resistant, alkali-resistant, as compared with the powder paint used by TGIC hardener. The glass transition temperature was little low. But there was slightly different results. After the study results, we reached the conclusion that thermosetting powder used by PT 910 is alterative to by TGIC hardener.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.6
• /
• pp.312-324
• /
• 2008

In this study, the functional property as a super abrasive material was secured for CBN powder by the electroless Ni-P plating on the surface of the particle. The plating solution has been prepared to control the surface morphology by regulating surfactants and process conditions. The effects of processing parameters on the surface morphology of CBN powder was discussed. The results are summarized as follows; A stable plating tendency was achieved from 1 hour after quantitatively dropping reducing agent. It was observed that more than 50% of the weight gain was obtained by Ni-P coating on the surface of CBN super abrasive powder. The morphology of the Ni-P coating layer is consisted of botryoidal and spiky type and it could be controlled by regulating processing parameters. Superior characteristic in terms of surface morphology was found in the nonionic surfactant XL-80N. It was found that XL-80N considerably decreased surface tension of CBN powder and Ni-P alloy surface then enhance wettability as well as plating rate. Metal coated CBN powder as a raw material of resin bond wheel has been developed through this investigation.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.12
• /
• pp.49-55
• /
• 2020

In order to improve the electromagnetic shielding rate of Carbon Fiber (CF), it was produced using the nickel nano-powder impregnating method. Using two types of nickel powder having thicknesses of 50 ㎛ and 100 ㎛, and a thermoplastic elastomer resin, a compound containing 10-20% nickel content was mixed and then manufactured through an extruder. The CF coated with the compound was woven and manufactured using a 1-ply specimen. The final nickel content of the specimen was verified using TGA and the distribution of nickel powder on the CF surface was verified using SEM. The metal shows a high shielding rate in the low-frequency band, but the shielding rate decreases at higher-frequency bands. The CF improves at the higher frequency band, and metals reflect electromagnetic waves while carbon absorbs electromagnetic waves. The study of shielding materials, which are stronger and lighter than metal, by using CF lighter than metal and enabling the shielding rate from low-frequency band to high-frequency band, confirmed that the larger the area coated with nickel nano-powder, the better the electromagnetic shielding performance. In particular, CF coated with a thickness of 100 ㎛ has a shielding rate similar to that of copper and can also be used for EV/HEV automotive cables and other applications in the future.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.619-620
• /
• 2013

• Journal of agriculture & life science
• /
• v.46 no.2
• /
• pp.43-48
• /
• 2012

This study was investigated on the properties of board made from Miscanthus sinensis var. purpurascens particles differed in density of board and mixed ratio of powder type- and liquid type-phenolic resin. As the board density increase, thickness swelling and bending strength increased while water absorption decreased. With increasing the resin content, water absorption and thickness swelling decreased while MOR and internal bond strength increased. The board made of liquid type phenol-formaldehyde resin was low in water absorption and thickness swelling, and there were similar bending strengths between power type- and liquid type-phenol resin in resin cont of 11% and 13% at the board density $0.4g/cm^3$ and internal bond strength was higher with liquid type-phenolic resin in its bending strength.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.595-599
• /
• 2011

ALC(Autoclaved Lightweight Concrete) is produced using quartz sand, lime and cement and water. And aluminum powder is used for blowing agent. ALC is manufactured by autoclave chamber under high-temperature and high-pressure. Generally, ALC is 1/4 levels lighter than concrete and mortar, because it has a lot of pores. So density of ALC is about 0.45~0.65 g/$cm^3$. But, ALC has a weakness, typically low strength, with its porous structure. So, it is necessary to excellent strength properties for extensive apply of ALC materials in high porosity. In this study, melamine resin was used to improve the strength characteristics of ALC materials. We performed compressive and bending strength measurements. Compressive strength of ALC with 2% melamine resin increased 26.88% than 'melamine-free' ALC. Also we performed functionality evaluation such as thermal conductivity, sound absorption, and flame-resistance.

• Fire Science and Engineering
• /
• v.12 no.4
• /
• pp.41-49
• /
• 1998

In this study, the thermal improvement of an isophthalic acid polyester resin by the incorporation of flame retardants has been investigated. Aluminium hydroxide, antimony oxide and alumina powder were used to formulate the flame retardant systems. The improvement of an isophthalic resin by incorporating aluminium hydroxide is dramatic(burning rate and smoke emission are reduced), although the mechanical property is decreased significantly. The addition of small amount(2.5 phr) of antimony oxide produces high char yield(31%) which acts as a protective layer on the surface of the resin.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.4
• /
• pp.607-615
• /
• 2015

To investigate the adhesion effect of various kinds and contents of polymeric methylene diphenyl diisocyanates (pMDIs) on adhesion performance, wood adhesives (A-1~5) were synthesized and characterized. As results, when the amount of pMDI increased in adhesives, the dry tensile strength was found to be proportionally increased sustaining at around $16.0{\sim}21.6kgf/cm^2$. The polyurethane (PU) resin, which used M11S as a source of pMDI showed the best wet tensile strength at $11.9kgf/cm^2$ and cyclic boil tensile strength at $8.1kgf/cm^2$, which satisfied the requirement of over $7kgf/cm^2$. Thermal properties of the rice powder (RP) based polyurethane resins were characterized by differential scanning calorimetry (DSC) and Thermal gravimetric analysis (TGA). Thermal stability of polyurethane resins increased to $250^{\circ}C$ with adding pMDIs. The more pMDI (M5S) was added to adhesive, the higher thermal stability of the resin was observed by TGA.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.31-36
• /
• 2013

${\beta}$-SiC powders were synthesized by a carbothermal reduction process using $SiO_2$-C precursors fabricated by a sol-gel process using phenol resin and TEOS as starting materials for carbon and Si sources, respectively. The C/Si molar ratio was selected as an important parameter for synthesizing SiC powders using a sol-gel process, and the effects of the C/Si molar ratio (1.4-3.0) on the particle size, particle size distribution, and yield of the synthesized ${\beta}$-SiC powders were investigated. It was found that (1) the particle size of the synthesized ${\beta}$-SiC powders decreased with an increase in the C/Si molar ratio in the $SiO_2$-C hybrid precursors, (2) the particle size distribution widened with an increase in the C/Si molar ratio, and (3) the yield of the ${\beta}$-SiC powder production increased with an increase in the C/Si molar ratio.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.1
• /
• pp.11-15
• /
• 2008

The composite membrane for direct methanol fuel cell (DMFC) was developed using $H_3O^+-{\beta}"-Al_2O_3$ powder and perfluorosulfonylfluroride copolymer (Nafion) resin. The perfluorosulfonylfluroride copolymer (Nafion) resin was mixed with $H_3O^+-{\beta}"-Al_2O_3$ powder and it was made to sheet form by hot pressing. The electrodes were prepared with 60 wt% PtRu/C and 60wt% Pt/C catalysts for anode and cathode, respectively. The morphology and the chemical composition of the composite membrane have been investigated by using SEM and EDXA, respectively. The composite membrane and $H_3O^+-{\beta}"-Al_2O_3$ were analyzed by using FT-IR and XRD. The methanol permeability of the composite membranes was also measured by gas chromatography (GC). The performance of the MEA containing the composite membrane (2wt% $H_3O^+-{\beta}"-Al_2O_3$) was higher than that of normal pure Nafion membrane at high operating temperature (e.g. $110^{\circ}C$), due to the homogenous distribution of $H_3O^+-{\beta}"-Al_2O_3$, which decreased the methanol permeability through the membrane and enhanced the water contents in the composite membrane.